PolyOne Versollan™ OM 1255NX-9 Thermoplastic Elastomer (TPE)

Category Polymer , Thermoplastic , Elastomer, TPE
Manufacturer PolyOne Corporation
Trade Name Versollan™
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF PolyOne Versollan™ OM 1255NX-9 Thermoplastic Elastomer (TPE).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Versollan™ OM 1255NX-9 is a performance TPU alloy designed for thin wall overmolding onto polycarbonate (PC), ABS and PC/ABS substrates. - Improved Grip with Matte, Rubbery Finish - Superior Adhesion to PC, ABS, PC/ABS, PC/PBT and CopolyesterPurge thoroughly before and after use of this product with a low flow (0.5 - 2.5 MFR) polyethylene (PE) or polypropylene (PP). Regrind levels up to 20% can be used with Versollan™ OM 1255NX-9 with minimal property loss, provided that the regrind is free of contamination. To minimize losses during molding, the melt temperature should remain as low as possible. The final determination of regrind effectiveness should be determined by the customer. The Versollan™ OM 1255NX-9 should not be left in the barrel for extended idle periods (greater than 5 minutes). Suggested Dewpoint: -40°F Injection Speed: 0.5 to 2 in/sec 1st Stage - Boost Pressure: 200 to 800 psi 2nd Stage - Hold Pressure: 30% of Boost Hold Time (Thick Part): 4 to 10 sec Hold Time (Thin Part): 1 to 3 secInformation provided by PolyOne
Physical Properties Metric English Comments
Specific Gravity 1.05 g/cc
1.05 g/cc
ASTM D792
Viscosity 16700 cP

@Shear Rate 11200 1/s,
Temperature 200 °C
16700 cP

@Shear Rate 11200 1/s,
Temperature 392 °F
ASTM D3835
Maximum Moisture Content 0.020 - 0.030
0.020 - 0.030
Linear Mold Shrinkage, Flow 0.011 - 0.017 cm/cm
0.011 - 0.017 in/in
ASTM D955
Melt Flow 6.0 g/10 min

@Load 2.16 kg,
Temperature 190 °C
6.0 g/10 min

@Load 4.76 lb,
Temperature 374 °F
ASTM D1238
60 g/10 min

@Load 5.00 kg,
Temperature 200 °C
60 g/10 min

@Load 11.0 lb,
Temperature 392 °F
ASTM D1238
Mechanical Properties Metric English Comments
Hardness, Shore A 59
59
10 sec; ASTM D2240
Tensile Strength at Break 6.58 MPa

@Temperature 23.0 °C
954 psi

@Temperature 73.4 °F
Die C2 hr; ASTM D412
Tensile Stress 1.93 MPa

@Strain 100 %,
Temperature 23.0 °C
280 psi

@Strain 100 %,
Temperature 73.4 °F
Die C2 hr; ASTM D412
3.39 MPa

@Strain 300 %,
Temperature 23.0 °C
492 psi

@Strain 300 %,
Temperature 73.4 °F
Die C2 hr; ASTM D412
Elongation at Break 650 %

@Temperature 23.0 °C
650 %

@Temperature 73.4 °F
Die C2 hr; ASTM D412
Tear Strength 38.5 kN/m
220 pli
ASTM D624
Compression Set 24 %

@Temperature 23.0 °C,
Time 79200 sec
24 %

@Temperature 73.4 °F,
Time 22.0 hour
ASTM D395B
Thermal Properties Metric English Comments
Brittleness Temperature -68.5 °C
-91.3 °F
Thickness = 1.90mm Conditioned for 40hrs at 23C at 50% RH; ASTM D746
Flammability, UL94 HB

@Thickness 1.50 mm
HB

@Thickness 0.0591 in
UL 94
Processing Properties Metric English Comments
Rear Barrel Temperature 163 - 188 °C
325 - 370 °F
Middle Barrel Temperature 182 - 199 °C
360 - 390 °F
Front Barrel Temperature 188 - 210 °C
370 - 410 °F
Nozzle Temperature 193 - 216 °C
379 - 421 °F
Mold Temperature 21.1 - 48.9 °C
70.0 - 120 °F
Drying Temperature 51.7 - 54.4 °C
125 - 130 °F
Dry Time 3.00 - 4.00 hour
3.00 - 4.00 hour
Back Pressure 0.000 - 0.552 MPa
0.000 - 80.1 psi
Screw Speed 75 - 125 rpm
75 - 125 rpm
Descriptive Properties Value Comments
Agency Ratings UL 94 .QMFZ2.E76261
Appearance Black
Features Good Moldability
Good Processability
Low Gloss
Forms Pellets
Generic Material TPE
Generic Name Thermoplastic Elastomer (TPE)
Manufacturer / Supplier GLS Thermoplastic Elastomers
Processing Method Injection Molding
Regional Availability Africa & Middle East
Asia Pacific
Europe
North America
South America
RoHS Compliance RoHS Compliant
Suggested Max Regrind 20%
Uses Business Equipment
Consumer Applications
Electrical/Electronic Applications
Flexible Grips
Overmolding
Power/Other Tools
Thin-walled Parts