Polymer Property : Modulus of Elasticity = 203 ksi Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.
Mechanical Properties Metric English Comments
Modulus of Elasticity 1.40 GPa
203 ksi
4 mm thick;10.0 mm wide molded rod; ISO 178
Premix Thermoplastics PRE-ELEC® PP 1386
PRE-ELEC PP 1386 is a conductive thermoplastic compound based on polypropylene. Conductivity is achieved by using special conductive carbon black. In addition to a low electrical resistivity PRE-ELE..
Modulus of Elasticity 1.40 GPa
203 ksi
ISO 178
Premix Thermoplastics PRE-ELEC® PP 1395
PRE-ELEC PP 1395 is a dissipative thermoplastic compound based on polypropylene. The electrical dissipation is achieved by using special conductive carbon black. In addition to stable surface resist..
Modulus of Elasticity 1.40 - 2.00 GPa
203 - 290 ksi
ASTM D638-04
Proto3000 Objet Digital Materials™ DM_8425 Rigid Opaque Prototyping Polymer
Primary material: VeroWhitePlusSecondary material: TangoPlusDigital Materials are made up of two Objet materials. The two materials are combined in specific concentrations and structures, to provide..
Modulus of Elasticity 1.40 - 2.00 GPa
203 - 290 ksi
ASTM D638-04
Proto3000 Objet Digital Materials™ DM_8505Gray50 Rigid Opaque Prototyping Polymer
Primary material: VeroWhitePlusSecondary material: TangoBlackPlusDigital Materials are made up of two Objet materials. The two materials are combined in specific concentrations and structures, to pr..
Modulus of Elasticity 1.40 GPa
203 ksi
DIN 53457
Ineos Nova S-6600MG Compact Polystyrene Microgranulates  (discontinued **)
High impact polystyrene Microgranulates, having a diameter of 0.8 - 1.0 mm especially useful for compounding and extrusion applications. Due to the higher viscosity intensive mixing with thermoplas..
Modulus of Elasticity 1.40 - 2.80 GPa
203 - 406 ksi
Average value: 2.10 GPa Grade Count:61
Overview of materials for Acrylonitrile Butadiene Styrene (ABS), Impact Grade, Molded
This property data is a summary of similar materials in the MatWeb database for the category "Acrylonitrile Butadiene Styrene (ABS), Impact Grade, Molded". Each property range of values reported is ..
Modulus of Elasticity 1.40 - 5.12 GPa
203 - 743 ksi
Average value: 2.33 GPa Grade Count:141
Overview of materials for Polycarbonate/Polybutylene Terephthalate (PBT) Blend, Unreinforced
This property data is a summary of similar materials in the MatWeb database for the category "Polycarbonate/Polybutylene Terephthalate (PBT) Blend, Unreinforced". Each property range of values repor..
Modulus of Elasticity 1.40 - 3.30 GPa
203 - 479 ksi
Average value: 2.46 GPa Grade Count:26
Overview of materials for Polypropylene with 40% Calcium Carbonate (CaCO3) Filler
This property data is a summary of similar materials in the MatWeb database for the category "Polypropylene with 40% Calcium Carbonate (CaCO3) Filler". Specific grades with primary filler content be..
Modulus of Elasticity 1.40 - 10.0 GPa
203 - 1450 ksi
Average value: 3.12 GPa Grade Count:6
Overview of materials for Nylon, Amorphous Transparent Alloy
This property data is a summary of similar materials in the MatWeb database for the category "Nylon, Amorphous Transparent Alloy". Each property range of values reported is minimum and maximum value..
Modulus of Elasticity 1.40 GPa

@Temperature -40.0 °C
203 ksi

@Temperature -40.0 °F
ASTM D638
Micropol Isoplas P501 Crosslinkable Polyethylene
Information provided by Micropol Limited
Modulus of Elasticity 1.40 GPa
203 ksi
ISO 527-2
Tisan TISOPLEN® 10% Calcite Filled Heat Stabilized Homopolymer Polypropylene
TISOPLEN has a wide area of application in furniture, durable goods, household appliances, electrics/electronics, and telecommunication industries. General specifications include Low densityLow mois..
Modulus of Elasticity 1.40 - 1.40 GPa

@Temperature 120 - 120 °C
203 - 203 ksi

@Temperature 248 - 248 °F
Average value: 1.40 GPa Grade Count:1
Overview of materials for Cellulose Acetate Propionate, Molded
This property data is a summary of similar materials in the MatWeb database for the category "Cellulose Acetate Propionate, Molded". Each property range of values reported is minimum and maximum val..
Modulus of Elasticity 1.40 - 5.17 GPa
203 - 750 ksi
Average value: 3.21 GPa Grade Count:45
Overview of materials for Polypropylene with 40% Talc Filler
This property data is a summary of similar materials in the MatWeb database for the category "Polypropylene with 40% Talc Filler". Specific grades with primary filler content between 35% and 44% are..