SABIC Innovative Plastics Cycoloy® CM6210 PC+ABS (Asia Pacific)

Category Polymer , Thermoplastic , ABS Polymer , Polycarbonate/ABS Alloy, Unreinforced , Polycarbonate (PC)
Manufacturer SABIC Innovative Plastics (GE Plastics)
Trade Name Cycoloy®
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF SABIC Innovative Plastics Cycoloy® CM6210 PC+ABS (Asia Pacific).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Cycoloy* resin CM6210 is a high-modulus flame retardant PC/ABS with non-brominated and non-chlorinated FR system. It can be used for extrusion & thermoforming applications and also for injection molding applications where higher stiffness is needed.
Physical Properties Metric English Comments
Specific Gravity 1.28 g/cc
1.28 g/cc
ASTM D792
Density 1.27 g/cc
0.0459 lb/in³
ISO 1183
Moisture Absorption 0.100 %
0.100 %
23°C / 50% RH; ISO 62
Water Absorption at Saturation 0.30 %
0.30 %
ISO 62
Linear Mold Shrinkage, Flow 0.0040 - 0.0060 cm/cm

@Thickness 3.20 mm
0.0040 - 0.0060 in/in

@Thickness 0.126 in
SABIC Method
Melt Flow 11.5 g/10 min

@Load 5.00 kg,
Temperature 260 °C
11.5 g/10 min

@Load 11.0 lb,
Temperature 500 °F
ASTM D1238
Melt Index of Compound 9.0 g/10 min

@Load 5.00 kg,
Temperature 260 °C
9.0 g/10 min

@Load 11.0 lb,
Temperature 500 °F
MVR [cm^3/10 min]; ISO 1133
Mechanical Properties Metric English Comments
Hardness, Rockwell R 98
98
ISO 2039-2
Tensile Strength at Break 50.0 MPa
7250 psi
Type I, 5 mm/min; ASTM D638
50.0 MPa
7250 psi
50 mm/min; ISO 527
65.0 MPa
9430 psi
5 mm/min; ISO 527
Tensile Strength, Yield 59.0 MPa
8560 psi
5 mm/min; ISO 527
63.0 MPa
9140 psi
50 mm/min; ISO 527
64.0 MPa
9280 psi
Type I, 5 mm/min; ASTM D638
Elongation at Break 80 %
80 %
Type I, 5 mm/min; ASTM D638
97 %
97 %
50 mm/min; ISO 527
101 %
101 %
5 mm/min; ISO 527
Elongation at Yield 3.5 %
3.5 %
50 mm/min; ISO 527
3.6 %
3.6 %
5 mm/min; ISO 527
4.9 %
4.9 %
Type I, 5 mm/min; ASTM D638
Tensile Modulus 3.57 GPa
518 ksi
5 mm/min; ASTM D638
3.66 GPa
531 ksi
1 mm/min; ISO 527
Flexural Yield Strength 106 MPa
15400 psi
2 mm/min; ISO 178
110 MPa
16000 psi
1.3 mm/min, 50 mm span; ASTM D790
Flexural Modulus 3.50 GPa
508 ksi
1.3 mm/min, 50 mm span; ASTM D790
3.56 GPa
516 ksi
2 mm/min; ISO 178
Izod Impact, Notched 5.00 J/cm
9.37 ft-lb/in
ASTM D256
0.900 J/cm

@Temperature -30.0 °C
1.69 ft-lb/in

@Temperature -22.0 °F
ASTM D256
Izod Impact, Notched (ISO) 45.0 kJ/m²
21.4 ft-lb/in²
80*10*3; ISO 180/1A
10.0 kJ/m²

@Temperature -30.0 °C
4.76 ft-lb/in²

@Temperature -22.0 °F
80*10*3; ISO 180/1A
Charpy Impact, Notched 4.50 J/cm²
21.4 ft-lb/in²
Edgew 80*10*3 sp=62mm; ISO 179/1eA
1.00 J/cm²

