- Polymer Property : Linear Mold Shrinkage, Transverse = 0.0010 in/in
Polymer Property : Linear Mold Shrinkage, Transverse = 0.0010 in/in Product List
Physical PropertiesTips: 30 items are displayed at most. For the rest of the results, please contact customer service.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Linear Mold Shrinkage, Transverse | 0.0010 - 0.0030 cm/cm @Thickness 3.20 mm |
0.0010 - 0.0030 in/in @Thickness 0.126 in |
SABIC Method |
| SABIC Innovative Plastics Lexan® HFD4413 PC Lexan* HFD4413 is a 30% glass filled, injection moldable grade designed for high flow and superior surface appearance. Internal mold release. |
|||
| Linear Mold Shrinkage, Transverse | 0.0010 - 0.0030 cm/cm @Thickness 3.20 mm |
0.0010 - 0.0030 in/in @Thickness 0.126 in |
SABIC Method |
| SABIC Innovative Plastics Lexan® LGK5030 PC (Asia Pacific) Glass reinforced. Flame retardant. |
|||
| Linear Mold Shrinkage, Transverse | 0.0010 cm/cm | 0.0010 in/in | ISO 294-4 |
| Celanese VECTRA B230 LCP, 30% Specialty
(Unverified Data**) Exceptional strength and stiffness. Suitable for metal replacement applications. Electrically conductive. 30% carbon fiber reinforced.30% carbon fiber,exceptional strength and stiffness, conductiv.. |
|||
| Linear Mold Shrinkage, Transverse | 0.0010 cm/cm @Temperature 150 °C, Time 900 sec |
0.0010 in/in @Temperature 302 °F, Time 0.250 hour |
DIN 40634 |
| Mitsubishi Hostaphan® RN, 23 micron Nominal Thickness Universal Polyethylene Terephthalate Film Hostaphan® RN is a transparent, biaxially oriented film made of polyethylene terephthalate (PET) and characterized by outstanding physical properties. Hostaphan® RN is the standard product for.. |
|||
| Linear Mold Shrinkage, Transverse | 0.0010 cm/cm | 0.0010 in/in | Post-shrinkage, 60x60x2; 120°C; 4 hour; ISO 294-4 |
| Lanxess Pocan® B 3216 HR 000000 PBT 16% Glass Fiber PBT, 16% glass fibers, injection molding, improved impact strength, hydrolysis stabilizedInformation provided by LANXESS. |
|||
| Linear Mold Shrinkage, Transverse | 0.0010 cm/cm | 0.0010 in/in | Post-shrinkage, 60x60x2; 120°C; 4 hour; ISO 294-4 |
| Lanxess Pocan® DP 7102 000000 PBT, 32% Mineral PBT, 32% mineral, injection molding, LDSInformation provided by LANXESS. |
|||
| Linear Mold Shrinkage, Transverse | 0.0010 cm/cm | 0.0010 in/in | Post-shrinkage, 60x60x2; 120°C; 4 hour; ISO 294-4 |
| Lanxess Pocan® ECO T 3240 000000 PBT + PET, 45% Glass Fiber PBT + PET, 45% glass fibers, injection molding, improved surface finish, contains 25% post-consumer recycled material, increased temperature peak loadInformation provided by LANXESS. |
|||
| Linear Mold Shrinkage, Transverse | 0.0010 cm/cm | 0.0010 in/in | Post-shrinkage, 60x60x2; 120°C; 4 hour; ISO 294-4 |
| Lanxess Pocan® T 7391 POS151 900044 PBT + PET, 45% Glass Fiber PBT + PET, 45% glass fibers, injection molding, improved surface finish, increased temperature peak load UV stabilizedInformation provided by LANXESS. |
|||
| Linear Mold Shrinkage, Transverse | 0.0010 cm/cm | 0.0010 in/in | Post-shrinkage, 150x105x3; 120°C; 4 hour; ISO 2577 |
| Lanxess Durethan® BKV 35 H3.0 000000 Nylon 6, Glass Fiber Reinforced PA 6, 35% glass fibers, injection molding, heat-aging stabilizedInformation provided by LANXESS. |
|||
| Linear Mold Shrinkage, Transverse | 0.0010 - 0.0030 cm/cm | 0.0010 - 0.0030 in/in | Post-shrinkage, 60x60x2; 120°C; 4 hour; ISO 294-4 |
| Lanxess Durethan® ECO BV 30 H2 900500 Nylon 6, 30% Glass Fiber PA 6, 30% glass fibers, injection molding, heat-ageing stabilized, contains 30% pre-consumer recycled materialInformation provided by LANXESS. |
