Arkema Group Kynar Super Flex® 2500 PVDF Copolymer (discontinued **)

Category	Polymer , Thermoplastic , Fluoropolymer , PVDF , Polyvinylidinefluoride (PVDF), Molded/Extruded
Manufacturer
Trade Name
Port	Ningbo port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Arkema Group Kynar Super Flex® 2500 PVDF Copolymer (discontinued **).pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Copolymer Series, Kynar® components are used extensively in the high purity semiconductor market, the pulp and paper industry, nuclear waste processing, and the general chemical processing industryInformation provided by Arkema Group

Physical Properties	Metric	English	Comments
Specific Gravity	1.80 - 1.82 g/cc	1.80 - 1.82 g/cc	ASTM D792
Water Absorption	0.040 - 0.070 %	0.040 - 0.070 %	24 hr / 20°C; ASTM D570
Viscosity	8.00e+6 cP @Shear Rate 100 1/s, Temperature 232 °C	8.00e+6 cP @Shear Rate 100 1/s, Temperature 450 °F	ASTM D3835
Ash	0.00 - 5.0 %	0.00 - 5.0 %	Thermal Decomposition/ in air

Mechanical Properties	Metric	English	Comments
Hardness, Shore D	55 - 60	55 - 60	ASTM D2240
Tensile Strength, Ultimate	27.6 - 41.4 MPa	4000 - 6000 psi	ASTM D638
Tensile Strength, Yield	11.7 - 19.3 MPa	1700 - 2800 psi	ASTM D638
Elongation at Break	500 - 800 %	500 - 800 %	ASTM D638
Elongation at Yield	12 - 25 %	12 - 25 %	ASTM D638
Tensile Modulus	0.241 - 0.379 GPa	35.0 - 55.0 ksi	ASTM D638
Flexural Strength	10.3 - 17.2 MPa	1500 - 2500 psi	@ 5% strain; ASTM D790
Flexural Modulus	0.193 - 0.248 GPa	28.0 - 36.0 ksi	ASTM D790
Compressive Strength	13.8 - 20.7 MPa	2000 - 3000 psi	ASTM D695
Izod Impact, Notched	NB	NB	ASTM D256
Izod Impact, Unnotched	NB	NB	ASTM D256
Coefficient of Friction, Dynamic	0.54	0.54	vs. Steel; ASTM D1894
Coefficient of Friction, Static	0.49	0.49	vs. Steel; ASTM D1894
Taber Abrasion, mg/1000 Cycles	28 - 33	28 - 33	CS-17 1000g:load

Thermal Properties	Metric	English	Comments
CTE, linear	153 - 194 µm/m-°C @Temperature 20.0 °C	85.0 - 108 µin/in-°F @Temperature 68.0 °F	ASTM D696
Specific Heat Capacity	1.17 - 1.51 J/g-°C	0.280 - 0.360 BTU/lb-°F	DSC
Thermal Conductivity	0.144 - 0.180 W/m-K	1.00 - 1.25 BTU-in/hr-ft²-°F	ASTM D433
Melting Point	116 - 121 °C	240 - 250 °F	ASTM D3418
Deflection Temperature at 1.8 MPa (264 psi)	26.7 - 37.8 °C	80.0 - 100 °F	ASTM D648
Glass Transition Temp, Tg	-46.0 - -40.0 °C	-50.8 - -40.0 °F	(DMA) @ 1 Hz
Decomposition Temperature	375 °C	707 °F	1% wt. loss / in air
	410 °C	770 °F	1% wt. loss / in nitrogen
Oxygen Index	42 %	42 %	Optional product available with value of 95% O<sub>2</sub>; ASTM D2868

Optical Properties	Metric	English	Comments
Refractive Index	1.40 @Temperature 25.0 °C, Wavelength 589.3 nm	1.40 @Temperature 77.0 °F, Wavelength 589.3 nm	Sodium D line; ASTM D542

Electrical Properties	Metric	English	Comments
Volume Resistivity	2.00e+14 ohm-cm	2.00e+14 ohm-cm	DC, 65% RH; ASTM D257
Dielectric Constant	4.5 - 5.8 @Frequency 1e+8 Hz	4.5 - 5.8 @Frequency 1e+8 Hz	ASTM D150
	10.9 - 13.5 @Frequency 100 Hz	10.9 - 13.5 @Frequency 100 Hz	ASTM D150
Dielectric Strength	31.5 - 43.3 kV/mm	800 - 1100 kV/in	ASTM D149
Dissipation Factor	0.060 - 0.10 @Frequency 100 Hz	0.060 - 0.10 @Frequency 100 Hz	ASTM D150
	0.25 - 0.29 @Frequency 1e+8 Hz	0.25 - 0.29 @Frequency 1e+8 Hz	ASTM D150