LNP Stat-Kon® EC-1004 Polyetherimide, Carbon Fiber Reinforcement  (discontinued **)

Category Polymer , Thermoplastic , Polyetherimide (PEI) , Polyetherimide (PEI), Carbon Fiber Filled
Manufacturer
Trade Name
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF LNP Stat-Kon® EC-1004 Polyetherimide, Carbon Fiber Reinforcement  (discontinued **).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Features: Electrically ConductiveForms: PelletsProcessing Method: Injection MoldingInformation provided by LNP, a GE Plastics Company.This data sheet is labeled Discontinued; however many LNP grades are still active under new names instituted after the SABIC purchase.
Physical Properties Metric English Comments
Specific Gravity 1.34 g/cc
1.34 g/cc
Method A; ASTM D792
Linear Mold Shrinkage, Transverse 0.0040 cm/cm
0.0040 in/in
ASTM D955
Mechanical Properties Metric English Comments
Tensile Strength at Break 232 MPa
33600 psi
ASTM D638
Elongation at Break 1.7 %
1.7 %
ASTM D638
Flexural Strength 303 MPa
43900 psi
ASTM D790
Flexural Modulus 16.0 GPa
2320 ksi
ASTM D790
Izod Impact, Notched 0.587 J/cm

@Thickness 3.18 mm
1.10 ft-lb/in

@Thickness 0.125 in
ASTM D256
Izod Impact, Unnotched 5.34 J/cm

@Thickness 3.18 mm
10.0 ft-lb/in

@Thickness 0.125 in
ASTM D256
Thermal Properties Metric English Comments
Deflection Temperature at 1.8 MPa (264 psi) 213 °C
415 °F
Unannealed; ASTM D648
Electrical Properties Metric English Comments
Volume Resistivity 1.00e+6 ohm-cm
1.00e+6 ohm-cm
ASTM D257
Surface Resistance 10000 ohm
10000 ohm
ASTM D257
Processing Properties Metric English Comments
Melt Temperature 360 - 366 °C
680 - 691 °F
Mold Temperature 121 - 149 °C
250 - 300 °F
Drying Temperature 121 - 149 °C
250 - 300 °F
Dry Time 4 hour
4 hour
Moisture Content 0.020 %
0.020 %
Suggested
Back Pressure 0.345 - 0.689 MPa
50.0 - 99.9 psi