Polymer Property : Flexural Strength = 210 MPa Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.
Mechanical Properties Metric English Comments
Flexural Strength 210 MPa
30500 psi
Plastcom SLOVAMID 6 GF 30 006/1M PA6 reinforced with 30% glass fibre
Features: PA 6 for injection moulding, chemically strengthened with 30% of milled glass fibre, for mouldings with high strength and toughness used in the automotive, electrical, engineering and cons..
Flexural Strength 210 MPa

@Temperature 23.0 °C
30500 psi

@Temperature 73.4 °F
ISO 178
DuPont Performance Polymers Crastin® SK609 BK851 PBT  (Unverified Data**)
Crastin® SK609 BK851 is a 50% glass fiber reinforced, lubricated, black polybutylene terephthalate resin for injection molding.Information provided by DuPont Performance Polymers
Flexural Strength 210 MPa
30500 psi
ISO 178
PolyOne Edgetek® AM-35GF/000 FR NH Polyphthalamide (PPA)
The Edgetek® Engineering Thermoplastic Compounds portfolio covers a broad range of standard and custom-formulated high performance materials. This portfolio includes high-temperature materials for ..
Flexural Strength 210 MPa
30500 psi
Lehmann & Voss LUVOCOM® 1105-8317/RD PEEK, with glass fiber
Applications: Automotive industry, textile machinery, medical- and precision engineering, aircraft industry.Strong, stiff parts.Chemical and hydrolysis resistance parts, non flammable.High dimension..
Flexural Strength 210 MPa
30500 psi
Lehmann & Voss LUVOCOM® 1105-8350 PEEK, with carbon fiber, PTFE, lubricant modified
Applications: Automotive industry, textile machinery, medical- and precision engineering, aircraft industry.Strong, stiff parts; low thermal coefficient of expansion.Dynamic stressed parts at high m..
Flexural Strength 210 MPa
30500 psi
Lehmann & Voss LUVOCOM® 3/CF/12/EG Polyamide 6, with carbon fiber, high viscosity
Applications: Automotive industry, textile machinery, apparatus- and precision engineering.High-strength and stiff parts; low coefficient of expansion.dynamic stressElectrically conductive, suitable..
Flexural Strength 210 MPa
30500 psi
Lehmann & Voss LUVOCOM® 1100-8194 Polyether sulfone, with glass fiber
Applications: Apparatus- and precision engineering, film- and photo industry, sporting- and leisure goods, medical- and electrical enineering, aircraft- and aerospace industry.High dimensionally sta..
Flexural Strength 210 MPa
30500 psi
Lehmann & Voss LUVOCOM® 1105-0797 PEEK, with glass fiber
Applications: Automotive industry, textile machinery, medical- and precision engineering, aircraft industry.Strong, stiff parts.High dimensionally stable precision parts, high continuous use tempera..
Flexural Strength 210 MPa
30500 psi
Lehmann & Voss LUVOCOM® 1105-0895/BL PEEK, with glass fiber
Applications: Automotive industry, textile machinery, medical- and precision engineering, aircraft industry.Strong, stiff parts.Chemical and hydrolysis resistance parts, non flammable.High dimension..
Flexural Strength 210 MPa
30500 psi
Lehmann & Voss LUVOCOM® 1105-0904/GN PEEK, with glass fiber
Applications: Automotive industry, textile machinery, medical- and precision engineering, aircraft industry.Strong, stiff parts.High dimensionally stable precision parts, high continuous use tempera..
Flexural Strength 210 MPa
30500 psi
2 mm/min; ISO 178
SABIC Innovative Plastics ULTEM 2200R PEI (Europe-Africa-Middle East)
20% Glass fiber filled, standard flow Polyetherimide (Tg 217C) with internal mold release. Resin is RoHS compliant. UL94 V0 and 5VA listing.
Flexural Strength 210 MPa
30500 psi
ISO 178
Solvay Specialty Polymers Ryton® R-7-121NA Polyphenylene Sulfide (PPS), GlassMineral Filled
Ryton® R-7-121NA and R-7-121BL glass fiber and mineral filled polyphenylene sulfide compounds provide good mechanical strength with good flow and low maintenance molding using conventional moldin..
Flexural Strength 210 MPa
30500 psi
Bending Strength; ASTM-F417
CeramTec Rubalit® 600 Alumina, 48%
Rubalit® 600 is suitable for both mechanical and laser trimming and is chiefly used as the core for high-grade carbon-film resistors.
Flexural Strength 210 MPa
30500 psi
ISO 178
Polyplastics FR-PET® CN9030 Glass Fiber Reinforced Polyethylene Terephthalate (GF-PET), Flame retardant, General purpose
Information provided by PolyPlastics.
