Polymer Property : Flexural Strength = 30500 psi Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.
Mechanical Properties Metric English Comments
Flexural Strength 210 MPa
30500 psi
Three Point Bend
Osprey Metals CE17 Al-Si Controlled Expansion Alloy
Al-27%Si controlled expansion alloy manufactured and patented by Osprey Metals Ltd.Information provided to MatWeb by Osprey Metals.
Flexural Strength 210 MPa
30500 psi
ISO 178
Celanese Celanex® 2302 GV1/30 PBT, 30% Glass Reinforced  (Unverified Data**)
Chemical abbreviation according to ISO 1043-1: PBT30% glass fiber reinforced, high glossInformation provided by Celanese
Flexural Strength 210 MPa
30500 psi
ISO 178
Celanese Celanex® 3300-2 PBT, 30% Glass Reinforced  (Unverified Data**)
Celanex 3300-2 is a general purpose, 30% glass reinforced, polybutylene terephthalate that offers a superior combination of mechanical, electrical, and thermal properties. This grade provides outsta..
Flexural Strength 210 MPa
30500 psi
ISO 178
Celanese Celanex® 3309HRLM PBT, 30% Glass Reinforced  (Unverified Data**)
Celanex 3309HRLM is a non-lubricated, 30% fiberglass reinforced Polybutylene Terephthalate which has excellent hydrolysis resistance, mechanical properties and processability.30% glass filled PBT, h..
Flexural Strength 210 MPa
30500 psi
ISO 178
Celanese VECTRA E115i LCP, 15% Glass Reinforced  (Unverified Data**)
15% Glass ReinforcedInformation provided by Celanese
Flexural Strength 210 MPa
30500 psi
Lehmann & Voss LUVOCOM® 20-8112 Polyphthalamide, with carbon fiber, lubricant modified
Applications: Automotive industry, textile- and office machinery, apparatus- and precision engineering.Strong, stiff parts.Dynamic stressed parts at high movement velocity.Improved friction and wear..
Flexural Strength 210 MPa
30500 psi
Lehmann & Voss LUVOCOM® 1100-8194 Polyether sulfone, with glass fiber
Applications: Apparatus- and precision engineering, film- and photo industry, sporting- and leisure goods, medical- and electrical enineering, aircraft- and aerospace industry.High dimensionally sta..
Flexural Strength 210 MPa
30500 psi
Lehmann & Voss LUVOCOM® 1105-1963 PEEK, with glass fiber
Applications: Automotive industry, textile machinery, medical- and precision engineering, aircraft industry.Strong, stiff parts.Dynamic stressed parts.Chemical and hydrolysis resistance parts, non f..
Flexural Strength 210 MPa
30500 psi
Lehmann & Voss LUVOCOM® 1105-7826/BL PEEK, with glass fiber
Applications: Automotive industry, textile machinery, medical- and precision engineering, aircraft industry.Strong, stiff parts.Chemical and hydrolysis resistance parts, non flammable.High dimension..
Flexural Strength 210 MPa
30500 psi
Lehmann & Voss LUVOCOM® 1105-7876-1 PEEK, with carbon fiber
Applications: Automotive industry, textile machinery, medical- and precision engineering, aircraft industry.Strong, stiff parts.Low warpage.Emergency running property.Information provided by Lehmann..
Flexural Strength 210 MPa
30500 psi
Lehmann & Voss LUVOCOM® 1-7956 Polyamide 66, with carbon fiber
Applications: Automotive industry, textile- and office machinery, apparatus- and precision engineering.Strong, stiff parts.Reduced moment of inertia compared with metal parts.Electrically conductive..
Flexural Strength 210 MPa
30500 psi
ISO 178
SABIC Innovative Plastics LNP LUBRICOMP ECL36 PEI
LNP* Lubricomp* ECL36 is a compound based on Polyetherimide resin containing 30% Carbon Fiber, 15% PTFE. Added features of this material include: Internally Lubricated.
Flexural Strength 210 MPa
30500 psi
ISO 178
SABIC Innovative Plastics LNP LUBRICOMP RFL159 PA 66
LNP* LUBRICOMP* RFL159 is a compound based on Nylon 66 resin containing 25% Glass Fiber, 5% PTFE. Added features of this material include: Wear Resistant, Flame Retardant
Flexural Strength 210 MPa
30500 psi
2 mm/min; ISO 178
SABIC Innovative Plastics ULTEM 2200 PEI (Europe-Africa-Middle East)
20% Glass fiber filled, standard flow Polyetherimide (Tg 217C). Resin is RoHS compliant. UL94 V0 and 5VA listing.
Flexural Strength 210 MPa
30500 psi
2 mm/min; ISO 178
SABIC Innovative Plastics ULTEM 2200F PEI (Europe-Africa-Middle East)
20% Glass fiber filled, standard flow Polyetherimide (Tg 217C). Resin is RoHS compliant. US FDA and European Food Contact approved. Effective June, 2007 this grade will no longer be supported with b..
