DuPont Performance Polymers Hytrel® 4069 TPC-ET  (Unverified Data**)

Category Polymer , Thermoplastic , Elastomer, TPE , Polyester, TP , Polyester Thermoplastic Elastomer
Manufacturer
Trade Name
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF DuPont Performance Polymers Hytrel® 4069 TPC-ET  (Unverified Data**).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Hytrel® 4069 is a low modulus grade with nominal hardness of 40D. It contains non-discoloring stabilizer. It can be processed by many conventional thermoplastic processing techniques like injection molding and extrusion.Information provided by DuPont Performance Polymers
Physical Properties Metric English Comments
Specific Gravity 1.11 g/cc
1.11 g/cc
ASTM D792
Density 1.11 g/cc
0.0401 lb/in³
ISO 1183
Water Absorption 0.20 %

@Temperature 23.0 °C
 0.20 %

@Temperature 73.4 °F
 Equilibrium 50%RH; ISO 62
0.70 %

@Temperature 23.0 °C
 0.70 %

@Temperature 73.4 °F
 Immersion 24h; ASTM D570
0.70 %

@Temperature 23.0 °C
 0.70 %

@Temperature 73.4 °F
 Immersion 24h; ISO 62
0.70 %

@Temperature 23.0 °C
 0.70 %

@Temperature 73.4 °F
 Saturation, immersed; ISO 62
Linear Mold Shrinkage 0.0080 cm/cm
0.0080 in/in
Flow; ASTM D955
Linear Mold Shrinkage, Flow 0.0080 cm/cm

@Thickness 2.00 mm
 0.0080 in/in

@Thickness 0.0787 in
 ISO 294-4
Linear Mold Shrinkage, Transverse 0.0080 cm/cm

@Thickness 2.00 mm
 0.0080 in/in

@Thickness 0.0787 in
 ISO 294-4
Melt Flow 8.5 g/10 min

@Load 2.16 kg,
Temperature 220 °C
 8.5 g/10 min

@Load 4.76 lb,
Temperature 428 °F
 ASTM D1238
8.5 g/10 min

@Load 2.16 kg,
Temperature 220 °C
 8.5 g/10 min

@Load 4.76 lb,
Temperature 428 °F
 ISO 1133
Melt Index of Compound 7.7 g/10 min

@Load 2.16 kg,
Temperature 220 °C
 7.7 g/10 min

@Load 4.76 lb,
Temperature 428 °F
 cm3/10 min; ISO 1133
Mechanical Properties Metric English Comments
Hardness, Shore D <= 37
<= 37
ISO 868
<= 40
<= 40
ASTM D2240
33

@Time 15.0 sec
 33

@Time 0.00417 hour
 ISO 868
Tensile Strength at Break 20.0 MPa

@Temperature 23.0 °C
 2900 psi

@Temperature 73.4 °F
 ASTM D638
28.0 MPa

@Temperature 23.0 °C
 4060 psi

@Temperature 73.4 °F
 ISO 527 (1BA bar)
Tensile Stress 2.40 MPa

@Strain 5.00 %,
Temperature 23.0 °C
 348 psi

@Strain 5.00 %,
Temperature 73.4 °F
 ASTM D638
3.20 MPa

@Strain 10.0 %,
Temperature 23.0 °C
 464 psi

@Strain 10.0 %,
Temperature 73.4 °F
 ISO 527 (1BA bar)
3.50 MPa

@Strain 10.0 %,
Temperature 23.0 °C
 508 psi

@Strain 10.0 %,
Temperature 73.4 °F
 ASTM D638
6.70 MPa

@Strain 50.0 %,
Temperature 23.0 °C
 972 psi

@Strain 50.0 %,
Temperature 73.4 °F
 ISO 527 (1BA bar)
Elongation at Break >= 50 %

