Polymer Property : Tensile Strength at Break = 149 MPa Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.
Mechanical Properties Metric English Comments
Tensile Strength at Break 149 MPa
21600 psi
5 mm/min; ISO 527
SABIC Innovative Plastics LNP LUBRICOMP RFL159 PA 66
LNP* LUBRICOMP* RFL159 is a compound based on Nylon 66 resin containing 25% Glass Fiber, 5% PTFE. Added features of this material include: Wear Resistant, Flame Retardant
Tensile Strength at Break 149 MPa
21600 psi
ASTM D638
SABIC Innovative Plastics LNP LUBRICOMP SFL2A PA 12 (Asia Pacific)
LNP* LUBRICOMP* SFL2A is a compound based on Nylon 12 resin containing Glass Fiber, PTFE. Added features of this material include: Internally Lubricated.
Tensile Strength at Break 149 MPa
21600 psi
ASTM D638
SABIC Innovative Plastics LNP LUBRICOMP SFL2A PA12
LNP* LUBRICOMP* SFL2A is a compound based on Nylon 12 resin containing 50% Glass Fiber, 10% PTFE. Added feature of this material is: Wear Resistant.
Tensile Strength at Break 149 MPa
21600 psi
ASTM D 638
SABIC Innovative Plastics LNP Thermocomp JF008 PES
LNP* Thermocomp* JF008 is a compound based on Polyethersulfone resin containing Glass Fiber.This data was supplied by SABIC-IP for the Americas region.
Tensile Strength at Break 149 MPa
21600 psi
Type I, 5 mm/min; ASTM D638
SABIC Innovative Plastics LNP THERMOCOMP RF004XXH PA 66
LNP THERMOCOMP* RF004XXH is a compound based on Nylon 66 resin containing 20% Glass Fiber. Added feature of this grade is: Healthcare.
Tensile Strength at Break 149 MPa
21600 psi
5 mm/min; ISO 527
SABIC Innovative Plastics LNP THERMOCOMP RF007ES PA 66
LNP* THERMOCOMP* RF007ES is a compound based on Nylon 66 resin containing 35% Glass Fiber. Added features of this material include: Heat Stabilized, Easy Molding.
Tensile Strength at Break 149 MPa
21600 psi
ASTM D638
SABIC Innovative Plastics LNP LUBRICOMP QFL36 PA 6/10
LNP LUBRICOMP* QFL36 is a compound based on Nylon 6/10 resin containing 30% Glass Fiber, 15% PTFE. Added features of this material include: Wear Resistant.
Tensile Strength at Break 149 MPa
21600 psi
ISO 527
SABIC Innovative Plastics LNP STAT-KON EX99550C PEI
LNP* STAT-KON* EX99550C is a compound based on Polyetherimide resin containing Proprietary Filler(s). Added features of this material include: Clean Compounding System, Electrically Conductive.
Tensile Strength at Break 149 MPa
21600 psi
ASTM D638
LNP Lubricomp® QFL-4036 BK8-115 Polyamide 6/10 Copolymer, Glass Fiber Reinforcement, PTFE Lubricant  (disconti
Features: LubricatedForms: PelletsProcessing Method: Injection MoldingInformation provided by LNP, a GE Plastics Company.This data sheet is labeled Discontinued; however many LNP grades are still ac..
Tensile Strength at Break 149 MPa
21600 psi
ISO 527
SABIC Innovative Plastics LNP Verton NV006E PC/ABS
LNP* Verton* NV006E is a compound based on PC/ABS resin containing Long Glass Fiber. Added features of this material include: Easy Molding.This data was supplied by SABIC-IP for the Americas region..
Tensile Strength at Break 149 MPa
21600 psi
ISO 527
SABIC Innovative Plastics LNP VERTON NV006E PC/ABS (Asia Pacific)
LNP* Verton* NV006E is a compound based on PC/ABS resin containing Long Glass Fiber. Added features of this material include: Easy Molding.
Tensile Strength at Break 149 MPa
21600 psi
ASTM D638
SABIC Innovative Plastics LNP STAT-KON LX04420C PEEK
LNP* STAT-KON* LX04420C is a compound based on Polyetheretherketone resin containing Proprietary Filler(s). Added features of this material include: Electrically Conductive, Clean Compounding Syst..
Tensile Strength at Break 149 MPa
21600 psi
ISO 527
SABIC Innovative Plastics LNP STAT-KON LX04420C PEEK
LNP* STAT-KON* LX04420C is a compound based on Polyetheretherketone resin containing Proprietary Filler(s). Added features of this material include: Electrically Conductive, Clean Compounding Syst..
Tensile Strength at Break 149 MPa
21600 psi
ISO 527
SABIC Innovative Plastics LNP VERTON NV006E PC+ABS
LNP* Verton* NV006E is a compound based on PC+ABS blend resin containing 30% Long Glass Fiber. Added features of this material include: Easy Molding, Structural.