@Temperature -30.0 °C
4.76 ft-lb/in²

@Temperature -22.0 °F
Edgew 80*10*3 sp=62mm; ISO 179/1eA
Dart Drop, Total Energy 45.0 J

@Temperature 23.0 °C
33.2 ft-lb

@Temperature 73.4 °F
ASTM D3763
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 52.0 µm/m-°C

@Temperature -40.0 - 40.0 °C
28.9 µin/in-°F

@Temperature -40.0 - 104 °F
ISO 11359-2
52.0 µm/m-°C

@Temperature 23.0 - 60.0 °C
28.9 µin/in-°F

@Temperature 73.4 - 140 °F
ISO 11359-2
57.0 µm/m-°C

@Temperature -40.0 - 40.0 °C
31.7 µin/in-°F

@Temperature -40.0 - 104 °F
ASTM E 831
CTE, linear, Transverse to Flow 60.0 µm/m-°C

@Temperature -40.0 - 40.0 °C
33.3 µin/in-°F

@Temperature -40.0 - 104 °F
ISO 11359-2
60.0 µm/m-°C

@Temperature 23.0 - 60.0 °C
33.3 µin/in-°F

@Temperature 73.4 - 140 °F
ISO 11359-2
70.0 µm/m-°C

@Temperature -40.0 - 40.0 °C
38.9 µin/in-°F

@Temperature -40.0 - 104 °F
ASTM E 831
Thermal Conductivity 0.300 W/m-K
2.08 BTU-in/hr-ft²-°F
ISO 8302
Hot Ball Pressure Test <= 95.0 °C
<= 203 °F
IEC 60695-10-2
Deflection Temperature at 0.46 MPa (66 psi) 99.0 °C
210 °F
Edgew 120*10*4 sp=100mm; ISO 75/Be
Deflection Temperature at 1.8 MPa (264 psi) 89.0 °C
192 °F
Edgew 120*10*4 sp=100mm; ISO 75/Ae
90.0 °C

@Thickness 3.20 mm
194 °F

@Thickness 0.126 in
unannealed; ASTM D648
Vicat Softening Point 106 °C
223 °F
Rate B/50; ASTM D1525
112 °C
234 °F
Rate B/50; ISO 306
114 °C
237 °F
Rate B/120; ISO 306
UL RTI, Electrical 60.0 °C
140 °F
UL 746B
UL RTI, Mechanical with Impact 60.0 °C
140 °F
UL 746B
UL RTI, Mechanical without Impact 60.0 °C
140 °F
UL 746B
Flammability, UL94 V-0

@Thickness 1.50 mm
V-0

@Thickness 0.0591 in
UL 94
Electrical Properties Metric English Comments
Dielectric Constant 2.8

@Frequency 1.00e+6 Hz
2.8

@Frequency 1.00e+6 Hz
IEC 60250
2.9

@Frequency 50.0 - 60.0 Hz
2.9

@Frequency 50.0 - 60.0 Hz
IEC 60250
Dielectric Strength 17.0 kV/mm

@Thickness 3.20 mm
432 kV/in

@Thickness 0.126 in
in oil; IEC 60243-1
26.0 kV/mm

@Thickness 1.60 mm
660 kV/in

@Thickness 0.0630 in
in oil; IEC 60243-1
38.0 kV/mm

@Thickness 0.800 mm
965 kV/in

@Thickness 0.0315 in
in oil; IEC 60243-1
Dissipation Factor 0.0030

@Frequency 50.0 - 60.0 Hz
0.0030

@Frequency 50.0 - 60.0 Hz
IEC 60250
0.0040

@Frequency 1.00e+6 Hz
0.0040

@Frequency 1.00e+6 Hz
IEC 60250
Comparative Tracking Index 250 V
250 V
IEC 60112
Descriptive Properties Value Comments
Ball Pressure Test, 75°C +/- 2°C pass
IEC 60695-10-2