EMS-Grivory Grivory® BKZ-30 PA6-GB30
| Category | Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, Glass Bead Filled |
| Manufacturer | EMS-Grivory (EMS-CHEMIE) |
| Trade Name | Grivory® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | EMS-Grivory Grivory® BKZ-30 PA6-GB30.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by EMS Grivory
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.34 g/cc | 0.0484 lb/in³ | ISO 1183 |
| Water Absorption | 8.0 % | 8.0 % | ISO 62 |
| Moisture Absorption | 2.00 % | 2.00 % | ISO 62 |
| Linear Mold Shrinkage, Flow | 0.0090 cm/cm | 0.0090 in/in | ISO 294-4, 2577 |
| Linear Mold Shrinkage, Transverse | 0.010 cm/cm | 0.010 in/in | ISO 294-4, 2577 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Ball Indentation Hardness | 85.0 MPa | 12300 psi | conditioned; ISO 2039-1 |
| 115 MPa | 16700 psi | dry; ISO 2039-1 | |
| Tensile Strength at Break | 40.0 MPa | 5800 psi | conditioned; ISO 527-1/-2 |
| 65.0 MPa | 9430 psi | dry; ISO 527-1/-2 | |
| Elongation at Break | 15 % | 15 % | dry; ISO 527-1/-2 |
| 40 % | 40 % | conditioned; ISO 527-1/-2 | |
| Tensile Modulus | 1.90 GPa | 276 ksi | conditioned; ISO 527-1/-2 |
| 3.40 GPa | 493 ksi | dry; ISO 527-1/-2 | |
| Charpy Impact Unnotched | 7.00 J/cm² | 33.3 ft-lb/in² | dry; ISO 179/1eU |
| 9.00 J/cm² | 42.8 ft-lb/in² | conditioned; ISO 179/1eU | |
| 7.00 J/cm² @Temperature 30.0 °C |
33.3 ft-lb/in² @Temperature 86.0 °F |
dry; ISO 179/1eU | |
| 9.00 J/cm² @Temperature 30.0 °C |
42.8 ft-lb/in² @Temperature 86.0 °F |
conditioned; ISO 179/1eU | |
| Charpy Impact, Notched | 0.600 J/cm² | 2.86 ft-lb/in² | dry; ISO 179/1eA |
| 1.00 J/cm² | 4.76 ft-lb/in² | conditioned; ISO 179/1eA | |
| 0.500 J/cm² @Temperature 30.0 °C |
2.38 ft-lb/in² @Temperature 86.0 °F |
dry; ISO 179/1eU | |
| 0.800 J/cm² @Temperature 30.0 °C |
3.81 ft-lb/in² @Temperature 86.0 °F |
conditioned; ISO 179/1eU |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 222 °C | 432 °F | 10°C/min; ISO 11357-1/-3 |
| Deflection Temperature at 1.8 MPa (264 psi) | 75.0 °C | 167 °F | ISO 75-1/-2 |
| Flammability, UL94 | HB | HB | IEC 60695-11-10 |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Automotive | Interior | |
| Electricals & Electronics | Electrical appliances | |
| Form | Granules | |
| Industry & Consumer goods | Housewares | |
| Sports & Leisure | ||
| Tools & Accessories | ||
| Processing | Injection Molding | |
| Special Characteristics | High impact or impact modified |
Users viewing this material also viewed the following:
- Quadrant EPP Ketron® CM HPV PEEK Polyetheretherketone; PTFE, Graphite, and Carbon Fiber Filled Bearing Grade, compression molded (ASTM Product Data Sheet)
- PolyOne Elastamax™ XL-2175 Thermoplastic Polyolefin Elastomer (TPO (POE))
- Lord Adhesives 18 Mix-In Accelerator for use with all Lord Acrylic Adhesives
- Mid-Mountain Materials ARMATEX® SF90 Silicone Rubber Coated Glass Fabric
- SABIC Innovative Plastics PC1000 PC
- Saint-Gobain Fluoroloy® A12 High Performance Seal Material
- ExxonMobil Diol 17 RD 40
- Total Lumicene® MR 2001 Polypropylene, Metallocene Polypropylene
- Arkema Group LOTRYL® 17 BA 07 Copolymer Ethylene - Butyl Acrylate
Copyright © lookpolymers.com All Rights Reserved