DuPont Performance Polymers Crastin® S600F20 NC010 PBT  (Unverified Data**)

Category Polymer , Thermoplastic , Polyester, TP , Polybutylene Terephthalate (PBT)
Manufacturer
Trade Name
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF DuPont Performance Polymers Crastin® S600F20 NC010 PBT  (Unverified Data**).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Crastin® S600F20 NC010 is an unreinforced, lubricated, medium viscosity polybutylene terephthalate resin for injection molding.Information provided by DuPont Performance Polymers
Physical Properties Metric English Comments
Density 1.31 g/cc
0.0473 lb/in³
ISO 1183
Water Absorption 0.20 %

@Temperature 23.0 °C
 0.20 %

@Temperature 73.4 °F
 Equilibrium 50%RH; ISO 62, Similar to
0.40 %

@Temperature 23.0 °C
 0.40 %

@Temperature 73.4 °F
 Saturation, immersed; ISO 62, Similar to
Linear Mold Shrinkage, Flow 0.020 cm/cm
0.020 in/in
Annealed; ISO 294-4
0.017 cm/cm

@Thickness 2.00 mm
 0.017 in/in

@Thickness 0.0787 in
 ISO 294-4
Linear Mold Shrinkage, Transverse 0.021 cm/cm
0.021 in/in
Annealed; ISO 294-4
0.016 cm/cm

@Thickness 2.00 mm
 0.016 in/in

@Thickness 0.0787 in
 ISO 294-4
Melt Flow 19.1 g/10 min

@Load 2.16 kg,
Temperature 250 °C
 19.1 g/10 min

@Load 4.76 lb,
Temperature 482 °F
 ISO 1133
Melt Index of Compound 20 g/10 min

@Load 2.16 kg,
Temperature 250 °C
 20 g/10 min

@Load 4.76 lb,
Temperature 482 °F
 cm3/10 min; ISO 1133
Mechanical Properties Metric English Comments
Tensile Strength, Yield 58.0 MPa

@Temperature 23.0 °C
 8410 psi

@Temperature 73.4 °F
 ISO 527
Elongation at Break 40 %

@Temperature 23.0 °C
 40 %

@Temperature 73.4 °F
 nominal; ISO 527
>= 50 %

@Temperature 23.0 °C
 >= 50 %

@Temperature 73.4 °F
 50mm/min; ISO 527
Elongation at Yield 7.0 %

@Temperature 23.0 °C
 7.0 %

@Temperature 73.4 °F
 ISO 527
Tensile Modulus 0.242 GPa

@Temperature 120 °C
 35.1 ksi

@Temperature 248 °F
 DAM; ISO 527
0.358 GPa

@Temperature 90.0 °C
 51.9 ksi

@Temperature 194 °F
 DAM; ISO 527
0.545 GPa

@Temperature 60.0 °C
 79.0 ksi

@Temperature 140 °F
 DAM; ISO 527
1.259 GPa

@Temperature 40.0 °C
 182.6 ksi

@Temperature 104 °F
 DAM; ISO 527
2.60 GPa

@Temperature 23.0 °C
 377 ksi

@Temperature 73.4 °F
 ISO 527
2.682 GPa

@Temperature 0.000 °C
 389.0 ksi

@Temperature 32.0 °F
 DAM; ISO 527
2.965 GPa

@Temperature -20.0 °C
 430.0 ksi

@Temperature -4.00 °F
 DAM; ISO 527
3.291 GPa

@Temperature -40.0 °C
 477.3 ksi

@Temperature -40.0 °F
 DAM; ISO 527
Flexural Strength 85.0 MPa

@Temperature 23.0 °C
 12300 psi

@Temperature 73.4 °F
 ISO 178
Flexural Modulus 2.20 GPa

@Temperature 23.0 °C
 319 ksi

@Temperature 73.4 °F
 ISO 178
Izod Impact, Notched (ISO) 4.50 kJ/m²

@Temperature 23.0 °C
 2.14 ft-lb/in²

@Temperature 73.4 °F
 ISO 180/1A
Izod Impact, Unnotched (ISO) NB

@Temperature 23.0 °C
 NB

@Temperature 73.4 °F
 ISO 180/1U
Charpy Impact Unnotched NB

@Temperature -30.0 °C
 NB

@Temperature -22.0 °F
 ISO 179/1eU
NB

@Temperature 23.0 °C
 NB

@Temperature 73.4 °F
 ISO 179/1eU
Charpy Impact, Notched 0.400 J/cm²

@Temperature -30.0 °C
 1.90 ft-lb/in²

@Temperature -22.0 °F
 ISO 179/1eA
0.500 J/cm²

@Temperature 23.0 °C
 2.38 ft-lb/in²

@Temperature 73.4 °F
 ISO 179/1eA
Tensile Creep Modulus, 1 hour 2600 MPa

@Temperature 23.0 °C
 377000 psi

@Temperature 73.4 °F
 ISO 899
Tensile Creep Modulus, 1000 hours 1800 MPa

@Temperature 23.0 °C
 261000 psi

@Temperature 73.4 °F
 ISO 899
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 500 µm/m-°C

