Lanxess Durethan® BKV 25 F30 000000 Nylon 6, Glass Fiber Reinforced, Flame Retardant

Category Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, Glass Fiber Filled, Flame Retardant
Manufacturer Lanxess
Trade Name Durethan®
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Lanxess Durethan® BKV 25 F30 000000 Nylon 6, Glass Fiber Reinforced, Flame Retardant.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
PA 6, 25% glass fibers, injection molding, flame retardantInformation provided by LANXESS.
Physical Properties Metric English Comments
Specific Gravity 1.60 g/cc
1.60 g/cc
ISO 1183
Linear Mold Shrinkage, Flow 0.0010 cm/cm
0.0010 in/in
Post-shrinkage, 60x60x2; 120°C; 4 hour; ISO 294-4
0.0030 cm/cm
0.0030 in/in
60x60x2; 280°C / MT 80°C; 600 bar; ISO 294-4
Linear Mold Shrinkage, Transverse 0.0010 cm/cm
0.0010 in/in
Post-shrinkage, 60x60x2; 120°C; 4 hour; ISO 294-4
0.0060 cm/cm
0.0060 in/in
60x60x2; 280°C / MT 80°C; 600 bar; ISO 294-4
Mechanical Properties Metric English Comments
Tensile Strength at Break 90.0 MPa
13100 psi
cond.; ISO 527-1, -2; 5 mm/min
150 MPa
21800 psi
d.a.m.; ISO 527-1, -2; 5 mm/min
Elongation at Break 2.3 %
2.3 %
d.a.m.; ISO 527-1, -2; 5 mm/min
4.4 %
4.4 %
cond.; ISO 527-1, -2; 5 mm/min
Tensile Modulus 7.30 GPa
1060 ksi
cond.; ISO 527-1, -2; 1 mm/min
11.0 GPa
1600 ksi
d.a.m.; ISO 527-1, -2; 1 mm/min
Flexural Strength 155 MPa

@Strain 4.00 %
 22500 psi

@Strain 4.00 %
 cond., 2 mm/min; ISO 178-A
230 MPa

@Strain 2.50 %
 33400 psi

@Strain 2.50 %
 d.a.m., 2 mm/min; ISO 178-A
Flexural Modulus 7.00 GPa
1020 ksi
cond., 2 mm/min; ISO 178-A
10.0 GPa
1450 ksi
d.a.m., 2 mm/min; ISO 178-A
Izod Impact, Notched (ISO) <= 10.0 kJ/m²