|||
| Linear Mold Shrinkage, Transverse | 0.0010 cm/cm | 0.0010 in/in | Post-shrinkage, 60x60x2; 120°C; 4 hour; ISO 294-4 |
| Lanxess Pocan® T 7141 000000 PET + PBT, 40% Glass Fiber/Mineral PET + PBT, 40% glass fibers/mineral, injection molding, improved flowability, high thermal dimensional stabilityInformation provided by LANXESS. |
|||
| Linear Mold Shrinkage, Transverse | 0.0010 - 0.0040 cm/cm @Time 86400 sec |
0.0010 - 0.0040 in/in @Time 24.0 hour |
ASTM D955 |
| SABIC Innovative Plastics LNP LUBRICOMP ECL36XXQ PEI LNP* Lubricomp* ECL36XXQ is a compound based on Polyetherimide containing 30% Carbon Fiber, 15% PTFE. Added features of this material include: Internally Lubricated. |
|||
| Linear Mold Shrinkage, Transverse | 0.0010 cm/cm | 0.0010 in/in | ASTM D955 |
| Solvay Specialty Polymers Amodel® AS-1145 HS Polyphthalamide (PPA), 45% Glass Fiber (Conditioned) Amodel® AS-1145 HS is a 45% glass reinforced heat stabilized polyphthalamide (PPA) resin that provides excellent structural integrity in molded parts, even those with wall thicknesses greater tha.. |
|||
| Linear Mold Shrinkage, Transverse | 0.0010 - 0.0030 cm/cm @Thickness 3.20 mm |
0.0010 - 0.0030 in/in @Thickness 0.126 in |
SABIC Method |
| SABIC Innovative Plastics LNP STAT-KON DX10315C PC (Asia Pacific) LNP* Stat-Kon* DX10315C is carbon fiber filled polycarbonate composite with good stiffness, good flow ability, ESD safety, and high level of cleanliness for the most demanding application. This comp.. |
|||
| Linear Mold Shrinkage, Transverse | 0.0010 - 0.0080 cm/cm @Time 86400 sec |
0.0010 - 0.0080 in/in @Time 24.0 hour |
ASTM D 955 |
| SABIC Innovative Plastics LNP Stat-kon REL36 PA 66 LNP* Stat-Kon* REL36 is a compound based on Nylon 6/6 containing carbon fiber and PTFE. Characteristics of this grade are Statically Conductive.This data was supplied by SABIC-IP for the Americas r.. |
|||
| Linear Mold Shrinkage, Transverse | 0.0010 - 0.0030 cm/cm @Time 86400 sec |
0.0010 - 0.0030 in/in @Time 24.0 hour |
ASTM D955 |
| SABIC Innovative Plastics LNP THERMOCOMP D351 PC (Asia Pacific) LNP* Thermocomp* D351 (experimental grade name as EXTC8143) is a compound based on Polycarbonate resin containing Glass Fiber, Flame Retardant. Added features of this material include: High modulus,.. |
|||
| Linear Mold Shrinkage, Transverse | 0.0010 - 0.0025 cm/cm @Time 86400 sec |
0.0010 - 0.0025 in/in @Time 24.0 hour |
ASTM D955 |
| SABIC Innovative Plastics LNP THERMOCOMP D451 PC (Asia Pacific) LNP* Thermocomp* D451 (or EXTC8141) is a compound based on Polycarbonate resin containing Glass Fiber, Flame Retardant. Added features of this material include: High modulus, good flatness, good duc.. |
|||
| Linear Mold Shrinkage, Transverse | 0.0010 - 0.0050 cm/cm @Time 86400 sec |
0.0010 - 0.0050 in/in @Time 24.0 hour |
ASTM D955 |
| SABIC Innovative Plastics LNP THERMOCOMP EC008PXQ PEI LNP* THERMOCOMP* EC008PXQ is a compound based on Polyetherimide containing 40% Carbon FIber. Added features include: Electrically Conductive, Exceptional Processing |
|||
| Linear Mold Shrinkage, Transverse | 0.0010 cm/cm @Thickness 3.20 mm |
0.0010 in/in @Thickness 0.126 in |
ASTM D955 |
| Samsung Cheil Industries Infino® HN-3104 PC, 10% Glass Filled FR Information provided by Samsung Cheil Industries. |
|||
| Linear Mold Shrinkage, Transverse | 0.0010 cm/cm | 0.0010 in/in | ASTM D955 |
