Overview of materials for Acetal Copolymer, 30% Glass Fiber Reinforced

Category Polymer , Thermoplastic , Acetal (POM) , Acetal Copolymer, 30% Glass Fiber Reinforced
Manufacturer
Trade Name
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Overview of materials for Acetal Copolymer, 30% Glass Fiber Reinforced.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
This property data is a summary of similar materials in the MatWeb database for the category "Acetal Copolymer, 30% Glass Fiber Reinforced". Specific grades with glass content between 25% and 34% are included. Each property range of values reported is minimum and maximum values of appropriate MatWeb entries. The comments report the average value, and number of data points used to calculate the average. The values are not necessarily typical of any specific grade, especially less common values and those that can be most affected by additives or processing methods.
Physical Properties Metric English Comments
Density 1.35 - 1.75 g/cc
0.0488 - 0.0632 lb/in³
Average value: 1.60 g/cc Grade Count:76
Filler Content 25.0 - 30.0 %
25.0 - 30.0 %
Average value: 27.8 % Grade Count:18
Water Absorption 0.180 - 0.900 %
0.180 - 0.900 %
Average value: 0.470 % Grade Count:24
Moisture Absorption at Equilibrium 0.100 - 0.300 %
0.100 - 0.300 %
Average value: 0.201 % Grade Count:18
Water Absorption at Saturation 0.200 - 0.900 %
0.200 - 0.900 %
Average value: 0.686 % Grade Count:11
Linear Mold Shrinkage 0.00100 - 0.0220 cm/cm
0.00100 - 0.0220 in/in
Average value: 0.00589 cm/cm Grade Count:58
Linear Mold Shrinkage, Transverse 0.00800 - 0.0400 cm/cm
0.00800 - 0.0400 in/in
Average value: 0.0140 cm/cm Grade Count:25
Melt Flow 0.300 - 16.0 g/10 min
0.300 - 16.0 g/10 min
Average value: 6.67 g/10 min Grade Count:26
Mechanical Properties Metric English Comments
Hardness, Rockwell M 80.0 - 95.0
80.0 - 95.0
Average value: 87.2 Grade Count:9
Hardness, Rockwell R 84.0 - 112
84.0 - 112
Average value: 99.5 Grade Count:11
Ball Indentation Hardness 175 - 239 MPa
25400 - 34700 psi
Average value: 204 MPa Grade Count:7
Tensile Strength, Ultimate 10.0 - 182 MPa
1450 - 26400 psi
Average value: 103 MPa Grade Count:57
45.0 - 158.579 MPa

@Temperature -40.0 - 120 °C
6530 - 23000.0 psi

@Temperature -40.0 - 248 °F
Average value: 75.1 MPa Grade Count:3
Tensile Strength, Yield 38.0 - 137 MPa
5510 - 19800 psi
Average value: 91.6 MPa Grade Count:23
26.2001 - 125 MPa

@Temperature -40.0 - 120 °C
3800.01 - 18100 psi

@Temperature -40.0 - 248 °F
Average value: 74.9 MPa Grade Count:2
Elongation at Break 1.00 - 13.0 %
1.00 - 13.0 %
Average value: 2.92 % Grade Count:68
4.00 - 5.80 %

@Temperature 60.0 - 90.0 °C
4.00 - 5.80 %

@Temperature 140 - 194 °F
Average value: 4.90 % Grade Count:1
Elongation at Yield 2.00 - 6.00 %
2.00 - 6.00 %
Average value: 3.42 % Grade Count:8
Modulus of Elasticity 3.70 - 12.9 GPa
537 - 1870 ksi
Average value: 8.84 GPa Grade Count:52
2.50 - 8.10 GPa

@Temperature 40.0 - 140 °C
363 - 1170 ksi

@Temperature 104 - 284 °F
Average value: 5.10 GPa Grade Count:2
Flexural Yield Strength 38.0 - 285 MPa
5510 - 41300 psi
Average value: 161 MPa Grade Count:54
Flexural Modulus 3.24 - 10.9 GPa
470 - 1580 ksi
Average value: 7.78 GPa Grade Count:62
3.44738 - 5.70 GPa

@Temperature 60.0 - 120 °C
500.008 - 827 ksi

@Temperature 140 - 248 °F
Average value: 4.45 GPa Grade Count:2
Izod Impact, Notched 0.374 - 5.34 J/cm
0.700 - 10.0 ft-lb/in
Average value: 0.765 J/cm Grade Count:48
0.37373 - 0.550 J/cm