Flexural Strength 210 MPa
30500 psi
ISO 178
Solvay Specialty Polymers Ryton® R-7-121NA Polyphenylene Sulfide (PPS), GlassMineral Filled
Ryton® R-7-121NA and R-7-121BL glass fiber and mineral filled polyphenylene sulfide compounds provide good mechanical strength with good flow and low maintenance molding using conventional moldin..
Flexural Strength 210 MPa
30500 psi
ISO 178
SABIC Innovative Plastics LNP Thermocomp OFJ66 PPS - Linear
LNP* Thermocomp* OFJ66 is a compound based on PPS - Linear resin containing Glass Fiber, Mineral. Added features of this material include: Low Warpage.This data was supplied by SABIC-IP for the Ame..
Flexural Strength 210 MPa
30500 psi
ASTM D 790
RTP Company RTP 281 TFE 20 Nylon 6/6 (PA), Carbon Fiber - PTFE Lubricated
Flexural Strength 210 MPa
30500 psi
cond; ISO 178
DSM Novamid® 3010GN30 NAT PA66-GF30 FR(17)
30% Glass Reinforced, Flame Retardant
Flexural Strength 210 MPa
30500 psi
ASTM D790
Ensinger Tecapeek® XP-98 Medical Compression Molded PEEK Compound, 30% Carbon Fiber
Ensinger Special Polymers offers over twenty different VICTREX® PEEK blends to choose from and has the capability to blend custom compounds for specific applications. Compression molding results in..
Flexural Strength 210 MPa
30500 psi
ISO 178
Eurostar Starflam PF0057E PA6, 25% Glass Filled, Injection Molded
Halogen Free and Red Phosphorous Free, Flame Retardant, Glass Fiber Reinforced, Polyamide 6 Injection Molding Resin (also known as PF-1005 Z270)Information provided by Polymer Technology & Services,..
Flexural Strength 210 MPa
30500 psi
ISO 178
Celanese CELANEX 2302 GV1/30 PBT, 30% Glass Reinforced
Chemical abbreviation according to ISO 1043-1: PBTInformation provided by Celanese
Flexural Strength 210 MPa
30500 psi
ISO 178
Celanese Celanex® 1662Z PBT, 30% Glass Reinforced
Celanex 1662Z is a 30% glass reinforced polybutylene terephthalate with a good balance of mechanical properties and processabilityTo avoid hydrolytic degradation during processing, CELANEX resins ha..
Flexural Strength 210 MPa
30500 psi
ISO 178
Celanese VECTRA E115i LCP, 15% Glass Reinforced
15% glass reinforcedInformation provided by Celanese
Flexural Strength 210 MPa
30500 psi
2 [mm/min]; ISO 178
Akro-Plastic Akromid® S3 GF 23 1 (2917) PA 6.10 Dry, 23% Glass Filled
A characteristic property of AKROMID® S (PA 6.10) is that it has a renewable-resource content of up to 70 % and therefore fulfils the current definition of a bioplastic. The plant-based raw materia..
Flexural Strength 210 MPa
30500 psi
ASTM D790
Beijing Chemical Industry KAIFA® 3030F PET Resin
High mechanical strength, Creep resistant, Low friction, High crystallizationInformation provided by Beijing Chemical Industry Research Institute (Group)
Flexural Strength 210 MPa
30500 psi
ISO Data
BASF Ultramid® 8333G HI HS BK-102 33% Glass Filled PA6 (Dry)
Ultramid 8333G HI HS BK-102 is a 33% glass reinforced, heat stabilized, impact modified, pigmented black, PA6 injection molding compound developed for applications requiring improved dry as molded t..
Flexural Strength 210 MPa
30500 psi
BCC Products BC 5010 Epoxy Laminating System
BC 5010 is a high quality, low viscosity room temperature curing laminating resin. A Safety System for the production of a variety of dimensionally stable fiberglass tools. BC 5010 features low odor..
Flexural Strength 210 MPa
30500 psi
ASTM-D790
Polyram Polytron P50B01 Homopolymer Polypropylene, Chemically Coupled 50% LGF
A chemically coupled 50% LGF reinforced black PP, heat stabilized for high temperature applications such as under the hood automotive parts.Information provided by Polyram Ram On Ind.
Flexural Strength 210 MPa
30500 psi
ASTM D790
Solvay Specialty Polymers Amodel® A-1565 HS Polyphthalamide (PPA)  (Unverified Data**)
Amodel A-1565 HS is a 65% glass and mineral-reinforced polyphthalamide (PPA) designed to be cost-effective in applications requiring high stiffness, good dimensional stability and good retention of ..