Songhan Plastic Technology Co.,Ltd.
 POLYMER SEARCH

Polymer Property : Tensile Strength at Break = 7300 psi Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.
Mechanical Properties Metric English Comments
Tensile Strength at Break 50.3 MPa
7300 psi
Type I, 5.1 mm/min; ASTM D638
PolyOne LubriOne™ ATH-000/04S Acetal (POM) Homopolymer
LubriOne™ Lubricated and Wear-Resistant Compounds have been specifically formulated to be self-lubricating materials, offering low coefficient of friction and improved wear resistance properties. L..
Tensile Strength at Break 50.3 MPa
7300 psi
2 in/min; ASTM D638
RheTech Products GC10P100-00 10% Glass Fiber Reinforced Polypropylene, Chemically Coupled, Natural
Applications: Air ducts - distributionFuel filler pocketsInjection molding conditions reported in table.Information provided by RheTech Products.
Tensile Strength at Break 50.3 MPa
7300 psi
2 in/min; ASTM D638
RheTech Products GC10P100-01 10% Glass Fiber Reinforced Polypropylene, Chemically Coupled, Black
Applications: Air ducts - distributionFuel filler pocketsInjection molding conditions reported in table.Information provided by RheTech Products.
Tensile Strength at Break 50.3 MPa
7300 psi
Type I, 5.1 mm/min; ASTM D638
PolyOne Nymax™ 1010 A Black 13 Polyamide 6 (Nylon 6)
The Nymax® Series of nylon 6 compounds have been specifically developed to deliver outstanding performance in a wide range of application areas. These materials are available with a broad range of ..
Tensile Strength at Break 50.3 MPa
7300 psi
ASTM D638
Polymer Resources NY66-IM2-[color]-H Impact Modified Nylon 66, Heat Stabilized
Nylon 66, Superior Impact Modified, Heat Stabilized, LubricatedProcess: Injection MoldingNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, test samples. ..
Tensile Strength at Break 50.3 MPa
7300 psi
ASTM D638
Polymer Resources PC/TP-GP2 PC/Polyester Alloy
High Impact, Excellent Chemical ResistanceProcess: Injection MoldingNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, test samples.Information provided b..
Tensile Strength at Break 50.3 MPa
7300 psi
ASTM D638
Polymer Resources PC/TP-GP2-[color]-UV PC/Polyester Alloy, UV-stabilized
High Impact, Excellent Chemical Resistance, UV-stabilizedProcess: Injection MoldingNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, test samples.Informa..
Tensile Strength at Break 50.3 MPa
7300 psi
ASTM D638
Polymer Resources PPX-FR2-[color]EN Modified PPO, UL 94 V-1 with HDT of 210 F, Extrusion Grade
Process: ExtrusionNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, test samples. Information provided by Polymer Resources Corporation.
Tensile Strength at Break 50.3 MPa
7300 psi
ASTM D638
Polymer Resources NY66-IM2 Impact Modified Nylon 66
Nylon 66, Superior Impact Modified, LubricatedProcess: Injection MoldingNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, test samples. Nylon grades are ..
Tensile Strength at Break >= 50.3 MPa
>= 7300 psi
Resin Technology Group TIGA 110-EXDP Low Viscosity, Optically Clear Glass Bonder
Mix ratio 100/50 by volume.TIGA 110EX-DP is a transparent, low viscosity epoxy resin formulation recommended for industrial adhesive, small potting and laminating applications where sparkling clarit..
Tensile Strength at Break 50.3 MPa
7300 psi
ASTM D638
LG Chemical Lupox® PBT-HI1002F Impact Modified, Flame Retardant PBT Alloy
Information provided by US distributor Polymer Technology and Services, LLC (PTS).
Tensile Strength at Break 50.3 MPa
7300 psi
2.0 in/min; ASTM D638
LTL Color Compounds ColorFast® PAHF Polycarbonate-ABS Alloy
General purpose HB-rated PC/ABS with improved chemical resistanceAll information provided by LTL Color Compounders, Inc.
Tensile Strength at Break 50.3 MPa
7300 psi
100% Ret.
UBE UBESTA® 3030U Nylon 12 (After Hexane for 500 hours)
Description: UBESTA has a strong resistance to chemicals. Under normal conditions, it is not significantly affected by alkalis, alcohols, ethers, ketones, hydrocarbons, lubricating oils, gasoline, c..
Tensile Strength at Break 50.3 MPa
7300 psi
ASTM D412
Compuestos Dominicanos Polycom PW-103099 PVC Compound
Compuestos Dominicanos' rigid PVC compounds for the extrusion of pipes have excellent processing characteristics and are available in the form of pellets and dry-blend. Also available are compounds..
Tensile Strength at Break 50.3 MPa
7300 psi
ASTM D638
Polymer Resources PPX-FR2 Modified PPO, UL 94 V-1 with HDT of 210 F  (Unverified Data**)
Process: Injection MoldingNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, test samples. Information provided by Polymer Resources Corporation.