Polymer Property : Tensile Creep Modulus, 1000 hours = 261000 psi Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Tensile Creep Modulus, 1000 hours	1800 MPa @Temperature 23.0 °C	261000 psi @Temperature 73.4 °F	ISO 899
DuPont Performance Polymers Crastin® FG6129 NC010 PBT (Unverified Data**) Crastin® FG6129 NC010 is an unreinforced, high viscosity polybutylene terephthalate resin for extrusion and injection molding. It has been developed for consideration into applications such as part..
Tensile Creep Modulus, 1000 hours	1800 MPa @Temperature 23.0 °C	261000 psi @Temperature 73.4 °F	ISO 899
DuPont Performance Polymers Crastin® S600F20 NC010 PBT (Unverified Data**) Crastin® S600F20 NC010 is an unreinforced, lubricated, medium viscosity polybutylene terephthalate resin for injection molding.Information provided by DuPont Performance Polymers
Tensile Creep Modulus, 1000 hours	1800 MPa @Temperature 23.0 °C	261000 psi @Temperature 73.4 °F	ISO 899
DuPont Performance Polymers Crastin® S600F40 NC010 PBT (Unverified Data**) Crastin® S600F40 NC010 is an unreinforced, lubricated, low viscosity polybutylene terephthalate resin for injection molding.Information provided by DuPont Performance Polymers
Tensile Creep Modulus, 1000 hours	1800 MPa	261000 psi	ISO 899-1
Lanxess PocanÂ® B 2505 000000 PBT PBT, non-reinforced, injection molding, flame retardant
Tensile Creep Modulus, 1000 hours	1800 MPa @Time 3.60e+6 sec	261000 psi @Time 1000 hour	ISO 899-1
DuPont Performance Polymers Crastin® FG6129 NC010 Polybutylene Terephthalate (PBT) (Unverified Data**)< Unreinforced High Viscosity Polybutylene Terephthalate Developed for Food Contact Applications and Extrusion and Injection Molding Crastin FG6129 NC010 is an unreinforced high viscosity polybutylene..
Tensile Creep Modulus, 1000 hours	1800 MPa @Time 3.60e+6 sec	261000 psi @Time 1000 hour	ISO 899-1
DuPont Performance Polymers Crastin® FG6130 NC010 Polybutylene Terephthalate (PBT) (Unverified Data**)< Unreinforced High Viscosity Polybutylene Terephthalate Developed for Food Contact Applications and Extrusion and Injection Molding Crastin FG6130 NC010 is an unreinforced medium high viscosity polyb..
Tensile Creep Modulus, 1000 hours	1800 MPa @Time 3.60e+6 sec	261000 psi @Time 1000 hour	ISO 899-1
DuPont Performance Polymers Crastin® FGS600F10 NC010 Polybutylene Terephthalate (PBT) (Unverified Data**) Unreinforced Polybutylene Terephthalate Developed for Food Contact ApplicationsInformation provided by DuPont Performance Polymers
Tensile Creep Modulus, 1000 hours	1800 MPa @Time 3.60e+6 sec	261000 psi @Time 1000 hour	ISO 899-1
DuPont Performance Polymers Crastin® FGS600F40 NC010 Polybutylene Terephthalate (PBT) (Unverified Data**) Unreinforced Low Viscosity Polybutylene Terephthalate Developed for Food Contact Applications Crastin FGS600F40 NC010 is an unreinforced low viscosity polybutylene terephthalate resin for injection ..
Tensile Creep Modulus, 1000 hours	1800 MPa @Time 3.60e+6 sec	261000 psi @Time 1000 hour	ISO 899-1
DuPont Performance Polymers Crastin® S600F40 NC010 Polybutylene Terephthalate (PBT) (Unverified Data**)&l Unreinforced Low Viscosity Polybutylene Terephthalate Crastin S600F40 NC010 is an unreinforced lubricated low viscosity polybutylene terephthalate resin for injection molding.Information provided by..
Tensile Creep Modulus, 1000 hours	1800 MPa @Time 3.60e+6 sec	261000 psi @Time 1000 hour	ISO 899-1
DuPont Performance Polymers Crastin® S620F20 NC010 Polybutylene Terephthalate (PBT) (Unverified Data**)&l Unreinforced Medium Viscosity Polybutylene Terephthalate Crastin S620F20 NC010 is an unreinforced nucleated lubricated medium viscosity polybutylene terephthalate resin for fast injection molding.In..
