- Polymer Property : Melt Index of Compound = 20 g/10 min
Polymer Property : Melt Index of Compound = 20 g/10 min Product List
Physical PropertiesTips: 30 items are displayed at most. For the rest of the results, please contact customer service.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Index of Compound | 20 g/10 min @Load 2.16 kg, Temperature 230 °C |
20 g/10 min @Load 4.76 lb, Temperature 446 °F |
ISO 1133 |
| Polykemi AB POLYfill PP CCP20020 UV Polypropylene, Mineral Reinforced, UV stabilized Information provided by Polykemi AB |
|||
| Melt Index of Compound | 20 g/10 min @Load 2.16 kg, Temperature 230 °C |
20 g/10 min @Load 4.76 lb, Temperature 446 °F |
ISO 1133 |
| Polykemi AB POLYfill PPC K20010 PP, 10% Mineral Reinforced Information provided by Polykemi AB |
|||
| Melt Index of Compound | 20 g/10 min @Load 2.16 kg, Temperature 230 °C |
20 g/10 min @Load 4.76 lb, Temperature 446 °F |
ISO 1133 |
| Polykemi AB POLYfill PPH K20020 D Polypropylene Homopolymer, Mineral Reinforced, Detergent Resistant Information provided by Polykemi AB |
|||
| Melt Index of Compound | 20 g/10 min @Load 5.00 kg, Temperature 260 °C |
20 g/10 min @Load 11.0 lb, Temperature 500 °F |
ISO 1133 |
| Polykemi AB SCANBLEND FS7 PC/ASA Blend with Improved Weather Resistance Information provided by Polykemi AB |
|||
| Melt Index of Compound | 20 g/10 min @Load 5.00 kg, Temperature 260 °C |
20 g/10 min @Load 11.0 lb, Temperature 500 °F |
MVR [cm^3/10 min]; ISO 1133 |
| SABIC Innovative Plastics Lexan® ML6413 PC Lexan* ML6413 resin is an impact modified, flame retardant polycarbonate grade with Br- & Cl-free FR systems. It features improved light shielding capability with good flow, impact and thermal prope.. |
|||
| Melt Index of Compound | 20 g/10 min @Load 21.6 kg, Temperature 190 °C |
20 g/10 min @Load 47.6 lb, Temperature 374 °F |
|
| Huntsman IROGRAN® A 85 H 4827 TPU-Polyester Introduction: IROGRAN A 85 H 4827 is a thermoplastic polyester polyurethane for injection molding applications. IROGRAN A 85 H 4827 is part of the HUNTSMAN technical injection molding product range .. |
|||
| Melt Index of Compound | 20 g/10 min @Load 2.16 kg, Temperature 190 °C |
20 g/10 min @Load 4.76 lb, Temperature 374 °F |
ASTM D1238 |
| ICO Polymers ICOFLOâ„¢ 510-5007 1200 Micron HDPE Powder Description: ICOFLO 510-5007 is a premium polyethylene powder specifically designed to be used in the preparation of masterbatch (concentrate). By utilizing a free flowing powder as a carrier in ma.. |
|||
| Melt Index of Compound | 20 g/10 min @Load 2.16 kg, Temperature 190 °C |
20 g/10 min @Load 4.76 lb, Temperature 374 °F |
ASTM D1238 |
| ICO Polymers ICOFLOâ„¢ 510-5072 1200 Micron LLDPE Powder Description: ICOFLO 510-5072 is a premium polyethylene powder specifically designed to be used in the preparation of masterbatch (concentrate). By utilizing a free flowing powder as a carrier in ma.. |
|||
| Melt Index of Compound | 20 g/10 min @Load 2.16 kg, Temperature 190 °C |
20 g/10 min @Load 4.76 lb, Temperature 374 °F |
ASTM D1238 |
| ICO Polymers ICOTEXâ„¢ 520-5076 500 Micron EVA Powder Description: ICOTEX 520-5076 is an EVA powder that has been developed to meet the special requirements of the textile coating industry. Its key characteristics are a good melt flow and flexibility,.. |
|||
| Melt Index of Compound | 20 g/10 min @Load 5.00 kg, Temperature 360 °C |
20 g/10 min @Load 11.0 lb, Temperature 680 °F |
MVR [cm^3/10 min]; ISO 1133 |
