PolyOne Edgetek® 5209 Black 30 A 1 Acetal (POM) Copolymer

Category Polymer , Thermoplastic , Acetal (POM)
Manufacturer PolyOne Corporation
Trade Name Edgetek®
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF PolyOne Edgetek® 5209 Black 30 A 1 Acetal (POM) Copolymer.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
The Edgetek® Engineering Thermoplastic Compounds portfolio covers a broad range of standard and custom-formulated high performance materials. This portfolio includes high-temperature materials for elevated service temperature environments, high-modulus / structural materials for load-bearing and high-strength applications and flame-retardant products. These compounds are based on select engineering thermoplastic resins that are compounded with reinforcing additives such as carbon fiber, glass fiber and glass beads.Information provided by PolyOne
Physical Properties Metric English Comments
Specific Gravity 1.41 g/cc
1.41 g/cc
ASTM D792
Water Absorption 0.20 %

@Thickness 3.18 mm
0.20 %

@Thickness 0.125 in
@ 24 hrs; ASTM D570
Linear Mold Shrinkage, Flow 0.025 - 0.027 cm/cm
0.025 - 0.027 in/in
ASTM D955
Melt Flow 8.2 g/10 min

@Load 2.16 kg,
Temperature 190 °C
8.2 g/10 min

@Load 4.76 lb,
Temperature 374 °F
Procedure A; ASTM D1238
Mechanical Properties Metric English Comments
Tensile Strength, Yield 65.5 MPa
9500 psi
Type I, 5.1 mm/min; ASTM D638
Elongation at Break 40 %
40 %
Type I, 5.1 mm/min; ASTM D638
Tensile Modulus 2.52 GPa
365 ksi
Type I, 5.1 mm/min; ASTM D638
Flexural Strength 89.6 MPa
13000 psi
ASTM D790
Flexural Modulus 2.52 GPa
365 ksi
ASTM D790
Izod Impact, Notched 0.690 J/cm

@Thickness 3.18 mm,
Temperature 23.0 °C
1.29 ft-lb/in

@Thickness 0.125 in,
Temperature 73.4 °F
Injection Molded; ASTM D256A
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 86.0 µm/m-°C
47.8 µin/in-°F
ASTM D696
Deflection Temperature at 1.8 MPa (264 psi) 110 °C

@Thickness 3.18 mm
230 °F

@Thickness 0.125 in
Unannealed; ASTM D648
Processing Properties Metric English Comments
Melt Temperature 188 - 210 °C
370 - 410 °F
Mold Temperature 48.9 - 82.2 °C
120 - 180 °F
Drying Temperature 82.2 °C
180 °F
Dry Time 2.00 hour
2.00 hour
Descriptive Properties Value Comments
Appearance Black
Features Copolymer
General Purpose
Good Wear Resistance
Low Friction
Forms Pellets
Generic Material Acetal (POM) Copolymer
Generic Name Acetal (POM) Copolymer
Processing Method Injection Molding
Regional Availability Africa & Middle East
Asia Pacific
Europe
North America
South America
Uses Automotive Applications
Bearings
Business Equipment
Consumer Applications
Gears
General Purpose
Industrial Applications
Pulleys
Rollers