- Clariant Renol 612G10-L Nylon 612, 10% Glass Fiber Reinforced, Lubricated
Clariant Renol 612G10-L Nylon 612, 10% Glass Fiber Reinforced, Lubricated
| Category | Polymer , Thermoplastic , Nylon , Nylon 612 , Nylon 612, Glass Fiber Filler |
| Manufacturer | Clariant |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Clariant Renol 612G10-L Nylon 612, 10% Glass Fiber Reinforced, Lubricated.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Data provided by Clariant Masterbatches
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Filler Content | 10 % | 10 % | ASTM D2584 |
| Linear Mold Shrinkage | 0.0040 - 0.0060 cm/cm | 0.0040 - 0.0060 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 75.8 MPa | 11000 psi | ASTM D638 |
| Elongation at Yield | 4.0 % | 4.0 % | ASTM D638 |
| Flexural Yield Strength | 110 MPa | 16000 psi | ASTM D790 |
| Flexural Modulus | 3.45 GPa | 500 ksi | ASTM D790 |
| Izod Impact, Notched | 0.427 J/cm @Temperature 22.8 °C |
0.800 ft-lb/in @Temperature 73.0 °F |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 196 °C | 385 °F | ASTM D648 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 243 - 271 °C | 470 - 520 °F | |
| Mold Temperature | 79.4 - 93.3 °C | 175 - 200 °F | |
| Dry Time | 2 - 4 hour @Temperature 79.4 °C |
2 - 4 hour @Temperature 175 °F |
to ensure moisture content of 0.2% or less |
| Injection Pressure | 4.96 - 8.27 MPa | 720 - 1200 psi | Secondary |
| 8.27 - 13.8 MPa | 1200 - 2000 psi | Initial | |
| Back Pressure | 0.172 - 0.517 MPa | 25.0 - 75.0 psi | |
| Shot Size | 30 - 80 % | 30 - 80 % | |
| Screw Speed | 20 - 100 rpm | 20 - 100 rpm |
Users viewing this material also viewed the following:
- NanoAmor 50% DWNT Double Walled Carbon Nanotubes
- Hyosung Topilene J340F PP
- LG Chemical LUCEL N127LD POM, Chemical Resistance
- Industrial Laminates/Norplex MC511A Glass Fabric
- SABIC Innovative Plastics Ultem ATX203R PEI+PCE (Asia Pacific)
- A. Schulman POLYFLAM™ E-13030B Reinforced Super Coupled Polypropylene Black
- ExxonMobil Paxon™ AD60-007 Blow Molding Resin
- ACC SMP™ EP EF SP EPI Engineered Polymers Extra Flex with Silicone
- Formosa Plastics Formolene® 5181K Homopolymer Polypropylene
- Karina 06/152-FC-LMP Blue Color Concentrate for PVC
Copyright © lookpolymers.com All Rights Reserved