@Temperature 23.0 °C
 >= 50 %

@Temperature 73.4 °F
 nominal; ISO 527 (1BA bar)
>= 300 %

@Temperature 23.0 °C
 >= 300 %

@Temperature 73.4 °F
 ISO 527 (1BA bar)
650 %

@Temperature 23.0 °C
 650 %

@Temperature 73.4 °F
 ISO 527 (1BA bar)
700 %

@Temperature 23.0 °C
 700 %

@Temperature 73.4 °F
 ASTM D638
800 %

@Temperature 23.0 °C
 800 %

@Temperature 73.4 °F
 nominal; ISO 527 (1BA bar)
Tensile Modulus 0.0450 GPa

@Temperature 23.0 °C
 6.53 ksi

@Temperature 73.4 °F
 ISO 527
Flexural Modulus 0.0280 GPa

@Temperature 100 °C
 4.06 ksi

@Temperature 212 °F
 ASTM D790
0.0280 GPa

@Temperature 100 °C
 4.06 ksi

@Temperature 212 °F
 ISO 178
0.0470 GPa

@Temperature 23.0 °C
 6.82 ksi

@Temperature 73.4 °F
 ISO 178
0.0550 GPa

@Temperature 23.0 °C
 7.98 ksi

@Temperature 73.4 °F
 ASTM D790
0.172 GPa

@Temperature -40.0 °C
 24.9 ksi

@Temperature -40.0 °F
 ASTM D790
0.172 GPa

@Temperature -40.0 °C
 24.9 ksi

@Temperature -40.0 °F
 ISO 178
Izod Impact, Notched NB

@Temperature -40.0 °C
 NB

@Temperature -40.0 °F
 ASTM D256
NB

@Temperature 23.0 °C
 NB

@Temperature 73.4 °F
 ASTM D256
Izod Impact, Notched (ISO) NB

@Temperature -40.0 °C
 NB

@Temperature -40.0 °F
 ISO 180/1A
NB

@Temperature 23.0 °C
 NB

@Temperature 73.4 °F
 ISO 180/1A
Charpy Impact Unnotched NB

@Temperature -30.0 °C
 NB

@Temperature -22.0 °F
 ISO 179/1eU
NB

@Temperature 23.0 °C
 NB

@Temperature 73.4 °F
 ISO 179/1eU
Charpy Impact, Notched NB

@Temperature -40.0 °C
 NB

@Temperature -40.0 °F
 ISO 179/1eA
NB

@Temperature -30.0 °C
 NB

@Temperature -22.0 °F
 ISO 179/1eA
NB

@Temperature 23.0 °C
 NB

@Temperature 73.4 °F
 ISO 179/1eA
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 500 µm/m-°C

@Temperature -40.0 - 23.0 °C
 278 µin/in-°F

@Temperature -40.0 - 73.4 °F
 ASTM E 831
500 µm/m-°C

@Temperature 23.0 - 55.0 °C
 278 µin/in-°F

@Temperature 73.4 - 131 °F
 ASTM E 831
500 µm/m-°C

@Temperature 55.0 - 120 °C
 278 µin/in-°F

@Temperature 131 - 248 °F
 ASTM E 831
500 µm/m-°C

@Temperature -40.0 - 23.0 °C
 278 µin/in-°F

@Temperature -40.0 - 73.4 °F
 ISO 11359-1/-2
500 µm/m-°C

@Temperature 23.0 - 55.0 °C
 278 µin/in-°F

@Temperature 73.4 - 131 °F
 ISO 11359-1/-2
500 µm/m-°C

@Temperature 55.0 - 120 °C
 278 µin/in-°F

@Temperature 131 - 248 °F
 ISO 11359-1/-2
CTE, linear, Transverse to Flow 190 µm/m-°C

@Temperature 23.0 - 55.0 °C
 106 µin/in-°F

@Temperature 73.4 - 131 °F
 ISO 11359-1/-2
190 µm/m-°C

@Temperature 55.0 - 120 °C
 106 µin/in-°F

@Temperature 131 - 248 °F
 ISO 11359-1/-2
192 µm/m-°C

@Temperature 55.0 - 120 °C
 107 µin/in-°F

@Temperature 131 - 248 °F
 ASTM E 831
219 µm/m-°C

@Temperature 23.0 - 55.0 °C
 122 µin/in-°F

@Temperature 73.4 - 131 °F
 ASTM E 831
270 µm/m-°C

@Temperature -40.0 - 23.0 °C
 150 µin/in-°F

@Temperature -40.0 - 73.4 °F
 ISO 11359-1/-2
277 µm/m-°C

@Temperature -40.0 - 23.0 °C
 154 µin/in-°F

@Temperature -40.0 - 73.4 °F
 ASTM E 831
Melting Point 193 °C
379 °F
10°C/min; ISO 11357-1/-3
193 °C
379 °F
ASTM D3418
Deflection Temperature at 0.46 MPa (66 psi) 50.0 °C
122 °F
ISO 75-1/-2
55.0 °C
131 °F
ASTM D648
Brittleness Temperature -95.0 °C
-139 °F
ISO 974
Glass Transition Temp, Tg -50.0 °C
-58.0 °F
10°C/min; ISO 11357-1/-2
UL RTI, Electrical 50.0 °C

@Thickness 1.50 mm
 122 °F

@Thickness 0.0591 in
 UL 746B
50.0 °C

@Thickness 3.00 mm
 122 °F

@Thickness 0.118 in
 UL 746B
Electrical Properties Metric English Comments
Volume Resistivity 4.00e+12 ohm-cm

@Temperature 23.0 °C
 4.00e+12 ohm-cm

@Temperature 73.4 °F
 IEC 60093
Surface Resistance 3.00e+14 ohm

@Temperature 23.0 °C
 3.00e+14 ohm

@Temperature 73.4 °F
 IEC 60093
Dielectric Constant 4.7

@Frequency 1.00e+6 Hz,
Temperature 23.0 °C
 4.7

@Frequency 1.00e+6 Hz,
Temperature 73.4 °F
 IEC 60250
4.8

@Frequency 100 Hz,
Temperature 23.0 °C
 4.8

@Frequency 100 Hz,
Temperature 73.4 °F
 IEC 60250
Dielectric Strength 18.0 kV/mm

@Temperature 23.0 °C
 457 kV/in

@Temperature 73.4 °F
 IEC 60243-1
Dissipation Factor 0.013

@Frequency 100 Hz,
Temperature 23.0 °C
 0.013

@Frequency 100 Hz,
Temperature 73.4 °F
 IEC 60250
0.020

@Frequency 1.00e+6 Hz,
Temperature 23.0 °C
 0.020

@Frequency 1.00e+6 Hz,
Temperature 73.4 °F
 IEC 60250
Comparative Tracking Index >= 600 V

@Temperature 23.0 °C
 >= 600 V

@Temperature 73.4 °F
 IEC 60112
>= 600 V

@Thickness 3.00 mm,
Temperature 23.0 °C
 >= 600 V

@Thickness 0.118 in,
Temperature 73.4 °F
 UL 746A