@Temperature 23.0 - 55.0 °C
 278 µin/in-°F

@Temperature 73.4 - 131 °F
 ASTM E 831
500 µm/m-°C

@Temperature -40.0 - 23.0 °C
 278 µin/in-°F

@Temperature -40.0 - 73.4 °F
 ISO 11359-1/-2
500 µm/m-°C

@Temperature 23.0 - 55.0 °C
 278 µin/in-°F

@Temperature 73.4 - 131 °F
 ISO 11359-1/-2
500 µm/m-°C

@Temperature 55.0 - 160 °C
 278 µin/in-°F

@Temperature 131 - 320 °F
 ISO 11359-1/-2
CTE, linear, Transverse to Flow 90.0 µm/m-°C

@Temperature -40.0 - 23.0 °C
 50.0 µin/in-°F

@Temperature -40.0 - 73.4 °F
 ISO 11359-1/-2
120 µm/m-°C

@Temperature 23.0 - 55.0 °C
 66.7 µin/in-°F

@Temperature 73.4 - 131 °F
 ISO 11359-1/-2
130 µm/m-°C

@Temperature 23.0 - 55.0 °C
 72.2 µin/in-°F

@Temperature 73.4 - 131 °F
 ASTM E 831
200 µm/m-°C

@Temperature 55.0 - 160 °C
 111 µin/in-°F

@Temperature 131 - 320 °F
 ISO 11359-1/-2
Melting Point 225 °C
437 °F
10°C/min; ISO 11357-1/-3
Deflection Temperature at 0.46 MPa (66 psi) 115 °C
239 °F
ISO 75-1/-2
180 °C
356 °F
Annealed; ISO 75-1/-2
Deflection Temperature at 1.8 MPa (264 psi) 50.0 °C
122 °F
ISO 75-1/-2
60.0 °C
140 °F
Annealed; ISO 75-1/-2
Glass Transition Temp, Tg 55.0 °C
131 °F
10°C/min; ISO 11357-1/-2
UL RTI, Electrical 130 °C

@Thickness 3.00 mm
 266 °F

@Thickness 0.118 in
 UL 746B
130 °C

@Thickness 1.50 mm
 266 °F

@Thickness 0.0591 in
 UL 746B
130 °C

@Thickness 6.00 mm
 266 °F

@Thickness 0.236 in
 UL 746B
130 °C

@Thickness 0.750 mm
 266 °F

@Thickness 0.0295 in
 UL 746B
UL RTI, Mechanical with Impact 115 °C

@Thickness 0.750 mm
 239 °F

@Thickness 0.0295 in
 UL 746B
115 °C

@Thickness 1.50 mm
 239 °F

@Thickness 0.0591 in
 UL 746B
115 °C

@Thickness 3.00 mm
 239 °F

@Thickness 0.118 in
 UL 746B
115 °C

@Thickness 6.00 mm
 239 °F

@Thickness 0.236 in
 UL 746B
UL RTI, Mechanical without Impact 120 °C

@Thickness 3.00 mm
 248 °F

@Thickness 0.118 in
 UL 746B
120 °C

@Thickness 0.750 mm
 248 °F

@Thickness 0.0295 in
 UL 746B
120 °C

@Thickness 1.50 mm
 248 °F

@Thickness 0.0591 in
 UL 746B
120 °C

@Thickness 6.00 mm
 248 °F

@Thickness 0.236 in
 UL 746B
Electrical Properties Metric English Comments
Volume Resistivity >= 1.00e+15 ohm-cm

@Temperature 23.0 °C
 >= 1.00e+15 ohm-cm

@Temperature 73.4 °F
 IEC 60093
Surface Resistance >= 1.00e+12 ohm

@Temperature 23.0 °C
 >= 1.00e+12 ohm

@Temperature 73.4 °F
 IEC 60093
Dielectric Constant 3.2

@Frequency 1.00e+6 Hz,
Temperature 23.0 °C
 3.2

@Frequency 1.00e+6 Hz,
Temperature 73.4 °F
 IEC 60250
3.8

@Frequency 100 Hz,
Temperature 23.0 °C
 3.8

@Frequency 100 Hz,
Temperature 73.4 °F
 IEC 60250
3.8

@Frequency 50.0 Hz,
Temperature 23.0 °C
 3.8

@Frequency 50.0 Hz,
Temperature 73.4 °F
 IEC 60250
Dielectric Strength 26.0 kV/mm

@Thickness 1.00 mm,
Temperature 23.0 °C
 660 kV/in

@Thickness 0.0394 in,
Temperature 73.4 °F
 IEC 60243-1
Dissipation Factor 0.0020

@Frequency 100 Hz,
Temperature 23.0 °C
 0.0020

@Frequency 100 Hz,
Temperature 73.4 °F
 IEC 60250
0.0020

@Frequency 50.0 Hz,
Temperature 23.0 °C
 0.0020

@Frequency 50.0 Hz,
Temperature 73.4 °F
 IEC 60250
0.020

@Frequency 1.00e+6 Hz,
Temperature 23.0 °C
 0.020

@Frequency 1.00e+6 Hz,
Temperature 73.4 °F
 IEC 60250
Comparative Tracking Index 250 V

@Temperature 23.0 °C
 250 V

@Temperature 73.4 °F
 UL 746A
600 V

@Temperature 23.0 °C
 600 V

@Temperature 73.4 °F
 IEC 60112