Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Modulus | 3.66 GPa | 531 ksi | 1 mm/min; ISO 527 |
SABIC Innovative Plastics Cycoloy® CM6210 PC+ABS Cycoloy* resin CM6210 is a high-modulus flame retardant PC/ABS with non-brominated and non-chlorinated FR system. It can be used for extrusion & thermoforming applications and also for injection mol.. |
|||
Tensile Modulus | 3.66 GPa | 531 ksi | 1 mm/min; ISO 527 |
SABIC Innovative Plastics Cycoloy® CM6210 PC+ABS (Asia Pacific) Cycoloy* resin CM6210 is a high-modulus flame retardant PC/ABS with non-brominated and non-chlorinated FR system. It can be used for extrusion & thermoforming applications and also for injection mol.. |
|||
Tensile Modulus | 3.66 GPa | 531 ksi | 1 mm/min; ISO 527 |
SABIC Innovative Plastics Cycoloy® CM6210 PC+ABS (Europe-Africa-Middle East) Cycoloy* resin CM6210 is a high-modulus flame retardant PC/ABS with non-brominated and non-chlorinated FR system. It can be used for extrusion & thermoforming applications and also for injection mol.. |
|||
Tensile Modulus | 3.66 GPa | 531 ksi | ASTM 638 |
NOVA Chemicals Dylark® 432 High-Heat Styrenic Copolymer Product Description and Features: Styrenic copolymer with excellent heat resistance and good modulus. Resin designed for use as an additive to promote adhesion and compatibility in compounding of .. |
|||
Tensile Modulus | 3.66 GPa | 531 ksi | 50 mm/min; ASTM D638 |
SABIC Innovative Plastics LNP THERMOCOMP EX06430H PEI LNP* THERMOCOMP* EX06430H is a compound based on Polyetherimide resin containing Proprietary Filler(s). Added feature of this grade is: Healthcare. |
|||
Tensile Modulus | 3.66 GPa | 531 ksi | 5 mm/min; ASTM D638 |
SABIC Innovative Plastics LNP THERMOCOMP MFB22S PP LNP* THERMOCOMP* MFB22S is a compound based on Polypropylene containing 10% Glass Fiber, 10% Glass Bead. Added feature of this grade is: Heat Stabilized. |
|||
Tensile Modulus | 3.66 GPa | 531 ksi | 5 mm/min; ASTM D 638 |
SABIC Innovative Plastics Noryl GTX GTX965 PPE+PA66 NORYL GTX965 is a mineral reinforced PPE/PA blend. It offers excellent surface appearance, processability and dimensional stability at elevated temperatures. The best molding condition for good appe.. |