- Polymer Property : Specific Heat Capacity = 0.112 BTU/lb-°F
Polymer Property : Specific Heat Capacity = 0.112 BTU/lb-°F Product List
Thermal PropertiesTips: 30 items are displayed at most. For the rest of the results, please contact customer service.
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Heat Capacity | 0.470 J/g-°C | 0.112 BTU/lb-°F | RT |
| Outokumpu 4828 High Temperature Austenitic Stainless Steel Standardized high temperature steel for service at temperatures of up to 950-1000°C in dry air. Utilization in the temperature range of 600-900°C can lead to embrittlement.Applications: Heat and .. |
|||
| Specific Heat Capacity | 0.470 J/g-°C | 0.112 BTU/lb-°F | RT |
| Outokumpu 4833 High Temperature Austenitic Stainless Steel Standardized high temperature steel for service at temperatures of up to 950-1000°C in dry air. Utilization in the temperature range of 600-900°C can lead to embrittlement.Applications: Heat and .. |
|||
| Specific Heat Capacity | 0.470 J/g-°C | 0.112 BTU/lb-°F | RT |
| Outokumpu 4841 High Temperature Austenitic Stainless Steel Variant of 1.4845 with an increased silicon content which enhances the steel's resistance to oxidation/corrosion but has also made it more susceptible to embrittlement.Applications: Heat and creep r.. |
|||
| Specific Heat Capacity | 0.470 J/g-°C | 0.112 BTU/lb-°F | RT |
| Outokumpu 4845 High Temperature Austenitic Stainless Steel Standardized high-temperature steel for use at temperatures up to 1100°C in dry air. Prone to embrittlement after exposure between 600-900°C. Applications: Heat and creep resistance. For use o.. |
|||
| Specific Heat Capacity | 0.470 J/g-°C @Temperature 100 °C |
0.112 BTU/lb-°F @Temperature 212 °F |
|
| Haynes 214® alloy, 0% cold reduction Intended principally for use at temperatures of 955°C and above, exhibits resistance to oxidation that exceeds virtually all conventional heat-resistant wrought alloys. Applications include mesh .. |
|||
| Specific Heat Capacity | 0.470 J/g-°C @Temperature 100 °C |
0.112 BTU/lb-°F @Temperature 212 °F |
|
| Haynes 214® alloy, 10% cold reduction Intended principally for use at temperatures of 955°C and above, exhibits resistance to oxidation that exceeds virtually all conventional heat-resistant wrought alloys. Applications include mesh .. |
|||
| Specific Heat Capacity | 0.470 J/g-°C @Temperature 100 °C |
0.112 BTU/lb-°F @Temperature 212 °F |
|
| Haynes 214® alloy, 10% cold reduction, 925°C for 5 minutes Intended principally for use at temperatures of 955°C and above, exhibits resistance to oxidation that exceeds virtually all conventional heat-resistant wrought alloys. Applications include mesh .. |
|||
| Specific Heat Capacity | 0.470 J/g-°C @Temperature 100 °C |
0.112 BTU/lb-°F @Temperature 212 °F |
|
| Haynes 214® alloy, 10% cold reduction, 980°C (1800°F) for 5 minutes Intended principally for use at temperatures of 955°C and above, exhibits resistance to oxidation that exceeds virtually all conventional heat-resistant wrought alloys. Applications include mesh .. |
|||
| Specific Heat Capacity | 0.470 J/g-°C @Temperature 100 °C |
0.112 BTU/lb-°F @Temperature 212 °F |
|
| Haynes 214® alloy, 20% cold reduction Intended principally for use at temperatures of 955°C and above, exhibits resistance to oxidation that exceeds virtually all conventional heat-resistant wrought alloys. Applications include mesh .. |
|||
| Specific Heat Capacity | 0.470 J/g-°C @Temperature 100 °C |
0.112 BTU/lb-°F @Temperature 212 °F |
|
| Haynes 214® alloy, 20% cold reduction, 980°C (1800°F) for 5 minutes Intended principally for use at temperatures of 955°C and above, exhibits resistance to oxidation that exceeds virtually all conventional heat-resistant wrought alloys. Applications include mesh .. |
