Polykemi AB POLYfill PPC GF2007 PD1 Polypropylene Copolymer, Glass Fiber Reinforced, Chemically Coupled

Category Polymer , Thermoplastic , Polypropylene (PP) , Polypropylene Copolymer , Polypropylene with 10% Glass Fiber Filler
Manufacturer Polykemi AB
Trade Name POLYfill
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Polykemi AB POLYfill PPC GF2007 PD1 Polypropylene Copolymer, Glass Fiber Reinforced, Chemically Coupled.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Information provided by Polykemi AB
Physical Properties Metric English Comments
Density 0.940 g/cc
0.0340 lb/in³
ISO 1183
Filler Content 7 %
7 %
±2%; Polykemi
Melt Index of Compound 2.0 g/10 min

@Load 2.16 kg,
Temperature 230 °C
 2.0 g/10 min

@Load 4.76 lb,
Temperature 446 °F
 ISO 1133
Mechanical Properties Metric English Comments
Tensile Strength at Break <= 30.0 MPa
<= 4350 psi
ISO/R527
Elongation at Break 13 %
13 %
ISO/R527
Flexural Strength <= 50.0 MPa
<= 7250 psi
ISO 178
Flexural Modulus 2.00 GPa

@Temperature 23.0 °C
 290 ksi

@Temperature 73.4 °F
 ISO 178
Charpy Impact Unnotched 2.10 J/cm²

@Temperature -20.0 °C
 9.99 ft-lb/in²

@Temperature -4.00 °F
 ISO 179
2.30 J/cm²

@Temperature 23.0 °C
 10.9 ft-lb/in²

@Temperature 73.4 °F
 ISO 179
Charpy Impact, Notched 0.700 J/cm²

@Temperature -20.0 °C
 3.33 ft-lb/in²

@Temperature -4.00 °F
 ISO 179
1.20 J/cm²

@Temperature 23.0 °C
 5.71 ft-lb/in²

@Temperature 73.4 °F
 ISO 179
Thermal Properties Metric English Comments
Deflection Temperature at 0.46 MPa (66 psi) 140 °C
284 °F
120°C/h; ISO 75/1
Deflection Temperature at 1.8 MPa (264 psi) 74.0 °C
165 °F
120°C/h; ISO 75/1
Vicat Softening Point 154 °C

@Load 1.00 kg
 309 °F

@Load 2.21 lb
 50°C/h; ISO 306
Flammability, UL94 HB

@Thickness 3.20 mm
 HB

@Thickness 0.126 in
Glow Wire Test 650 °C

@Thickness 3.20 mm
 1200 °F

@Thickness 0.126 in
 IEC 695-2-1
Processing Properties Metric English Comments
Melt Temperature 205 - 260 °C
401 - 500 °F
Mold Temperature 40.0 - 80.0 °C
104 - 176 °F
Drying Temperature 70.0 - 80.0 °C
158 - 176 °F
Dry Time 2 - 4 hour
2 - 4 hour
in circulation dryer
2 - 4 hour
2 - 4 hour
in desiccant air dryer
Injection Pressure 40.0 - 110 MPa
5800 - 16000 psi
Back Pressure 1.00 - 2.00 MPa
145 - 290 psi
Descriptive Properties Value Comments
Holding Pressure () 20-40
% of injection pressure
Injection Speed () High