Lubrizol ESTANE® 58887 Ether Based Thermoplastic Polyurethane

Category Polymer , Thermoplastic , Elastomer, TPE , Polyurethane, TP , Thermoplastic Polyurethane, Elastomer, Ether Grade
Manufacturer Lubrizol (former Noveon)
Trade Name ESTANE®
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Lubrizol ESTANE® 58887 Ether Based Thermoplastic Polyurethane.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Features: Excellent hydrolysis resistance, low temperature performance, clarity and wide processing window for extrusion.Uses: Blown and flat die/cast film extrusion, Injection and blow molding; cable jacketing and profile extrusion.Available in Americas, Europe, Middle East, Africa, India and AsiaInformation provided by Lubrizol.
Physical Properties Metric English Comments
Specific Gravity 1.12 g/cc
1.12 g/cc
ASTM D792
Maximum Moisture Content 0.020
0.020
Mechanical Properties Metric English Comments
Hardness, Shore A 84 - 90

@Time 5.00 sec
84 - 90

@Time 0.00139 hour
ASTM D2240
Tensile Strength 51.7 MPa
7500 psi
ASTM D412
38.78 MPa

@Temperature 75.0 °C,
Time 4.838e+6 sec
5625 psi

@Temperature 167 °F,
Time 1344 hour
30 mil sheet, Immersion in Water
43.95 MPa

@Temperature 75.0 °C,
Time 2.42e+6 sec
6374 psi

@Temperature 167 °F,
Time 672 hour
30 mil sheet, Immersion in Water
44.98 MPa

@Temperature 75.0 °C,
Time 1.21e+6 sec
6524 psi

@Temperature 167 °F,
Time 336 hour
30 mil sheet, Immersion in Water
45.5 MPa

@Temperature 75.0 °C,
Time 605000 sec
6600 psi

@Temperature 167 °F,
Time 168 hour
30 mil sheet, Immersion in Water
51.7 MPa

@Temperature 75.0 °C,
Time 0.000 sec
7500 psi

@Temperature 167 °F,
Time 0.000 hour
30 mil sheet, Immersion in Water
Elongation at Break 500 %
500 %
ASTM D412
100% Modulus 0.00690 GPa
1.00 ksi
ASTM D412
300% Modulus 0.0124 GPa
1.80 ksi
ASTM D412
Tear Strength 26.3 kN/m
150 pli
Trouser; ASTM D470
Graves Tear Strength 87.7 kN/m
500 pli
Die C; ASTM D624
Taber Abrasion, mg/1000 Cycles 40
40
H18, 1000g; ASTM D3389 B
Tensile Set 18 %
18 %
200% elongation; ASTM D412
Thermal Properties Metric English Comments
Melting Point 140 °C
284 °F
DSC
150 °C
302 °F
Kolfer
Glass Transition Temp, Tg -45.0 °C
-49.0 °F
DSC
Optical Properties Metric English Comments
Haze 1.0 %
1.0 %
pressed between glass; ASTM D1003
Processing Properties Metric English Comments
Zone 1 177 °C
351 °F
Extrusion
Zone 2 182 °C
360 °F
Extrusion
Zone 3 188 °C
370 °F
Extrusion
Zone 4 193 °C
379 °F
Extrusion
Adapter Temperature 193 °C
379 °F
5, Extrusion
Die Temperature 193 °C
379 °F
6, Zone 1, Extrusion
193 °C
379 °F
Zone 2, Extrusion
Drying Temperature 104 °C
219 °F
Dry Time 2.00 - 4.00 hour
2.00 - 4.00 hour
Dew Point -40.0 °C
-40.0 °F
Descriptive Properties Value Comments
Volume Swell in Water 1.1%
24h, 23°C; ASTM D471