@Temperature -40.0 - 82.2 °C
0.70015 - 1.03 ft-lb/in

@Temperature -40.0 - 180 °F
Average value: 0.459 J/cm Grade Count:3
Izod Impact, Unnotched 2.67 - 7.01 J/cm
5.00 - 13.1 ft-lb/in
Average value: 5.28 J/cm Grade Count:21
Izod Impact, Notched (ISO) 2.60 - 9.00 kJ/m²
1.24 - 4.28 ft-lb/in²
Average value: 6.18 kJ/m² Grade Count:20
6.00 - 9.00 kJ/m²

@Temperature -30.0 - -30.0 °C
2.86 - 4.28 ft-lb/in²

@Temperature -22.0 - -22.0 °F
Average value: 7.50 kJ/m² Grade Count:2
Izod Impact, Unnotched (ISO) 18.0 - 41.0 kJ/m²
8.57 - 19.5 ft-lb/in²
Average value: 30.5 kJ/m² Grade Count:8
Charpy Impact Unnotched 2.00 - 7.00 J/cm²
9.52 - 33.3 ft-lb/in²
Average value: 4.04 J/cm² Grade Count:13
1.80 - 6.00 J/cm²

@Temperature -40.0 - -20.0 °C
8.57 - 28.6 ft-lb/in²

@Temperature -40.0 - -4.00 °F
Average value: 3.64 J/cm² Grade Count:7
Charpy Impact, Notched 0.240 - 4.10 J/cm²
1.14 - 19.5 ft-lb/in²
Average value: 0.912 J/cm² Grade Count:29
0.220 - 0.880 J/cm²

@Temperature -30.0 - -30.0 °C
1.05 - 4.19 ft-lb/in²

@Temperature -22.0 - -22.0 °F
Average value: 0.539 J/cm² Grade Count:7
Dart Drop, Total Energy 8.00 - 10.0 J
5.90 - 7.38 ft-lb
Average value: 9.00 J Grade Count:6
Tensile Creep Modulus, 1 hour 3300 - 7700 MPa
479000 - 1.12e+6 psi
Average value: 4770 MPa Grade Count:3
Tensile Creep Modulus, 1000 hours 2100 - 5800 MPa
305000 - 841000 psi
Average value: 3850 MPa Grade Count:4
Thermal Properties Metric English Comments
CTE, linear 4.00 - 95.1 µm/m-°C
2.22 - 52.8 µin/in-°F
Average value: 55.2 µm/m-°C Grade Count:26
CTE, linear, Transverse to Flow 36.0 - 125 µm/m-°C
20.0 - 69.4 µin/in-°F
Average value: 77.1 µm/m-°C Grade Count:18
Specific Heat Capacity 1.21 - 1.81 J/g-°C
0.289 - 0.433 BTU/lb-°F
Average value: 1.40 J/g-°C Grade Count:6
Melting Point 165 - 203 °C
329 - 397 °F
Average value: 168 °C Grade Count:32
Maximum Service Temperature, Air 85.0 - 140 °C
185 - 284 °F
Average value: 109 °C Grade Count:7
Deflection Temperature at 0.46 MPa (66 psi) 149 - 183 °C
300 - 361 °F
Average value: 165 °C Grade Count:33
Deflection Temperature at 1.8 MPa (264 psi) 76.7 - 166 °C
170 - 331 °F
Average value: 156 °C Grade Count:62
Vicat Softening Point 150 - 162 °C
302 - 324 °F
Average value: 158 °C Grade Count:9
Flammability, UL94 HB
HB
Grade Count:38
Electrical Properties Metric English Comments
Electrical Resistivity 10000 - 1.00e+16 ohm-cm
10000 - 1.00e+16 ohm-cm
Average value: 1.10e+15 ohm-cm Grade Count:33
Surface Resistance 1.00e+6 - 5.00e+16 ohm
1.00e+6 - 5.00e+16 ohm
Average value: 6.27e+15 ohm Grade Count:23
Dielectric Constant 4.00 - 5.00
4.00 - 5.00
Average value: 4.30 Grade Count:11
Dielectric Strength 17.7 - 43.0 kV/mm
450 - 1090 kV/in
Average value: 27.4 kV/mm Grade Count:22
Dissipation Factor 0.00300 - 0.0300
0.00300 - 0.0300
Average value: 0.00987 Grade Count:11
Comparative Tracking Index 500 - 600 V
500 - 600 V
Average value: 592 V Grade Count:12
Processing Properties Metric English Comments
Processing Temperature 20.0 - 230 °C
68.0 - 446 °F
Average value: 160 °C Grade Count:25
Nozzle Temperature 180 - 220 °C
356 - 428 °F
Average value: 199 °C Grade Count:4