PolyOne LubriOne™ ATH-000/04S Acetal (POM) Homopolymer

Category Polymer , Thermoplastic , Acetal (POM) , Acetal Homopolymer, Unreinforced
Manufacturer PolyOne Corporation
Trade Name LubriOne™
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF PolyOne LubriOne™ ATH-000/04S Acetal (POM) Homopolymer.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
LubriOne™ Lubricated and Wear-Resistant Compounds have been specifically formulated to be self-lubricating materials, offering low coefficient of friction and improved wear resistance properties. LubriOne compounds have been demonstrated to reduce friction, noise, vibration, heat buildup and improve product durability.Information provided by PolyOne
Physical Properties Metric English Comments
Specific Gravity 1.39 g/cc
1.39 g/cc
ASTM D792
Linear Mold Shrinkage, Flow 0.020 - 0.040 cm/cm
0.020 - 0.040 in/in
ASTM D955
Linear Mold Shrinkage, Transverse 0.010 - 0.030 cm/cm
0.010 - 0.030 in/in
ASTM D955
Mechanical Properties Metric English Comments
Tensile Strength at Break 50.3 MPa
7300 psi
Type I, 5.1 mm/min; ASTM D638
Tensile Strength, Yield 50.3 MPa
7300 psi
Type I, 5.1 mm/min; ASTM D638
Elongation at Break 4.0 %
4.0 %
Type I, 5.1 mm/min; ASTM D638
Tensile Modulus 1.93 GPa
280 ksi
Type I, 5.1 mm/min; ASTM D638
Flexural Strength 75.8 MPa
11000 psi
1.3 mm/min; ASTM D790
Flexural Modulus 2.27 GPa
329 ksi
1.3 mm/min; ASTM D790
Izod Impact, Notched 0.530 J/cm

@Thickness 6.35 mm,
Temperature 23.0 °C
0.993 ft-lb/in

@Thickness 0.250 in,
Temperature 73.4 °F
Injection Molded; ASTM D256A
Coefficient of Friction, Dynamic 0.11
0.11
vs. Steel - Dynamic; ASTM D1894
Coefficient of Friction, Static 0.15
0.15
vs. Steel - Static; ASTM D1894
Thermal Properties Metric English Comments
Deflection Temperature at 0.46 MPa (66 psi) 158 °C
316 °F
Unannealed; ASTM D648
Deflection Temperature at 1.8 MPa (264 psi) 86.7 °C
188 °F
Unannealed; ASTM D648
Processing Properties Metric English Comments
Mold Temperature 60.0 - 71.1 °C
140 - 160 °F
Drying Temperature 71.1 °C
160 °F
Dry Time 2.00 hour
2.00 hour
Descriptive Properties Value Comments
Features Homopolymer
Low Friction
Lubricated
Forms Pellets
Generic Material Acetal (POM) Homopolymer
Generic Name Acetal (POM) Homopolymer
Regional Availability Africa & Middle East
Asia Pacific
Europe
North America
South America
RoHS Compliance RoHS Compliant
Uses Appliance Components
Automotive Applications
Bearings
Business Equipment
Consumer Applications
Conveyor Parts
Gears
Industrial Applications
Printer Parts
Pulleys
Rollers