|||
| Specific Heat Capacity | 0.470 J/g-°C @Temperature 100 °C |
0.112 BTU/lb-°F @Temperature 212 °F |
|
| Haynes 214® alloy, 30% cold reduction, 925°C for 5 minutes Intended principally for use at temperatures of 955°C and above, exhibits resistance to oxidation that exceeds virtually all conventional heat-resistant wrought alloys. Applications include mesh .. |
|||
| Specific Heat Capacity | 0.470 J/g-°C @Temperature 100 °C |
0.112 BTU/lb-°F @Temperature 212 °F |
|
| Haynes 214® alloy, 40% cold reduction, 925°C for 5 minutes Intended principally for use at temperatures of 955°C and above, exhibits resistance to oxidation that exceeds virtually all conventional heat-resistant wrought alloys. Applications include mesh .. |
|||
| Specific Heat Capacity | 0.470 J/g-°C @Temperature 100 °C |
0.112 BTU/lb-°F @Temperature 212 °F |
|
| Haynes 214® alloy, 40% cold reduction, 980°C (1800°F) for 5 minutes Intended principally for use at temperatures of 955°C and above, exhibits resistance to oxidation that exceeds virtually all conventional heat-resistant wrought alloys. Applications include mesh .. |
|||
| Specific Heat Capacity | 0.470 J/g-°C @Temperature 100 °C |
0.112 BTU/lb-°F @Temperature 212 °F |
|
| Haynes 214® alloy, 50% cold reduction Intended principally for use at temperatures of 955°C and above, exhibits resistance to oxidation that exceeds virtually all conventional heat-resistant wrought alloys. Applications include mesh .. |
|||
| Specific Heat Capacity | 0.470 J/g-°C @Temperature 100 °C |
0.112 BTU/lb-°F @Temperature 212 °F |
|
| Haynes 214® alloy, 50% cold reduction, 1095°C (2000°F) for 5 minutes Intended principally for use at temperatures of 955°C and above, exhibits resistance to oxidation that exceeds virtually all conventional heat-resistant wrought alloys. Applications include mesh .. |
|||
| Specific Heat Capacity | 0.470 J/g-°C @Temperature 100 °C |
0.112 BTU/lb-°F @Temperature 212 °F |
|
| Haynes 214® alloy, 50% cold reduction, 980°C (1800°F) for 5 minutes Intended principally for use at temperatures of 955°C and above, exhibits resistance to oxidation that exceeds virtually all conventional heat-resistant wrought alloys. Applications include mesh .. |
|||
| Specific Heat Capacity | 0.470 J/g-°C @Temperature 100 °C |
0.112 BTU/lb-°F @Temperature 212 °F |
|
| Haynes 214® alloy, hot rolled solution annealed plate 12.7 mm (1/2 in.) thick Intended principally for use at temperatures of 955°C and above, exhibits resistance to oxidation that exceeds virtually all conventional heat-resistant wrought alloys. Applications include mesh .. |
|||
| Specific Heat Capacity | 0.470 J/g-°C @Temperature 100 °C |
0.112 BTU/lb-°F @Temperature 212 °F |
|
| Haynes 214® alloy, sheet, 100 hours exposure at 760°C (1400°F) Intended principally for use at temperatures of 955°C and above, exhibits resistance to oxidation that exceeds virtually all conventional heat-resistant wrought alloys. Applications include mesh .. |
|||
| Specific Heat Capacity | 0.470 J/g-°C @Temperature 100 °C |
0.112 BTU/lb-°F @Temperature 212 °F |
|
| Haynes 214® alloy, sheet, 100 hours exposure at 980°C (1800°F) Intended principally for use at temperatures of 955°C and above, exhibits resistance to oxidation that exceeds virtually all conventional heat-resistant wrought alloys. Applications include mesh .. |
|||
| Specific Heat Capacity | 0.470 J/g-°C @Temperature 100 °C |
0.112 BTU/lb-°F @Temperature 212 °F |
|
| Haynes 214® alloy, sheet, 1000 hours exposure at 760°C (1400°F) Intended principally for use at temperatures of 955°C and above, exhibits resistance to oxidation that exceeds virtually all conventional heat-resistant wrought alloys. Applications include mesh .. |
