Outokumpu 4841 High Temperature Austenitic Stainless Steel
| Category | Metal , Ferrous Metal , Austenitic , Stainless Steel |
| Manufacturer | Outokumpu |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Outokumpu 4841 High Temperature Austenitic Stainless Steel.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Variant of 1.4845 with an increased silicon content which enhances the steel's resistance to oxidation/corrosion but has also made it more susceptible to embrittlement.Applications: Heat and creep resistance. For use over 550°C for equipment and components within: Iron, steel, and non-ferrous industriesEngineering industryEnergy conservation plantsCement industryAvailable in hot rolled plate (Quarto) form.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 7.80 g/cc | 0.282 lb/in³ | RT |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Ultimate | 595 MPa | 86300 psi | Outokumpu Typical, Hot Rolled Plate (Quarto); EN 10002-1 |
| Tensile Strength, Yield | 275 MPa @Strain 0.200 % |
39900 psi @Strain 0.200 % |
Outokumpu Typical,Hot Rolled Plate (Quarto); EN 10002-1 |
| 315 MPa @Strain 1.00 % |
45700 psi @Strain 1.00 % |
Outokumpu Typical,Hot Rolled Plate (Quarto); EN 10002-1 | |
| Elongation at Break | 55 % | 55 % | Outokumpu Typical, Hot Rolled Plate (Quarto); EN 10002-1 |
| Rupture Strength | 10.0 MPa @Temperature 900 °C, Time 3.60e+7 sec |
1450 psi @Temperature 1650 °F, Time 10000 hour |
|
| 14.0 MPa @Temperature 850 °C, Time 3.60e+7 sec |
2030 psi @Temperature 1560 °F, Time 10000 hour |
||
| 20.0 MPa @Temperature 800 °C, Time 3.60e+7 sec |
2900 psi @Temperature 1470 °F, Time 10000 hour |
||
| 28.0 MPa @Temperature 750 °C, Time 3.60e+7 sec |
4060 psi @Temperature 1380 °F, Time 10000 hour |
||
| 40.0 MPa @Temperature 700 °C, Time 3.60e+7 sec |
5800 psi @Temperature 1290 °F, Time 10000 hour |
||
| 65.0 MPa @Temperature 650 °C, Time 3.60e+7 sec |
9430 psi @Temperature 1200 °F, Time 10000 hour |
||
| 130 MPa @Temperature 600 °C, Time 3.60e+7 sec |
18900 psi @Temperature 1110 °F, Time 10000 hour |
||
| Modulus of Elasticity | 196 GPa | 28400 ksi | RT |
| 120 GPa @Temperature 1000 °C |
17400 ksi @Temperature 1830 °F |
||
| 158 GPa @Temperature 500 °C |
22900 ksi @Temperature 932 °F |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 18.8 µm/m-°C @Temperature 500 °C |
10.4 µin/in-°F @Temperature 932 °F |
|
| 20.0 µm/m-°C @Temperature 1000 °C |
11.1 µin/in-°F @Temperature 1830 °F |
||
| Specific Heat Capacity | 0.470 J/g-°C | 0.112 BTU/lb-°F | RT |
| 0.530 J/g-°C @Temperature 500 °C |
0.127 BTU/lb-°F @Temperature 932 °F |
||
| Thermal Conductivity | 11.9 W/m-K | 82.6 BTU-in/hr-ft²-°F | RT |
| 27.8 W/m-K @Temperature 1000 °C |
193 BTU-in/hr-ft²-°F @Temperature 1830 °F |
||
| Maximum Service Temperature, Air | 1125 °C | 2057 °F | Dry Air |
| Component Elements Properties | Metric | English | Comments |
|---|---|---|---|
| Carbon, C | 0.020 % | 0.020 % | |
| Chromium, Cr | 25 % | 25 % | |
| Iron, Fe | 54.98 % | 54.98 % | |
| Nickel, Ni | 20 % | 20 % |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Electrical Resistivity | 0.0000960 ohm-cm | 0.0000960 ohm-cm | RT |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Annealing Temperature | 1040 - 1070 °C | 1900 - 1960 °F | Stress Relief Annealing (min. 0.5 h) |
| 1050 - 1150 °C | 1920 - 2100 °F | Solution Annealing |