Polymer Property : Melt Flow = 11.5 g/10 min Product List

Physical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Physical Properties	Metric	English	Comments
Melt Flow	11.5 g/10 min	11.5 g/10 min	(Condition L) ASTM D-1238
Multibase Multi-Flex® TPE A 8021 BLK , 37.5% Filler Content Multi-Flex® TPE 8021 is a calcium carbonate filled TPE based on Kraton G. Its ease in processing makes it good for many applications, for either small or large parts. Multi-Flex TPE contains Krat..
Melt Flow	11.5 g/10 min @Load 2.16 kg, Temperature 190 °C	11.5 g/10 min @Load 4.76 lb, Temperature 374 °F	Procedure A Condition E; ASTM D1238
Network Polymers NPP 50-1052 Description: High Density Polyethylene (HDPE)Information provided by Network Polymers Inc.
Melt Flow	11.5 g/10 min @Load 5.00 kg, Temperature 260 °C	11.5 g/10 min @Load 11.0 lb, Temperature 500 °F	ASTM D1238
SABIC Innovative Plastics Cycoloy® CM6210 PC+ABS Cycoloy* resin CM6210 is a high-modulus flame retardant PC/ABS with non-brominated and non-chlorinated FR system. It can be used for extrusion & thermoforming applications and also for injection mol..
Melt Flow	11.5 g/10 min @Load 5.00 kg, Temperature 260 °C	11.5 g/10 min @Load 11.0 lb, Temperature 500 °F	ASTM D1238
SABIC Innovative Plastics Cycoloy® CM6210 PC+ABS (Asia Pacific) Cycoloy* resin CM6210 is a high-modulus flame retardant PC/ABS with non-brominated and non-chlorinated FR system. It can be used for extrusion & thermoforming applications and also for injection mol..
Melt Flow	11.5 g/10 min @Load 2.16 kg, Temperature 190 °C	11.5 g/10 min @Load 4.76 lb, Temperature 374 °F	ASTM D1238
NOVA Chemicals Sclair® 31E LLDPE Extrusion Resin Features: Excellent tensile properties, excellent impact toughness, outstanding gloss and clarity, excellent processability.Applications: Coating and sheathing.Data provided by the manufacturer.
Melt Flow	11.5 g/10 min @Load 2.16 kg, Temperature 190 °C	11.5 g/10 min @Load 4.76 lb, Temperature 374 °F	ASTM D 1238
NOVA Chemicals Sclair® 31G Butene Copolymer LLDPE Extrusion Coating Resin 31G complies with the U.S. FDA specifications for olefin polymers and may thus be used in the United States as an article or component of an article intended for use in contact with food. 31G is su..
Melt Flow	11.5 g/10 min	11.5 g/10 min	High load; ASTM D1238
LyondellBasell PetrotheneÂ® LP5100 High Density Polyethylene ApplicationsPETROTHENE LP 5100 is especially designed for large-part blow molding of durable goods and deep-draw sheet extrusion/thermoforming applications. LP 5100 exhibits excellent impact resist..
Melt Flow	11.5 g/10 min @Load 10.0 kg, Temperature 220 Â°C	11.5 g/10 min @Load 22.0 lb, Temperature 428 Â°F	ASTM D1238
LG Chemical XG569C MABS, Anti-Scratch, High Gloss Feature: Injection Molding, Anti-Scratch, High GlossApplication: LCD TV Front Cabinet, Bezel, Audio/Video HousingCSA No. 9011-14-7 and 9003-56-9Information provided by LG Chemical
Melt Flow	11.5 g/10 min @Load 10.0 kg, Temperature 220 Â°C	11.5 g/10 min @Load 22.0 lb, Temperature 428 Â°F	ASTM D1238
Samsung Cheil Industries StarexÂ® SD-0170 ABS, Unreinforced Information provided by Samsung Cheil Industries.
Melt Flow	11.5 g/10 min @Load 10.0 kg, Temperature 220 Â°C	11.5 g/10 min @Load 22.0 lb, Temperature 428 Â°F	ASTM D1238
Samsung Cheil Industries StarexÂ® SD-0170 ABS, Unreinforced Information provided by Samsung Cheil Industries.
Melt Flow	11.5 g/10 min @Load 6.60 kg, Temperature 337 Â°C	11.5 g/10 min @Load 14.6 lb, Temperature 639 Â°F	ASTM D1238
SABIC Innovative Plastics ULTEM 2110R PEI 10% Glass fiber filled, enhanced flow Polyetherimide (Tg 217C) with internal mold release. ECO Conforming, UL94 V0 and 5VA listing.
Melt Flow	11.5 g/10 min @Load 6.60 kg, Temperature 337 Â°C	11.5 g/10 min @Load 14.6 lb, Temperature 639 Â°F	ASTM D1238
SABIC Innovative Plastics ULTEM 2110R PEI (Asia Pacific) 10% Glass fiber filled, enhanced flow Polyetherimide (Tg 217C) with internal mold release. ECO Conforming, UL94 V0 and 5VA listing.
Melt Flow	11.5 g/10 min @Load 5.00 kg, Temperature 200 °C	11.5 g/10 min @Load 11.0 lb, Temperature 392 °F	ISO 1133 H
Total Polystyrene Impact 6540 Easy Flow Impact Polystyrene POLYSTYRENE IMPACT 6540 is an easy flowing, high impact polystyrene with a good balance of mechanical and thermal properties. This resin combines physical properties such as the flow necessary for ..
Melt Flow	11.5 g/10 min	11.5 g/10 min
Zylog Hipolyene® 9221 XM Thermoplastic Polyolefin & PP Compound Information provided by Zylog Plastalloys Pvt. Ltd.
Melt Flow	11.5 g/10 min @Load 2.16 kg, Temperature 230 °C	11.5 g/10 min @Load 4.76 lb, Temperature 446 °F	ISO 1133
Borealis Daplen™ EE065AI Polypropylene Elastomer Modified Daplen™ EE065AI is an elastomer modified polypropylene with increased crystallinity. This material has an excellent balance between impact strength and stiffness. The product is available in natu..
Melt Flow	11.5 g/10 min @Load 2.16 kg, Temperature 190 °C	11.5 g/10 min @Load 4.76 lb, Temperature 374 °F	ASTM D 1238
Chevron Phillips Marlex® 9012 HDPE Injection Molding Resin Resin Type: Linear Copolymer, ASTM D 4976 Classification: PE 232, A 55600Characteristics: Good Flow, Good Impact Strength, Good Stiffness, Good ESCR, Good Shrinkage ResistanceApplications:Food Pails..
Melt Flow	11.5 g/10 min	11.5 g/10 min	Condition 190/21.6, HLMI; ASTM D1238
Chevron Phillips Marlex® K608 HDPE Extrusion Molding Resin Resin Type: Ethylene HomopolymerCharacteristics: Good ESCRExceptional RigidityExcellent melt strengthGood whiteness in unpigmented partsApplications: Table topsNursery containersDunnage traysLarge t..
Melt Flow	11.5 g/10 min @Load 3.80 kg, Temperature 230 °C	11.5 g/10 min @Load 8.38 lb, Temperature 446 °F	ASTM D1238
Diamond Polymers DIAMALOY 801 Polycarbonate/Polyester Alloy Information Provided by Diamond Polymers, Inc. & Network Polymers, Inc.