| SABIC Innovative Plastics ULTEM ATX3562R PEI+PCE (Europe-Africa-Middle East) 50% Glass fiber and mineral filled, high flow Polyetherimide blend with internal mold release and enhanced dimensional stability. RoHS compliant. |
|||
| Melt Index of Compound | 20 g/10 min @Load 5.00 kg, Temperature 360 °C |
20 g/10 min @Load 11.0 lb, Temperature 680 °F |
MVR [cm^3/10 min]; ISO 1133 |
| SABIC Innovative Plastics ULTEM UF5011S PEI Enhanced flow, Specialty filtered Polyetherimide (Tg 225C) with enhanced chemical resistance to strong acids, bases, aromatics and ketones. ECO Conforming. |
|||
| Melt Index of Compound | 20 g/10 min @Load 1.20 kg, Temperature 250 °C |
20 g/10 min @Load 2.65 lb, Temperature 482 °F |
MVR [cm^3/10 min]; ISO 1133 |
| SABIC Innovative Plastics Valox® VX3101N PBT (Europe-Africa-Middle East) VALOX VX3101N is an unreinforced PBT injection moulding resin, with excellent flow properties, good hydrolitical stability and chemical resistance. |
|||
| Melt Index of Compound | 20 g/10 min @Load 2.16 kg, Temperature 300 °C |
20 g/10 min @Load 4.76 lb, Temperature 572 °F |
MVR [cm^3/10 min]; ISO 1133 |
| SABIC Innovative Plastics LNP THERMOCOMP D351 PC (Asia Pacific) LNP* Thermocomp* D351 (experimental grade name as EXTC8143) is a compound based on Polycarbonate resin containing Glass Fiber, Flame Retardant. Added features of this material include: High modulus,.. |
|||
| Melt Index of Compound | 20 - 30 g/10 min | 20 - 30 g/10 min | I Preparation |
| Sibur ABS 1030 (30,31) Molding Grade ABS Plastic With high fluidity of melting, thermal and light resistance for large parts of devices, parts of refrigerators, and for hearing aids. Mark is allowed for contact with food products. |
|||
| Melt Index of Compound | 20 g/10 min @Load 10.0 kg, Temperature 300 °C |
20 g/10 min @Load 22.0 lb, Temperature 572 °F |
MVR [cm^3/10 min]; ISO 1133 |
| SABIC Innovative Plastics NORYL GFN1740V PPE+PS Noryl* GFN1740V Polyphenylene Oxide (PPO) + Polystyrene (PS) resin is a 40 % Glass Reinforced, injection moldable grade with improved hydrolytic stability and with a Tensile Modulus > 11000 MPa; thi.. |
|||
| Melt Index of Compound | 20 g/10 min @Load 5.00 kg, Temperature 360 °C |
20 g/10 min @Load 11.0 lb, Temperature 680 °F |
MVR [cm^3/10 min]; ISO 1133 |
| SABIC Innovative Plastics ULTEM UF5011S PEI (Europe-Africa-Middle East) Enhanced flow, Specialty filtered Polyetherimide (Tg 225C) with enhanced chemical resistance to strong acids, bases, aromatics and ketones. ECO Conforming. |
|||
| Melt Index of Compound | 20 g/10 min @Load 2.16 kg, Temperature 250 °C |
20 g/10 min @Load 4.76 lb, Temperature 482 °F |
MVR [cm^3/10 min]; ISO 1133 |
| SABIC Innovative Plastics Valox® ENH3500 PBT (Europe-Africa-Middle East) Unfilled PBT, Non-Brominated & Non-Chlorinated Flame Retardant |
|||
| Melt Index of Compound | 20 g/10 min @Load 2.16 kg, Temperature 190 °C |
20 g/10 min @Load 4.76 lb, Temperature 374 °F |
Condition E; ASTM D1238 |
| A. Schulman CP808-01 Natural Linear, Low-Density Polyethylene DescriptionCP 808-01 is a lineal low-density polyethylene having good processability and exceptional toughness in injection molded parts. This compound has excellent flexibility, high impact streng.. |
|||
| Melt Index of Compound | 20 g/10 min @Load 2.16 kg, Temperature 190 °C |
20 g/10 min @Load 4.76 lb, Temperature 374 °F |
Condition E; ASTM D1238 |