@Temperature -30.0 °C
 <= 4.76 ft-lb/in²

@Temperature -22.0 °F
 d.a.m.; ISO 180-1A
<= 10.0 kJ/m²

@Temperature -30.0 °C
 <= 4.76 ft-lb/in²

@Temperature -22.0 °F
 cond.; ISO 180-1A
10.0 kJ/m²

@Temperature 23.0 °C
 4.76 ft-lb/in²

@Temperature 73.4 °F
 d.a.m.; ISO 180-1A
15.0 kJ/m²

@Temperature 23.0 °C
 7.14 ft-lb/in²

@Temperature 73.4 °F
 cond.; ISO 180-1A
Izod Impact, Unnotched (ISO) 45.0 kJ/m²

@Temperature -30.0 °C
 21.4 ft-lb/in²

@Temperature -22.0 °F
 d.a.m.; ISO 180-1U
50.0 kJ/m²

@Temperature 23.0 °C
 23.8 ft-lb/in²

@Temperature 73.4 °F
 d.a.m.; ISO 180-1U
50.0 kJ/m²

@Temperature -30.0 °C
 23.8 ft-lb/in²

@Temperature -22.0 °F
 cond.; ISO 180-1U
55.0 kJ/m²

@Temperature 23.0 °C
 26.2 ft-lb/in²

@Temperature 73.4 °F
 cond.; ISO 180-1U
Charpy Impact Unnotched 4.50 J/cm²

@Temperature -30.0 °C
 21.4 ft-lb/in²

@Temperature -22.0 °F
 d.a.m.; ISO 179-1eU
5.00 J/cm²

@Temperature -30.0 °C
 23.8 ft-lb/in²

@Temperature -22.0 °F
 cond.; ISO 179-1eU
5.50 J/cm²

@Temperature 23.0 °C
 26.2 ft-lb/in²

@Temperature 73.4 °F
 d.a.m.; ISO 179-1eU
5.50 J/cm²

@Temperature 23.0 °C
 26.2 ft-lb/in²

@Temperature 73.4 °F
 cond.; ISO 179-1eU
Charpy Impact, Notched <= 1.00 J/cm²

@Temperature -30.0 °C
 <= 4.76 ft-lb/in²

@Temperature -22.0 °F
 d.a.m.; ISO 179-1eA
<= 1.00 J/cm²

@Temperature -30.0 °C
 <= 4.76 ft-lb/in²

@Temperature -22.0 °F
 cond.; ISO 179-1eA
1.00 J/cm²

@Temperature 23.0 °C
 4.76 ft-lb/in²

@Temperature 73.4 °F
 d.a.m.; ISO 179-1eA
1.50 J/cm²

@Temperature 23.0 °C
 7.14 ft-lb/in²

@Temperature 73.4 °F
 cond.; ISO 179-1eA
Puncture Energy 1.90 J

@Load <=91.8 kg,
Temperature -30.0 °C
 1.40 ft-lb

@Load <=202 lb,
Temperature -22.0 °F
 ISO 6603-2
3.00 J

@Load <=102 kg,
Temperature 23.0 °C
 2.21 ft-lb

@Load <=225 lb,
Temperature 73.4 °F
 ISO 6603-2
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 20.0 µm/m-°C

@Temperature 23.0 - 55.0 °C
 11.1 µin/in-°F

@Temperature 73.4 - 131 °F
 ISO 11359-1, -2
CTE, linear, Transverse to Flow 90.0 µm/m-°C

@Temperature 23.0 - 55.0 °C
 50.0 µin/in-°F

@Temperature 73.4 - 131 °F
 ISO 11359-1, -2
Melting Point 222 °C
432 °F
10°C/min; ISO 11357-1, -3
Deflection Temperature at 0.46 MPa (66 psi) 215 °C
419 °F
ISO 75-1, -2
Deflection Temperature at 1.8 MPa (264 psi) 205 °C
401 °F
ISO 75-1, -2
Vicat Softening Point 205 °C

@Load 5.10 kg
 401 °F

@Load 11.2 lb
 120°C/hour; ISO 306
Flammability, UL94 V-0

@Thickness 0.400 mm
 V-0

@Thickness 0.0157 in
V-0

@Thickness 3.00 mm
 V-0

@Thickness 0.118 in
5VA

@Thickness 1.00 mm
 5VA

@Thickness 0.0394 in
Glow Wire Test 775 °C

@Diameter 0.800 mm
 1430 °F

@Diameter 0.0315 in
 GWIT; IEC 60695-2-13
775 °C

@Diameter 1.50 mm
 1430 °F

@Diameter 0.0591 in
 GWIT; IEC 60695-2-13
850 °C

@Diameter 0.400 mm
 1560 °F

@Diameter 0.0157 in
 GWIT; IEC 60695-2-13
850 °C

@Diameter 3.00 mm
 1560 °F

@Diameter 0.118 in
 GWIT; IEC 60695-2-13
960 °C

@Diameter 0.400 mm
 1760 °F

@Diameter 0.0157 in
 GWFI; IEC 60695-2-12
960 °C

@Diameter 0.800 mm
 1760 °F

@Diameter 0.0315 in
 GWFI; IEC 60695-2-12
960 °C

@Diameter 1.50 mm
 1760 °F

@Diameter 0.0591 in
 GWFI; IEC 60695-2-12
960 °C

@Diameter 3.00 mm
 1760 °F

@Diameter 0.118 in
 GWFI; IEC 60695-2-12
Electrical Properties Metric English Comments
Volume Resistivity 3.40e+14 ohm-cm
3.40e+14 ohm-cm
d.a.m.; IEC 60093
Surface Resistance 4.10e+13 ohm
4.10e+13 ohm
d.a.m.; IEC 60093
Comparative Tracking Index 400 V
400 V
d.a.m.; Solution A; IEC 60112
Processing Properties Metric English Comments
Melt Temperature 270 - 290 °C
518 - 554 °F
admissible residence time at Tmax >= 10 min
280 °C
536 °F
for test specimens; ISO 294
Mold Temperature 80.0 °C
176 °F
for test specimens; ISO 294
80.0 - 100 °C
176 - 212 °F
Drying Temperature 80.0 °C
176 °F
Dry Time 2 - 6 hour
2 - 6 hour
Moisture Content 0.030 - 0.12 %
0.030 - 0.12 %
residual; Karl Fischer Test
Descriptive Properties Value Comments
Flammability Test passed
ISO 3795; US-FMVSS302
ISO Shortname ISO 1874-PA 6, GFHR, 14-110, GF25; ISO 1043-PA GF FR (17)