Polymer Property : CTE, linear = 10.4 µin/in-°F Product List

Thermal Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Thermal Properties	Metric	English
CTE, linear	18.8 µm/m-°C @Temperature 500 °C	10.4 µin/in-°F @Temperature 932 °F
Outokumpu 4841 High Temperature Austenitic Stainless Steel Variant of 1.4845 with an increased silicon content which enhances the steel's resistance to oxidation/corrosion but has also made it more susceptible to embrittlement.Applications: Heat and creep r..
CTE, linear	18.7 µm/m-°C @Temperature 0.000 - 649 °C	10.4 µin/in-°F @Temperature 32.0 - 1200 °F
Crucible Steel 303 Plus Chromium-Nickel Steel Crucible 303 Plus is a non-hardenable austenitic chromium-nickel steel to which elements have been added to improve machinability and non-galling characteristics. Better machinability than that of..
CTE, linear	18.7 µm/m-°C @Temperature 0.000 - 649 °C	10.4 µin/in-°F @Temperature 32.0 - 1200 °F
Crucible Steel 303 SE Chromium-Nickel Steel Crucible 303 SE is a non-hardenable austenitic chromium-nickel steel to which selenium has been added to improve machinability and non-galling characteristics. This grade is non-magnetic in the anne..
CTE, linear	18.7 µm/m-°C @Temperature 0.000 - 649 °C	10.4 µin/in-°F @Temperature 32.0 - 1200 °F
Crucible Steel 304L Chromium-Nickel Steel Crucible 304L is a non-hardenable, low carbon austenitic chromium-nickel steel designed for special applications. It is particularly suitable for applications requiring welding operations where it i..
CTE, linear	18.7 µm/m-°C @Temperature <=649 °C	10.4 µin/in-°F @Temperature <=1200 °F
AK Steel 301 Austenitic Stainless steel AK Steel 301 provides high strength and good ductility when cold worked. It is a modification of AK Steel 302 to increase the cold work-hardening range, to permit higher tensile strengths to be ach..
CTE, linear	18.7 µm/m-°C @Temperature <=649 °C	10.4 µin/in-°F @Temperature <=1200 °F
AK Steel 304 Austenitic Stainless steel AK Steel 304 is a variation of the basic 18-8 grade, Type 302. Lower carbon, in Type 304, minimizes chromium carbide precipitation due to welding and its susceptibility to intergranular corrosion. ..
CTE, linear	18.7 µm/m-°C @Temperature <=649 °C	10.4 µin/in-°F @Temperature <=1200 °F
AK Steel 304L Austenitic Stainless steel AK Steel 304L is an extra low-carbon variation of Type 304, that eliminates carbide precipitation due to welding. AK Steel 304L can be used in the "as-welded" condition, even in severe corrosive co..
CTE, linear	18.7 µm/m-°C @Temperature <=649 °C	10.4 µin/in-°F @Temperature <=1200 °F
AK Steel 305 Austenitic Stainless steel AK Steel 305 can be spun and deep drawn more easily due to an increased nickel content that decreases work hardening. It is non-magnetic and cannot be hardened by heat treatment. Typical uses incl..