LG Chemical LUPOY GN5201F PC/ABS+GF20%, Halogen Free Flame Retardant

Category Polymer , Thermoplastic , ABS Polymer , Polycarbonate/ABS Alloy, Glass Fiber Filled , Polycarbonate (PC)
Manufacturer LG Chemical
Trade Name LUPOY
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF LG Chemical LUPOY GN5201F PC/ABS+GF20%, Halogen Free Flame Retardant.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Description: Injection Molding, PC/ABS+GF20%, Halogen Free Flame Retardant, High StiffnessApplication: E&E (Housing, OA Frame)CAS: 103598-77-2, 9003-56-9, 181028-79-5 and 65997-17-3Information provided by LG Chemical
Physical Properties Metric English Comments
Specific Gravity 1.36 g/cc
1.36 g/cc
ASTM D792
Maximum Moisture Content 0.040
0.040
Injection Molding
Linear Mold Shrinkage, Flow 0.0020 - 0.0040 cm/cm

@Thickness 3.20 mm
0.0020 - 0.0040 in/in

@Thickness 0.126 in
ASTM D955
Melt Flow 11 g/10 min

@Load 2.16 kg,
Temperature 250 °C
11 g/10 min

@Load 4.76 lb,
Temperature 482 °F
ASTM D1238
Mechanical Properties Metric English Comments
Tensile Strength, Yield 103 MPa

@Thickness 3.20 mm
14900 psi

@Thickness 0.126 in
50mm/min; ASTM D638
Elongation at Break 5.0 %

@Thickness 3.20 mm
5.0 %

@Thickness 0.126 in
50mm/min; ASTM D638
Flexural Yield Strength 147 MPa

@Thickness 3.20 mm
21300 psi

@Thickness 0.126 in
10mm/min; ASTM D790
Flexural Modulus 5.88 GPa

@Thickness 3.20 mm
853 ksi

@Thickness 0.126 in
10mm/min; ASTM D790
Izod Impact, Notched 1.08 J/cm

@Thickness 3.20 mm,
Temperature 23.0 °C
2.02 ft-lb/in

@Thickness 0.126 in,
Temperature 73.4 °F
ASTM D256
Thermal Properties Metric English Comments
Deflection Temperature at 1.8 MPa (264 psi) 105 °C

@Thickness 6.40 mm
221 °F

@Thickness 0.252 in
Unannealed; ASTM D648
UL RTI, Electrical 60.0 °C

@Thickness >=1.50 mm
140 °F

@Thickness >=0.0591 in
60.0 °C

@Thickness >=2.00 mm
140 °F

@Thickness >=0.0787 in
UL RTI, Mechanical with Impact 60.0 °C

@Thickness >=1.50 mm
140 °F

@Thickness >=0.0591 in
60.0 °C

@Thickness >=2.00 mm
140 °F

@Thickness >=0.0787 in
UL RTI, Mechanical without Impact 60.0 °C

@Thickness >=1.50 mm
140 °F

@Thickness >=0.0591 in
60.0 °C

@Thickness >=2.00 mm
140 °F

@Thickness >=0.0787 in
Flammability, UL94 V-0

@Thickness >=1.50 mm
V-0

@Thickness >=0.0591 in
V-0

@Thickness >=2.00 mm
V-0

@Thickness >=0.0787 in
5VA

@Thickness >=2.00 mm
5VA

@Thickness >=0.0787 in
Processing Properties Metric English Comments
Rear Barrel Temperature 230 - 250 °C
446 - 482 °F
Injection Molding
Middle Barrel Temperature 245 - 265 °C
473 - 509 °F
Injection Molding
Front Barrel Temperature 260 - 275 °C
500 - 527 °F
Injection Molding
Nozzle Temperature 260 - 275 °C
500 - 527 °F
Injection Molding
Melt Temperature 245 - 275 °C
473 - 527 °F
Injection Molding
Mold Temperature 60.0 - 80.0 °C
140 - 176 °F
Injection Molding
Drying Temperature 75.0 - 85.0 °C
167 - 185 °F
Injection Molding
Dry Time 3.00 - 4.00 hour
3.00 - 4.00 hour
Injection Molding
Back Pressure 0.981 - 1.96 MPa
142 - 284 psi
Injection Molding
Screw Speed 40 - 70 rpm
40 - 70 rpm
Injection Molding