- AK Steel 15-5 PH® Precipitation Hardening Stainless Steel, Condition H 1075
AK Steel 15-5 PH® Precipitation Hardening Stainless Steel, Condition H 1075
| Category | Metal , Ferrous Metal , Martensitic , Stainless Steel , Precipitation Hardening Stainless |
| Manufacturer | AK Steel |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | AK Steel 15-5 PH® Precipitation Hardening Stainless Steel, Condition H 1075.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
AK Steel 15-5 PH® provides high strength, good corrosion resistance, good mechanical properties at temperatures up to 600°F (316°C), and good toughness in both base metal and welds. Short-time, low-temperature heat treatments minimize distortion and scaling. AK Steel 15-5 PH® is the ferrite-free version of AK Steel 17-4 PH® Stainless Steel. Both alloys are widely used in the aerospace, chemical, petrochemical, food processing, paper and general metalworking industries. The material supplied from the mill is in Condition A. After fabrication eight standard heat treatments have been developed to provide a wide range of properties.Information provided by AK Steel
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 7.81 g/cc | 0.282 lb/in³ |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell C | 38 | 38 | Longitudinal |
| 38 | 38 | Transverse | |
| Tensile Strength, Ultimate | 1114 MPa | 161600 psi | Longitudinal |
| 1114 MPa | 161600 psi | Transverse | |
| Tensile Strength, Yield | 1102 MPa @Strain 0.200 % |
159800 psi @Strain 0.200 % |
Longitudinal |
| 1112 MPa @Strain 0.200 % |
161300 psi @Strain 0.200 % |
Transverse | |
| Elongation at Break | 11.4 % | 11.4 % | in 2 inches, Transverse |
| 12.8 % | 12.8 % | in 2 inches, Longitudinal |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 11.3 µm/m-°C @Temperature 21.0 - 93.0 °C |
6.28 µin/in-°F @Temperature 69.8 - 199 °F |
|
| 12.2 µm/m-°C @Temperature <=427 °C |
6.78 µin/in-°F @Temperature <=801 °F |
| Component Elements Properties | Metric | English | Comments |
|---|---|---|---|
| Carbon, C | <= 0.070 % | <= 0.070 % | |
| Chromium, Cr | 14 - 15.5 % | 14 - 15.5 % | |
| Copper, Cu | 2.5 - 4.5 % | 2.5 - 4.5 % | |
| Iron, Fe | 71.91 - 79.85 % | 71.91 - 79.85 % | As Remainder |
| Manganese, Mn | <= 1.0 % | <= 1.0 % | |
| Nb + Ta | 0.15 - 0.45 % | 0.15 - 0.45 % | |
| Nickel, Ni | 3.5 - 5.5 % | 3.5 - 5.5 % | |
| Phosphorous, P | <= 0.040 % | <= 0.040 % | |
| Silicon, Si | <= 1.0 % | <= 1.0 % | |
| Sulfur, S | <= 0.030 % | <= 0.030 % |