- Polymer Property : Tensile Strength at Break = 30.0 MPa
Polymer Property : Tensile Strength at Break = 30.0 MPa Product List
Mechanical PropertiesTips: 30 items are displayed at most. For the rest of the results, please contact customer service.
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | <= 30.0 MPa | <= 4350 psi | ISO/R527 |
| Polykemi AB POLYfill PP HIP16020FCF Polypropylene, Fast Cycle Information provided by Polykemi AB |
|||
| Tensile Strength at Break | 30.0 MPa | 4350 psi | ASTM D638 |
| Eastman Eastar GN125 Copolyester, Natural
(discontinued **) Eastar Copolyester GN125 is a glycol modified polyethylene terephthalate (PET) that contains an ultraviolet light inhibitor. This product is recommended for indoor applications requiring enhanced co.. |
|||
| Tensile Strength at Break | 30.0 MPa | 4350 psi | ISO 37 |
| Huntsman AVALON® 65 AB Thermoplastic Polyurethane Performance Features: AVALON® injection molding products are trusted worldwide to deliver:Outstanding flex performanceExcellent slip resistancePerfect surface definitionTransparency and transluce.. |
|||
| Tensile Strength at Break | 30.0 MPa | 4350 psi | ISO 37 |
| Huntsman AVALON® 65 AK-ESD Thermoplastic Polyurethane AVALON® ESD range are soft TPUs that deliver the improved bonding strength and mechanical properties required to produce high-quality footwear on roundtable machines – specifically safety sh.. |
|||
| Tensile Strength at Break | 30.0 MPa | 4350 psi | DIN 53504 |
| Huntsman IROGRAN® A 70 E 4675 Polyester-Based TPU-High Performance Grade Introduction: IROGRAN A 70 E 4675 is a softener free thermoplastic special-polyester-polyurethane for injection molding applications. Additional characteristics of the product are very short cycle t.. |
|||
| Tensile Strength at Break | 30.0 - 50.0 MPa | 4350 - 7250 psi | ISO 527 |
| Manifattura Cattaneo PVDF Manifattura Cattaneo products are available in semi-finished forms such as bars, profiles, sheets and plates.Information provided by Manifattura Cattaneo s.p.a. |
|||
| Tensile Strength at Break | 30.0 - 50.0 MPa | 4350 - 7250 psi | |
| GrafTech GRAFCELL® FFP-100 SERIES Flow Field Plate Graphite Manufactured from expanded natural graphite, GRAFCELL® Flow Field Plate (FFP) components retain a continuous graphitic phase. This phase continuity, combined with a low contact resistance, provid.. |
|||
| Tensile Strength at Break | 30.0 - 32.0 MPa | 4350 - 4640 psi | ASTM D683 |
| Loxim 820 02T HB Polypropylene Compound, 20% Talc Filled, Flame Retardant Information provided by Loxim Industries |
|||
| Tensile Strength at Break | 30.0 MPa | 4350 psi | DIN 53504 |
| Huntsman IROGRAN® A 80 P 4699L Ether-Based TPU-For Cable Industry Introduction: IROGRAN A 80 P 4699 L is a high performance polyether based thermoplastic polyurethane intended for extrusion and injection mold applications. IROGRAN A 80 P 4699 L is part of the HUNT.. |
|||
| Tensile Strength at Break | 30.0 MPa | 4350 psi | ISO 527 |
| Iran Petrochemical (PCC) I3 HC 7260(THE) High Density Polyethylene I3 (HC 7260) is a high density polyethylene with propylene as comonomer. The product has good impact strength, good stress cracking resistance, low warping and good flow ability as well as high dens.. |
|||
| Tensile Strength at Break | 30.0 MPa | 4350 psi | |
| LATI Laticonther 47/1 CP/80 PP Copolymer High thermal conductivity product based on Polypropylene copolymer (PPc). Special filler. Extrusion and molding injection grade.Availability: Africa & Middle East; Asia Pacific; Europe; Latin Americ.. |
|||
| Tensile Strength at Break | 30.0 MPa | 4350 psi | |
| LATI Latistat 52/7-02 MI/30 PP Homopolymer, 30% Mica Filled Dissipative product based on Polypropylene homopolymer (PPh). Mica filler. Availability: Africa & Middle East; Asia Pacific; Europe; Latin America; North AmericaInformation provided by Lati Industri.. |
|||
| Tensile Strength at Break | 30.0 MPa @Temperature 23.0 °C |
4350 psi @Temperature 73.4 °F |
50mm/min; ISO 527-2/1A/50 |
| SYNTHOS Forsan® 548 Acrylonitrile Butadiene Styrene (ABS) Easy flow, glossy, impact resistant.Applications: General purposeVarious technical parts, household appliances, hobby and office equipment, etc.Synthos was formerly known as Kaucuk. All information .. |
|||
| Tensile Strength at Break | 30.0 - 50.0 MPa @Thickness 2.00 mm |
4350 - 7250 psi @Thickness 0.0787 in |
50 mm/min; ASTM D638 |
| Solvay Specialty Polymers Solef® 9007 Polyvinylidene Fluoride (PVDF) Solef® 9007 PVDF homopolymer has low viscosity and is used in film extrusion and injection molding.Features: Homopolymer; Low ViscosityAdditional Properties: Crystallization Heat - ASTM D3418 53... |