| Solvay Specialty Polymers Amodel® A-1145 HS Polyphthalamide (PPA), 45% Glass Fiber (Conditioned) Amodel® A-1145 HS is a 45% glass reinforced, heat stabilized polyphthalamide (PPA) with a high heat deflection temperature, very high flexural modulus and very high tensile strength. Excellent cr.. |
|||
| Linear Mold Shrinkage, Transverse | 0.0010 - 0.0025 cm/cm @Thickness 3.20 mm |
0.0010 - 0.0025 in/in @Thickness 0.126 in |
SABIC Method |
| SABIC Innovative Plastics LNP STAT-KON DX09303C PC (Asia Pacific) LNP* Stat-Kon* DX09303C is carbon fiber filled polycarbonate composite with high modulus, good flow ability, and high level of cleanliness for the most demanding application. A unique feature of thi.. |
|||
| Linear Mold Shrinkage, Transverse | 0.0010 - 0.0050 cm/cm | 0.0010 - 0.0050 in/in | ASTM D955 |
| Lubrizol Estane® 2355-85ABR Thermoplastic Polyurethane Elastomer Formerly PellethaneFeature: FDA and USDA compliance, Blend resinAvailable in Americas, Europe, Middle East, Africa, India and AsiaData provided by Lubrizol.Lubrizol acquired the Pellethane product l.. |
|||
| Linear Mold Shrinkage, Transverse | 0.0010 cm/cm | 0.0010 in/in | Eurotec |
| Eurotec® Tecopet® PT74 GR20 BK002 DA PET, 20% glass fiber reinforced, high heat stabilized, black Information provided by Eurotec® |
|||
| Linear Mold Shrinkage, Transverse | 0.0010 cm/cm | 0.0010 in/in | ISO 294-4 |
| Barlog Plastics KEBAFLEX SG 25 A.1 TPE-S, Shore A25, natural TPE-SInformation provided by BARLOG plastics GmbH. |
|||
| Linear Mold Shrinkage, Transverse | 0.0010 cm/cm | 0.0010 in/in | Conditioned; ASTM D955 |
| Solvay Specialty Polymers Amodel® AS-1145 HS Polyphthalamide (PPA)
(Unverified Data**) Amodel AS-1145 HS is a 45% glass reinforced heat stabilized polyphthalamide (PPA) resin that provides excellent structural integrity in molded parts, even those with wall thicknesses greater than 0... |
|||
| Linear Mold Shrinkage, Transverse | 0.0010 - 0.0020 cm/cm | 0.0010 - 0.0020 in/in | ASTM D955 |
| Celanese Celstran® TPU-GF40-01-US TPU, 40% Glass Reinforced
(Unverified Data**) 40% long strand glass fiber reinforced thermoplastic polyurethane40% long strand glass fiber reinforced thermoplastic polyurethaneCelstran can be processed on a standard injection molding unit.Infor.. |
|||
| Linear Mold Shrinkage, Transverse | 0.0010 cm/cm | 0.0010 in/in | DAM; 48h at 80°C; ISO 294-4 |
| DuPont Performance Polymers Zytel® 101F NC010 Nylon 66
(Unverified Data**) Unreinforced Polyamide 66Zytel 101F NC010 is an internally lubricated polyamide 66 resin for injection molding. It was developed for fast cycles and high productivity.Information provided by DuPont .. |
|||
| Linear Mold Shrinkage, Transverse | 0.0010 cm/cm | 0.0010 in/in | ISO 294-4, 2577 |
| EMS-Grivory Grivory® TRVX-50X9 black 9230 PAMACM12-GF50 Product description: Grilamid TRVX-50X9 is a 50% glass fiber reinforced amorphous polyamide. This product shows a very low tendency of distortion and is therefore especially suitable for complex and.. |
|||
| Linear Mold Shrinkage, Transverse | 0.0010 cm/cm | 0.0010 in/in | ISO 294-4, 2577 |
| EMS-Grivory Grivory® TRVX-50X9 nat PAMACM12-GF50 Product description: Grilamid TRVX-50X9 is a 50% glass fiber reinforced amorphous polyamide. This product shows a very low tendency of distortion and is therefore especially suitable for complex and.. |
|||
| Linear Mold Shrinkage, Transverse | 0.0010 cm/cm | 0.0010 in/in | ISO 294-4, 2577 |
| Lanxess Pocan® B 3235 XF 000000 PBT, 30% Glass Fiber PBT, 30% glass fibers, injection molding, improved flowability |
|||