|||
| Specific Heat Capacity | 0.470 J/g-°C @Temperature 100 °C |
0.112 BTU/lb-°F @Temperature 212 °F |
|
| Haynes 214® alloy, sheet, 32 hours exposure at 760°C (1400°F) Intended principally for use at temperatures of 955°C and above, exhibits resistance to oxidation that exceeds virtually all conventional heat-resistant wrought alloys. Applications include mesh .. |
|||
| Specific Heat Capacity | 0.470 J/g-°C @Temperature 100 °C |
0.112 BTU/lb-°F @Temperature 212 °F |
|
| Haynes 214® alloy, sheet, 32 hours exposure at 980°C (1800°F) Intended principally for use at temperatures of 955°C and above, exhibits resistance to oxidation that exceeds virtually all conventional heat-resistant wrought alloys. Applications include mesh .. |
|||
| Specific Heat Capacity | 0.470 J/g-°C @Temperature 100 °C |
0.112 BTU/lb-°F @Temperature 212 °F |
|
| Haynes 214® alloy, 30% cold reduction, 980°C (1800°F) for 5 minutes Intended principally for use at temperatures of 955°C and above, exhibits resistance to oxidation that exceeds virtually all conventional heat-resistant wrought alloys. Applications include mesh .. |
|||
| Specific Heat Capacity | 0.470 J/g-°C @Temperature 600 °C |
0.112 BTU/lb-°F @Temperature 1110 °F |
|
| Haynes 242® alloy, after 4000 hours exposure at 650°C (1200°F) Age-hardenable, high ductility in the aged condition, lower thermal expansion than most alloys, very good oxidation resistance up to 815°C, excellent low cycle fatigue properties, very good therm.. |
|||
| Specific Heat Capacity | 0.470 J/g-°C @Temperature 600 °C |
0.112 BTU/lb-°F @Temperature 1110 °F |
|
| Haynes 242® alloy, after 8000 hours exposure at 650°C (1200°F) Age-hardenable, high ductility in the aged condition, lower thermal expansion than most alloys, very good oxidation resistance up to 815°C, excellent low cycle fatigue properties, very good therm.. |
|||
| Specific Heat Capacity | 0.470 J/g-°C @Temperature 600 °C |
0.112 BTU/lb-°F @Temperature 1110 °F |
|
| Haynes 242® alloy, cold reduced sheet, annealed Age-hardenable, high ductility in the aged condition, lower thermal expansion than most alloys, very good oxidation resistance up to 815°C, excellent low cycle fatigue properties, very good therm.. |
|||
| Specific Heat Capacity | 0.470 J/g-°C @Temperature 600 °C |
0.112 BTU/lb-°F @Temperature 1110 °F |
|
| Haynes 242® alloy, cold reduced sheet, annealed and 20% cold work Age-hardenable, high ductility in the aged condition, lower thermal expansion than most alloys, very good oxidation resistance up to 815°C, excellent low cycle fatigue properties, very good therm.. |
|||
| Specific Heat Capacity | 0.470 J/g-°C @Temperature 600 °C |
0.112 BTU/lb-°F @Temperature 1110 °F |
|
| Haynes 242® alloy, cold reduced sheet, annealed, 40% cold work, aged Age-hardenable, high ductility in the aged condition, lower thermal expansion than most alloys, very good oxidation resistance up to 815°C, excellent low cycle fatigue properties, very good therm.. |
|||
| Specific Heat Capacity | 0.467 J/g-°C | 0.112 BTU/lb-°F | RT |
| Haynes HR-120® alloy, solution heat-treated plate Excellent strength at elevated temperatures, combined with good resistance to carburizing and sulfidizing environments. Applications include bar frame heat treating baskets, wire mesh furnace belts .. |
|||
| Specific Heat Capacity | 0.470 J/g-°C | 0.112 BTU/lb-°F | RT |
| Outokumpu 4948 High Temperature Austenitic Stainless Steel Creep-resistant variant of 1.4301, with a standardized minimum carbon content for service at temperatures of up to 800°C in dry air.Applications: Heat and creep resistance. For use over 550°C for.. |
|||