|||
| Tensile Strength at Break | 30.0 MPa | 4350 psi | 0.2 in/min; ASTM Test |
| Styrolution Terblend® N NM-11 ABS/PA6 (Conditioned) Terblend N NM-11 is an ABS/PA6 blend combining very high impact strength, even at low temperatures, with an excellent processability and surface appearance.Information provided by STYROLUTION, which.. |
|||
| Tensile Strength at Break | 30.0 MPa | 4350 psi | ASTM D638 |
| Toyobo PELPRENE™ P55U Polyester TPE, Weather-resistant Features: Polyester TPE, Weather-resistantInformation provided by Toyobo. |
|||
| Tensile Strength at Break | 30.0 MPa | 4350 psi | |
| UBE UBEPOL BR15H HIPS (n-DM = 0.03 wt % and PH-3H = 0.03 wt %) Description: UBEPOL-BR15H is a in-between polymer of UBEPOL-BR15HB and UBEPOL-BR15HL.Information provided by UBE. |
|||
| Tensile Strength at Break | 30.0 MPa | 4350 psi | conditioned; ISO 527-1/-2 |
| EMS-Grivory Grivory® XE 3841 nat PA12 Product description: Grilamid XE 3841 is a flexible, heat stabilized and plasticizer-free Polyamide 12, which offers a very good processability for extrusion. Grilamid XE 3841 is qualified in Europe.. |
|||
| Tensile Strength at Break | 30.0 MPa | 4350 psi | 50 mm/min; ISO 527 |
| Chi Mei Polyrex® PH-888H Polystyrene - High Impact High FDI; high heat |
|||
| Tensile Strength at Break | 30.0 MPa @Temperature 23.0 °C |
4350 psi @Temperature 73.4 °F |
ISO 527 (1BA bar) |
| DuPont Performance Polymers Hytrel® G5564 TPC-ET
(Unverified Data**) Hytrel® G5564 is a 55 nom. Shore D, heat stable, plasticiser free high viscosity resin for extrusion; low temperature impact resistance as well as excellent mechanical properties; good hydrocarbon .. |
|||
| Tensile Strength at Break | 30.0 MPa | 4350 psi | ASTM D638 |
| Aclo Accutech Polypropylene Homopolymer HP0336W20L Wollastonite Reinforced |
|||
| Tensile Strength at Break | >= 30.0 MPa | >= 4350 psi | ASTM D638 |
| Braskem UTEC® 4041 Ultra High Molecular Weight Polyethylene Applications which require a good combination between impact and wear resistance - use of pigments and/or additives - technical and porous parts, filters, compression molded sheets.Information provi.. |
|||
| Tensile Strength at Break | 30.0 MPa | 4350 psi | ISO R 527 |
| Addiplast Addilene H 410 Polypropylene Homopolymer UnreinforcedInformation provided by Addiplast. |
|||
| Tensile Strength at Break | 30.0 MPa | 4350 psi | Conditioned; ISO R 527 |
| Addiplast Addinyl B2H G30 Flame Retardant Nylon 6, 30% Glass Bead Flame retardant, 30% glass bead filled, with halogensInformation provided by Addiplast. |
|||
| Tensile Strength at Break | 30.0 MPa @Temperature 80.0 °C |
4350 psi @Temperature 176 °F |
ISO Data |
| BASF Ultramid® 8202C PA6 (Conditioned) Ultramid 8202C is a modified crystalline and low viscosity, nylon 6 injection molding homopolymer. It is also available in heat stabilized (Ultamid 8202C HS) and/or pigmented versions. Its unique .. |
|||
| Tensile Strength at Break | 30.0 MPa @Temperature 80.0 °C |
4350 psi @Temperature 176 °F |
ISO Data |
| BASF Ultramid® 8231G HS BK-102 14% Glass Filled PA6 (Conditioned) Ultramid 8231G HS BK-102 is a black pigmented heat stabilized, 14% glass fiber reinforced PA6 injection molding compound.The glass fiber reinforcement enhances performance such as strength, stiffnes.. |
|||
| Tensile Strength at Break | >= 30.0 MPa | >= 4350 psi | ASTM D638 |
| Braskem Idealis 500 High Molecular Weight Polyethylene Powder Braskem Idealis 500 is the only High Molecular Weight Polyethylene resin in powder form specially designed for the compression molding process; Applications range from food handling cutting boards a.. |
|||
| Tensile Strength at Break | 30.0 MPa | 4350 psi | DIN EN ISO 527-3 |
| 3M Dyneon™ TF 2021Z PTFE Fine Powder Dyneon TF 2021 Z PTFE is an ideal grade for pipe liner applications because of its outstanding green strength. It is the preferred grade for unsintered thread sealing tapes, expanded join sealings, .. |
|||
| Tensile Strength at Break | 30.0 MPa @Temperature 23.0 °C |
4350 psi @Temperature 73.4 °F |
50 mm/min; ASTM D638 |
| Solvay Specialty Polymers Solef® 41308 Polyvinylidene Fluoride (PVDF)
(Unverified Data**) Solef® 41308/0001 PVDF is specifically developed for coextrusion.Information provided by Solvay Specialty Polymers. |
|||
| Tensile Strength at Break | 30.0 MPa | 4350 psi | ISO R 527 |
| Fainplast Compounds RE 236 Rigid PVC, Extrusion Electric channels |
|||