Tensile Creep Modulus, 1000 hours	1800 MPa @Time 3.60e+6 sec	261000 psi @Time 1000 hour	ISO 899-1
DuPont Performance Polymers Crastin® S650FR NC010 Polybutylene Terephthalate (PBT) (Unverified Data**)< Unreinforced Flame Retardant Polybutylene Terephthalate Crastin S650FR is an unreinforced flame retardant polybutylene terephthalate for injection molding.Information provided by DuPont Performance ..
Tensile Creep Modulus, 1000 hours	1800 MPa	261000 psi
BASF Polystyrol® 427 D Impact Grade Polystyrene (Europe) Heat distortion resistant, easy flowing, rapid freezing, low-impact grade for parts subjected to heat.Data was collected by ISO methods and provided by BASF.
Tensile Creep Modulus, 1000 hours	1800 MPa	261000 psi
BASF Polystyrol® 432 B Impact Grade Polystyrene (Europe) Very easy-flowing, low impact grade for parts with unfavorable flow path/wall-thickness ratios.Data was collected by ISO methods and provided by BASF.
Tensile Creep Modulus, 1000 hours	1800 MPa	261000 psi
Arkema Group Altuglas® GR 7E LIL Acrylic ALTUGLAS GR 7E LIL is an injection molding grade with excellent balance between mechanical, thermal and optical properties.Key features : easy processing and demolding improved chemical resistance ..
Tensile Creep Modulus, 1000 hours	1800 MPa	261000 psi
Arkema Group Altuglas® 84 L Acrylic-Styrene Copolymer ALTUGLAS 84 L is a new type of acrylic polymer produced by ATOHAAS which increases the range of material for injection molding applications. ALTUGLAS 84 L is a styrene methylmethacrylate copolymer s..
Tensile Creep Modulus, 1000 hours	1800 MPa	261000 psi
Arkema Group Oroglas® V 044 Acrylic, Extrusion Grade (discontinued **) OROGLAS V 044 is an extrusion grade offering good compromise between physical properties and thermal resistance.OROGLAS V 044 is recommended for extrusion of profiles, tubes and sheets.ISO data prov..
Tensile Creep Modulus, 1000 hours	1800 MPa	261000 psi
Arkema Group Oroglas® V 045 Acrylic, Extrusion Grade (discontinued **) OROGLAS V 045 is a lubricated extrusion grade offering good combination of physical and optical properties.OROGLAS V 045 provides easy processing behavior.OROGLAS V 045 is recommended for extrusion..
Tensile Creep Modulus, 1000 hours	1800 MPa	261000 psi
Arkema Group Oroglas® V 825 HID Acrylic, UV, Heat Resistant (discontinued **) OROGLAS HID is an acrylic resin formulated to withstand continuous exposure to high intensity discharge ( HID ) sources up to 90°c.Above 80°c, OROGLAS V 825 HID resin retains its original appearan..
Tensile Creep Modulus, 1000 hours	1800 MPa	261000 psi
Arkema Group Oroglas® V 825 T Acrylic (discontinued **) OROGLAS V 825 T exhibits an excellent balance of properties including superior thermal resistance with an easy processing behavior.OROGLAS V 825 T is then the material of choice for automotive appli..
Tensile Creep Modulus, 1000 hours	1800 MPa	261000 psi
Arkema Group Oroglas® V 920 Acrylic, Injection Molding Grade (discontinued **) OROGLAS V 920 is an injection molding grade with a good balance of properties :Superior flow with medium thermal resistance.The processing of OROGLAS V 920 is easy in terms of injection molding, mo..
Tensile Creep Modulus, 1000 hours	1800 MPa	261000 psi
Arkema Group Oroglas® V 920 T Acrylic, Injection Molding Grade (discontinued **) OROGLAS V 920 T is an injection molding grade with an improved thermal resistance HDT A ( 1.82 MPa ) = 96°c without any adverse effect on mechanical and optical properties.The processing of OROGLAS..