Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Strength, Yield | 103 MPa | 14900 psi | Type I, 5.1 mm/min; ASTM D638 |
PolyOne LubriOne™ PS-30GF/15T Natural Polybutylene Terephthalate (PBT) LubriOne™ Lubricated and Wear-Resistant Compounds have been specifically formulated to be self-lubricating materials, offering low coefficient of friction and improved wear resistance properties. L.. |
|||
Tensile Strength, Yield | 103 MPa | 15000 psi | F5, supporting material; ASTM D882 |
Rogers Corporation Poron® 4701-30-20 Supported Urethane Foam, Very Soft, Supported with Clear Polyester Film Very soft, easily compressed for use where flexibility is a key requirement. Contains PET film reinforcement.Features and Benefits of PORON Products: Excellent compression set resistance which ena.. |
|||
Tensile Strength, Yield | 103 MPa | 15000 psi | F5, supporting material; ASTM D882 |
Rogers Corporation Poron® 4701-30-25037 P Urethane Foam, Very Soft, Supported with Clear Polyester Film Very soft, easily compressed for use where flexibility is a key requirement. Standard available thickness range from 0.021"Features and Benefits of PORON Products: Excellent compression set resi.. |
|||
Tensile Strength, Yield | 103 MPa | 15000 psi | F5, supporting material; ASTM D882 |
Rogers Corporation Poron® Shock Seal™ 4790-79-12 Handheld Urethane Foam, Handheld Grade, PET Reinforced Extreme Impact Protection, Ultimate ReliabilitySpecifically engineered to protect sensitive components from damage caused by impactConsistent cushioning performance through repeated impactsExcellent.. |
|||
Tensile Strength, Yield | 103 MPa | 14900 psi | 50 mm/min; ASTM D638 |
Ovation Polymers Nima™ NH OPP66GF25 FR 25% Glass Filled Polyamide 66 Non-Hal red phosphorous based Flame Retardant CompoundAll properties after 48hrs conditioning at 23°C/50% RH |
|||
Tensile Strength, Yield | 103 MPa | 15000 psi | ASTM D638 |
Oxford Polymers 10GF 10% Glass Fiber Reinforced Polyetherimide/Polycarbonate Alloy 10% Glass Fiber Reinforced Polyetherimide/Polycarbonate AlloyInformation provided by Oxford Polymers. |
|||
Tensile Strength, Yield | 103 MPa | 14900 psi | Type I, 5 mm/min; ASTM D638 |
SABIC Innovative Plastics EXTEM XH1015 TPI Resin (Asia Pacific) Thermoplastic Polyimide Extem* XH1015 Resin. |
|||
Tensile Strength, Yield | 103 MPa | 14900 psi | 50 mm/min; ISO 527 |
SABIC Innovative Plastics Lexan® BFL2015 PC Non-brominated, non-chlorinated flame retardant, glass reinforced PC. Opaque colors only |
|||
Tensile Strength, Yield | 103 MPa | 15000 psi | ASTM D638 |
Polymer Resources PEI-GP1 Polyetherimide, Flame Retardant Polyetherimide, Flame Retardant, High Heat ResistanceProcess: Injection MoldingNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, test samples.Information.. |
|||
Tensile Strength, Yield | 103 MPa | 15000 psi | ASTM D638 |
Polymer Resources PPX-G30 Modified-PPO, 30% Glass Reinforced Modified-Polyphenylene Oxide, 30% Glass ReinforcedProcess: Injection MoldingNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, test samples.Information pr.. |
|||
Tensile Strength, Yield | 103 MPa | 15000 psi | 2.0 in/min; ASTM D638 |
LTL Color Compounds ColorFast® NY2GF130 Nylon 66, 13% Glass-Filled 13% glass-filled nylon 6,6All information provided by LTL Color Compounders, Inc. |
|||
Tensile Strength, Yield | 103 MPa | 14900 psi | ASTM D638 |
Lucent Polymers LPB-130 Polybutylene Terephthalate, 30% Glass Fiber/Mineral Reinforced, Low Warp Add "R" for Added ReleaseAdd "U" for UV StabilizerInformation provided by Lucent Polymers, Inc. |
|||
Tensile Strength, Yield | 103 MPa | 14900 psi | ASTM D 638 |
MRC Polymers NAXELL™ PC110-20G General Purpose Polycarbonate, Medium Viscosity, 20% Glass Fiber • Available in natural and custom colors• Can be UV Stabilized• Internal and external lubricants can be addedInformation provided by MRC Polymers Inc. |
|||
Tensile Strength, Yield | 103 MPa | 14900 psi | ISO 527 |
SABIC Innovative Plastics LNP Lubricomp KCL22 Acetal Copoly (Asia Pacific) LNP* Lubricomp* KCL22 is a compound based on Acetal Copolymer resin containing PTFE, Carbon Fiber. Added features of this material include: Internally Lubricated, Electrically Conductive.This data .. |
|||
Tensile Strength, Yield | 103 MPa | 14900 psi | Type I, 5 mm/min; ASTM D 638 |