Flexural Strength 210 MPa
30500 psi
ASTM D790
Polyram PlusTek PA324G6 Nylon 6.6, UL-94 V-0 30% Glass Fiber
Self extinguishing (UL-94 V-0) 30% glass fiber reinforced polyamide 6.6 for component with high stiffness and dimensional stabilityInformation provided by Polyram Ram On Ind.
Flexural Strength 210 MPa
30500 psi
ISO 178
Polyram PlusTek PA7800G33 Nylon 6.6 for Injection Molding, 33% Glass Fiber Reinforced, Heat Stabilized, Impact Modified
33% Glass fiber reinforced, heat stabilized, impact modified Nylon 6.6 for injection molding applications.Information provided by Polyram.
Flexural Strength 210 MPa
30500 psi
DIN EN ISO 178
Wolf Kunststoff ZEDEX® ZX-324VMT A3B PEEK, Fiber Reinforced
Main Characteristics: Maximum rigidity; Very good wear resistance; Low stick-slip tendency; Stress resistantApplications: Shipbuilding; Chemical Engineering; Automitve Technology; Machine ToolsInfor..
Flexural Strength 210 MPa
30500 psi
ASTM D 790
RTP Company RTP 281 TFE 20 Nylon 6/6 (PA), Carbon Fiber - PTFE Lubricated
Flexural Strength >= 210 MPa
>= 30500 psi
ASTM D790
Polyram PlusTek RA300G6 Nylon 6.6, 30% Glass Fiber
30% glass fiber reinforced polyamide 6.6 for injection molding applicationsInformation provided by Polyram Ram On Ind.
Flexural Strength 210 MPa
30500 psi
50%RH; ISO 178
DuPont Performance Polymers Zytel® HTN FR52G30BL BK337 Polyphthalamide (PPA)  (Unverified Data**)
30% Glass Reinforced Flame Retardant PPA High Performance Polyamide Zytel HTNFR52G30BL BK337 is a 30% glass reinforced flame retardant lubricated high performance polyamide resin that has been devel..
Flexural Strength 210 MPa
30500 psi
ISO 178
Celanese CELANEX 2302 GV1/30 PBT, 30% Glass Reinforced
Chemical abbreviation according to ISO 1043-1: PBTInformation provided by Celanese
Flexural Strength 210 MPa
30500 psi
ISO 178
Celanese Celanex® 1662Z PBT, 30% Glass Reinforced
Celanex 1662Z is a 30% glass reinforced polybutylene terephthalate with a good balance of mechanical properties and processabilityTo avoid hydrolytic degradation during processing, CELANEX resins ha..
Flexural Strength 210 MPa
30500 psi
ASTM Test
BASF Petra® 130 FR 30% Glass Filled PET
Petra 130 FR is a 30% glass fiber reinforced, flame retardant injection molding polyethylene terephthalate feedstocks. It is recognized as UL 94V-0/5VA by Underwriters Laboratories. It is also avail..
Flexural Strength 210 MPa
30500 psi
ISO 178
Celanese FORTRON 6165A4 PPS, 65% Mineral / Glass Reinforced
Fortron 6165A4 offers a unique balance of properties based on a high mineral and glass reinforced composition. The heat resistance under load bearing conditions is excellent for this product. As wit..
Flexural Strength 210 MPa
30500 psi
ISO 178
Celanese FORTRON ICE 717F PPS, 65% Mineral / Glass Reinforced
Fortron ICE 717F is a glass/mineral reinforced material with superior fuel resistance. It is specially designed to work in the environment of high temperature and high ethanol content. It offiers ..
Flexural Strength 210 MPa
30500 psi
ISO 178
BASF Ultramid® A3EG6 30% Glass Filled PA66 (Conditioned)
Ultramid A3EG6 is a 30% glass fiber reinforced injection molding PA66 grade for machinery components and housings of high stiffness and dimensional stability.
Flexural Strength 210 MPa
30500 psi
BCC Products BC 5010 Epoxy Laminating System
BC 5010 is a high quality, low viscosity room temperature curing laminating resin. A Safety System for the production of a variety of dimensionally stable fiberglass tools. BC 5010 features low odor..
Flexural Strength 210 MPa
30500 psi
ASTM-D790
Polyram Polytron P50B01 Homopolymer Polypropylene, Chemically Coupled 50% LGF
A chemically coupled 50% LGF reinforced black PP, heat stabilized for high temperature applications such as under the hood automotive parts.Information provided by Polyram Ram On Ind.
Flexural Strength 210 MPa
30500 psi
ISO 178
Celanese Celstran® PP-GF30-02 AF 3001 PP, 30% Glass Reinforced
30% long glass fiber reinforced polypropyleneInformation provided by Celanese
Flexural Strength 210 MPa
30500 psi
Lehmann & Voss LUVOCOM® 1105-7173/BL PEEK, with glass fiber
Applications: Automotive industry, textile machinery, medical- and precision engineering, aircraft industry.Strong, stiff parts.Chemical and hydrolysis resistance parts, non flammable.High dimension..