| A. Schulman CP808-01 Natural Linear, Low-Density Polyethylene DescriptionCP 808-01 is a lineal low-density polyethylene having good processability and exceptional toughness in injection molded parts. This compound has excellent flexibility, high impact streng.. |
|||
| Melt Index of Compound | 20 g/10 min | 20 g/10 min | Condition E; ASTM D1238 |
| A. Schulman LP481 Molding Grade High-Density Polyethylene DescriptionLP 481 is a molding grade high-density polyethylene. Information provided by A. Schulman. |
|||
| Melt Index of Compound | 20 g/10 min @Temperature 230 °C |
20 g/10 min @Temperature 446 °F |
ASTM D1238 |
| A. Schulman PP 1579 Polypropylene Impact Grade Polypropylene DescriptionPolypropylene PP 1579 is an impact grade of polypropylene for use in parts which require good impact and good appearance in light weight injection molded parts. Information provided by A.. |
|||
| Melt Index of Compound | 20 g/10 min | 20 g/10 min | 2.16/230; ASTM D1238 |
| A. Schulman POLYAXIS® PD8020 Polypropylene DescriptionPolyaxis PD 8020 is a polypropylene designed from rotational molding with a combination of good stiffness and ESCR.NOTE: Physical properties are based on rotationally molded samples from .. |
|||
| Melt Index of Compound | 20 g/10 min | 20 g/10 min | ASTM D1238 |
| Cheng Yu Plastic PP231H TALC 40 Polypropylene, 40% Talc, High Heat |
|||
| Melt Index of Compound | 20 - 30 g/10 min @Load 5.00 kg, Temperature 260 °C |
20 - 30 g/10 min @Load 11.0 lb, Temperature 500 °F |
ASTM D1238, ISO 1133 |
| EPICHEM Epiblend PC/ABS nero Polycarbonate/ABS |
|||
| Melt Index of Compound | 20 g/10 min @Load 2.16 kg, Temperature 190 °C |
20 g/10 min @Load 4.76 lb, Temperature 374 °F |
ASTM D1238 |
| Dow DMDA-8920 NT 7 High Density Polyethylene Resin DOW DMDA-8920 NT 7 is produced using UNIPOL™ process technology. It is intended for use in a broad range of injection molding applications such as housewares, toys, food containers and pails. Info.. |
|||
| Melt Index of Compound | 20 - 30 g/10 min @Load 5.00 kg, Temperature 260 °C |
20 - 30 g/10 min @Load 11.0 lb, Temperature 500 °F |
ASTM D1238, ISO 1133 |
| EPICHEM Epiblend PC/ABS nero Polycarbonate/ABS Characteristics: Thermic resistant |
|||
| Melt Index of Compound | 20 g/10 min @Temperature 230 °C |
20 g/10 min @Temperature 446 °F |
ASTM D1238 |
| Amco PRIMATOP PP HOMO 201NA Injection Molding Polypropylene Features:nucleationanti-statlow viscosityexcellent processabilityexcellent stiffnessminimal odor or tasteApplications:thin wall partsclosuressmall appliancesFormer A-Top Polymers product; part of Am.. |
|||
| Melt Index of Compound | 20 g/10 min @Load 2.16 kg, Temperature 230 °C |
20 g/10 min @Load 4.76 lb, Temperature 446 °F |
ISO 1133 |
| Polykemi AB POLYfill PPH T20040 Polypropylene Homopolymer, Mineral Reinforced Information provided by Polykemi AB |
|||
| Melt Index of Compound | 20 g/10 min @Load 2.16 kg, Temperature 190 °C |
20 g/10 min @Load 4.76 lb, Temperature 374 °F |
ASTM D1238 |
| Chase Plastics CP Pryme® PE200-HD20M General Purpose High Density Polyethylene Information provided by Chase Plastics. |
|||
| Melt Index of Compound | 20 g/10 min @Load 10.0 kg, Temperature 300 °C |
20 g/10 min @Load 22.0 lb, Temperature 572 °F |
MVR [cm^3/10 min]; ISO 1133 |
| SABIC Innovative Plastics NORYL FE1740PW PPE+PS (Europe-Africa-Middle East) Noryl* FE1740PW Polyphenylene Oxide (PPO) + Polystyrene (PS) resin is a 40 % Glass Reinforced, injection moldable grade with improved hydrolytic stability and with a Tensile Modulus > 11000 MPa; thi.. |
|||