Premix Thermoplastics PRE-ELEC® PP 1395

Category Polymer , Thermoplastic , Polypropylene (PP)
Manufacturer Premix Thermoplastics Inc.
Trade Name PRE-ELEC®
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Premix Thermoplastics PRE-ELEC® PP 1395.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
PRE-ELEC PP 1395 is a dissipative thermoplastic compound based on polypropylene. The electrical dissipation is achieved by using special conductive carbon black. In addition to stable surface resistance between 106-109 ohms PRE-ELEC PP 1395 has an excellent balance of mechanical properties and is easy to injection mould.Typical applications include injection molded crates, boxes, pallets and tote bins for electronic, automotive and chemical industry to prevent static charges. Test Specimen - 4.0 mm thick, 10.0 mm wide molded rod.Information provided by Premix Thermoplastics Inc.
Physical Properties Metric English Comments
Density 1.00 g/cc
0.0361 lb/in³
Linear Mold Shrinkage 0.013 - 0.016 cm/cm
0.013 - 0.016 in/in
ISO 294-4
Melt Flow 3.0 g/10 min

@Load 2.16 kg,
Temperature 230 °C
3.0 g/10 min

@Load 4.76 lb,
Temperature 446 °F
ISO 1133
16 g/10 min

@Load 5.00 kg,
Temperature 230 °C
16 g/10 min

@Load 11.0 lb,
Temperature 446 °F
ISO 1133
Mechanical Properties Metric English Comments
Hardness, Shore A 97
97
ISO 868
Hardness, Shore D 68
68
ISO 868
Tensile Strength, Ultimate 16.0 MPa
2320 psi
ISO 527
Tensile Strength, Yield 19.0 MPa
2760 psi
ISO 527
Elongation at Break 40 %
40 %
ISO 527
Elongation at Yield 9.0 %
9.0 %
ISO 527
Modulus of Elasticity 1.40 GPa
203 ksi
ISO 178
Izod Impact, Notched (ISO) 8.00 kJ/m²

@Thickness 4.00 mm,
Temperature -20.0 °C
3.81 ft-lb/in²

@Thickness 0.157 in,
Temperature -4.00 °F
ISO 180
40.0 kJ/m²

@Thickness 4.00 mm,
Temperature 23.0 °C
19.0 ft-lb/in²

@Thickness 0.157 in,
Temperature 73.4 °F
ISO 180
Izod Impact, Unnotched (ISO) 60.0 kJ/m²

@Thickness 4.00 mm,
Temperature -20.0 °C
28.6 ft-lb/in²

@Thickness 0.157 in,
Temperature -4.00 °F
ISO 180
NB

@Thickness 4.00 mm,
Temperature 23.0 °C
NB

@Thickness 0.157 in,
Temperature 73.4 °F
ISO 180
Thermal Properties Metric English Comments
Deflection Temperature at 0.46 MPa (66 psi) 82.0 °C
180 °F
ISO 75/Method Bf
Deflection Temperature at 1.8 MPa (264 psi) 51.0 °C
124 °F
ISO 75/Method Af
Vicat Softening Point 62.0 °C
144 °F
Rate B; ISO 306/B50
144 °C
291 °F
Rate A; ISO 306/A50
Electrical Properties Metric English Comments
Volume Resistivity 10000 - 1.00e+6 ohm-cm
10000 - 1.00e+6 ohm-cm
ISO D-257
Surface Resistance 1.00e+6 - 1.00e+9 ohm
1.00e+6 - 1.00e+9 ohm
ISO IEC 61340-5-1
Static Decay <= 2.0 sec
<= 2.0 sec
ISO IEC 61340-5-1
Processing Properties Metric English Comments
Melt Temperature 210 - 260 °C
410 - 500 °F
Mold Temperature 60.0 - 80.0 °C
140 - 176 °F
Drying Temperature 60.0 - 80.0 °C

@Time 7200 - 14400 sec
140 - 176 °F

@Time 2.00 - 4.00 hour
Pre-drying
Injection Pressure 60.0 - 80.0 MPa
8700 - 11600 psi
Shelf Life 12.0 Month
12.0 Month
Normal Storing Conditions
Descriptive Properties Value Comments
Injection Speed Moderate