SABIC Innovative Plastics Ultem DT1810E PEI Blend (Asia Pacific) Improved ductility, transparent, enhanced flow Polyetherimide blend (Tg 200C) with internal mold release and enhanced ductility. ECO Conforming.This data was supplied by SABIC-IP for the Asia Pacifi.. |
|||
Tensile Strength, Yield | 103 MPa | 14900 psi | Type I, 5 mm/min; ASTM D 638 |
SABIC Innovative Plastics Ultem DT1810EV PEI Blend (Europe-Africa-Middle East) Improved ductility, transparent, enhanced flow Polyetherimide blend (Tg 200C) with internal mold release and enhanced ductility. ECO Conforming, UL94 V0 listed.This data was supplied by SABIC-IP for.. |
|||
Tensile Strength, Yield | 103 MPa | 15000 psi | ASTM D638 |
Techmer ES HiFill® PA6/6 GF/B40 L 20% Glass Bead/Glass Fiber Filled Availability: North AmericaForms: PelletsFiller/Reinforcement: Glass Bead, 20% Filler by Weight and Glass Fiber Reinforcement, 20% Filler by WeightAdditive: LubricantFeatures: LubricatedInformation .. |
|||
Tensile Strength, Yield | 103 MPa | 15000 psi | ASTM D638 |
Techmer ES HiFill® PA6/6 GF13 TL10 13% Glass Filled Availability: North AmericaForms: PelletsFiller/Reinforcement: Glass Fiber Reinforcement, 13% Filler by Weight Additive: PTFE Lubricant (10%)Features: LubricatedAppearance: Natural ColorInformation .. |
|||
Tensile Strength, Yield | 103 MPa | 15000 psi | ASTM D638 |
Techmer ES HiFill® PBT WM35 X Availability: North AmericaForms: PelletsFiller/Reinforcement: Mineral FillerAdditive: LubricantFeatures: LubricatedInformation provided by TP Composites, Inc. |
|||
Tensile Strength, Yield | 103 MPa | 14900 psi | 5 mm/min; ISO 527 |
SABIC Innovative Plastics LNP THERMOCOMP 9X02540 PC+PET LNP* THERMOCOMP* PDX-02540 is a compound based on a PET+PC Blend containing Proprietary Filler. Flame Retardant. |
|||
Tensile Strength, Yield | 103 MPa | 14900 psi | 5 mm/min; ISO 527 |
SABIC Innovative Plastics ULTEM AUT210 PEI Transparent, Thermoplastic Polyimide (TPI). Glass transition Temperature (Tg) of 227degC. Haze onset temperature of 212degC (SABIC IP method). Very low outgassing and plateout, for automotive lighti.. |
|||
Tensile Strength, Yield | 103 MPa | 15000 psi | ASTM D638 |
Clariant Renol 612G20-L Nylon 612, 20% Glass Fiber Reinforced, Lubricated Data provided by Clariant Masterbatches |
|||
Tensile Strength, Yield | >= 103 MPa @Strain 0.200 % |
>= 15000 psi @Strain 0.200 % |
|
Carlson C 200 Commercially Pure Nickel General DescriptionCarlson Alloy C 200 is commercially pure nickel, combining good mechanical properties with excellent resistance to many corrosive environments. This alloy retains its strength at.. |
|||
Tensile Strength, Yield | 103 MPa | 14900 psi | ISO 527 |
Ascend Performance Materials Vydyne® R220/R228 Nylon 66, 40% Mineral Reinforced, Dry as Molded Vydyne® R220 is a 40% mineral reinforced Nylon 66 resin formulated for improved impact strength. Also available in black as R228. It is an injection molding grade formulated to retain the inherent .. |
|||
Tensile Strength, Yield | 103 MPa | 14900 psi | ASTM D638 |
Cheng Yu Plastic FR200GV15 Flame Retardant Nylon 66, 15% Glass Fiber |
|||
Tensile Strength, Yield | 103 MPa | 15000 psi | ASTM D638 |
Asahi Kasei Thermofil N-13FG-1626 13% Glass Fiber Reinforced, Heat Stabilized Information provided by Asahi Thermofil |
|||
Tensile Strength, Yield | 103 MPa | 14900 psi | At 50 mm/min; ISO 527-2 |
Borealis Xmod™ K65G3 30% Glass Fiber Reinforced Polypropylene Compound Xmod K65G3 is a 30% glass fiber reinforced grade intended for injection molding. Xmod K65G3 has been developed especially for the car industry, to be used UTB parts. Xmod K65G3 offers good balance.. |
|||
Tensile Strength, Yield | 103 MPa | 15000 psi | Type 1 - Rigids, Yield, 0.2 in/min; ASTM D638 |
PolyOne Edgetek® MLS-20GF/000 Polysulfone Alloy - 20% Glass Fiber Reinforced
(discontinued **) Data provided by PolyOne. |
|||
Tensile Strength, Yield | 103 - 138 MPa | 15000 - 20000 psi | Average value: 118 MPa Grade Count:7 |
Overview of materials for Polyphenylene Ether, 30% Glass Filled This property data is a summary of similar materials in the MatWeb database for the category "Polyphenylene Ether, 30% Glass Filled". Specific grades with glass content between 25% and 34% are inclu.. |
|||
Tensile Strength, Yield | 103 MPa | 14900 psi | 5 mm/min; ISO 527 |
SABIC Innovative Plastics LNP THERMOCOMP JF002 PES LNP THERMOCOMP* JF002 is a compound based on Polyethersulfone resin containing 10% Glass Fiber. |