Overview of materials for Polyphenylene Ether, 30% Glass Filled

Category Polymer , Thermoplastic , Polyphenylene Ether/PPO , Polyphenylene Ether, 30% Glass Filled
Manufacturer
Trade Name
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Overview of materials for Polyphenylene Ether, 30% Glass Filled.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
This property data is a summary of similar materials in the MatWeb database for the category "Polyphenylene Ether, 30% Glass Filled". Specific grades with glass content between 25% and 34% are included. Each property range of values reported is minimum and maximum values of appropriate MatWeb entries. The comments report the average value, and number of data points used to calculate the average. The values are not necessarily typical of any specific grade, especially less common values and those that can be most affected by additives or processing methods.
Physical Properties Metric English Comments
Density 1.24 - 1.33 g/cc
0.0448 - 0.0480 lb/in³
Average value: 1.29 g/cc Grade Count:24
Filler Content 30.0 %
30.0 %
Average value: 30.0 % Grade Count:3
Water Absorption 0.00600 - 0.500 %
0.00600 - 0.500 %
Average value: 0.105 % Grade Count:12
Linear Mold Shrinkage 0.00100 - 0.00600 cm/cm
0.00100 - 0.00600 in/in
Average value: 0.00253 cm/cm Grade Count:16
Linear Mold Shrinkage, Transverse 0.00400 - 0.00800 cm/cm
0.00400 - 0.00800 in/in
Average value: 0.00550 cm/cm Grade Count:4
Melt Flow 1.00 - 16.0 g/10 min
1.00 - 16.0 g/10 min
Average value: 8.42 g/10 min Grade Count:6
Mechanical Properties Metric English Comments
Hardness, Rockwell L 108
108
Average value: 108 Grade Count:3
Tensile Strength, Ultimate 82.7 - 124 MPa
12000 - 18000 psi
Average value: 104 MPa Grade Count:19
40.0 - 80.0 MPa

@Temperature 60.0 - 120 °C
5800 - 11600 psi

@Temperature 140 - 248 °F
Average value: 60.0 MPa Grade Count:2
Tensile Strength, Yield 103 - 138 MPa
15000 - 20000 psi
Average value: 118 MPa Grade Count:7
Elongation at Break 1.00 - 8.00 %
1.00 - 8.00 %
Average value: 3.61 % Grade Count:21
1.50 - 2.80 %

@Temperature 60.0 - 120 °C
1.50 - 2.80 %

@Temperature 140 - 248 °F
Average value: 2.17 % Grade Count:2
Elongation at Yield 1.00 - 2.00 %

@Temperature 120 - 120 °C
1.00 - 2.00 %

@Temperature 248 - 248 °F
Average value: 1.50 % Grade Count:2
Modulus of Elasticity 5.86 - 9.00 GPa
850 - 1310 ksi
Average value: 8.07 GPa Grade Count:12
4.30 - 7.80 GPa

@Temperature 60.0 - 120 °C
624 - 1130 ksi

@Temperature 140 - 248 °F
Average value: 6.02 GPa Grade Count:2
Flexural Yield Strength 117 - 228 MPa
17000 - 33100 psi
Average value: 154 MPa Grade Count:16
Flexural Modulus 4.83 - 8.27 GPa
700 - 1200 ksi
Average value: 7.02 GPa Grade Count:18
Izod Impact, Notched 0.694 - 1.27 J/cm
1.30 - 2.39 ft-lb/in
Average value: 1.01 J/cm Grade Count:17
0.5339 - 0.74746 J/cm

@Temperature -40.0 - -30.0 °C
1.000 - 1.4003 ft-lb/in

@Temperature -40.0 - -22.0 °F
Average value: 0.641 J/cm Grade Count:2
Izod Impact, Unnotched 3.20 - 6.41 J/cm
6.00 - 12.0 ft-lb/in
Average value: 4.34 J/cm Grade Count:4
Charpy Impact Unnotched 1.80 - 4.80 J/cm²
8.57 - 22.8 ft-lb/in²
Average value: 2.77 J/cm² Grade Count:6
2.00 - 2.50 J/cm²

@Temperature -20.0 - -20.0 °C
9.52 - 11.9 ft-lb/in²

@Temperature -4.00 - -4.00 °F
Average value: 2.25 J/cm² Grade Count:2
Charpy Impact, Notched 0.630 - 1.40 J/cm²
3.00 - 6.66 ft-lb/in²
Average value: 0.826 J/cm² Grade Count:8
0.600 - 0.600 J/cm²

@Temperature -20.0 - -20.0 °C
2.86 - 2.86 ft-lb/in²

@Temperature -4.00 - -4.00 °F
Average value: 0.600 J/cm² Grade Count:2
Thermal Properties Metric English Comments
CTE, linear 0.702 - 50.0 µm/m-°C
0.390 - 27.8 µin/in-°F
Average value: 29.7 µm/m-°C Grade Count:7
Thermal Conductivity 0.173 - 0.280 W/m-K
1.20 - 1.94 BTU-in/hr-ft²-°F
Average value: 0.231 W/m-K Grade Count:4
Maximum Service Temperature, Air 110 - 120 °C
230 - 248 °F
Average value: 114 °C Grade Count:4
Deflection Temperature at 0.46 MPa (66 psi) 130 - 254 °C
266 - 489 °F
Average value: 162 °C Grade Count:15
Deflection Temperature at 1.8 MPa (264 psi) 125 - 235 °C
257 - 455 °F
Average value: 150 °C Grade Count:23
Vicat Softening Point 135 - 195 °C
275 - 383 °F
Average value: 149 °C Grade Count:9
Flammability, UL94 HB - 5VA
HB - 5VA
Grade Count:13
Electrical Properties Metric English Comments
Electrical Resistivity 1.00e+15 - 1.00e+17 ohm-cm
1.00e+15 - 1.00e+17 ohm-cm
Average value: 3.95e+16 ohm-cm Grade Count:11
Surface Resistance 1.00e+13 - 1.00e+15 ohm
1.00e+13 - 1.00e+15 ohm
Average value: 3.22e+14 ohm Grade Count:5
Dielectric Constant 2.90 - 3.15
2.90 - 3.15
Average value: 2.99 Grade Count:6
Dielectric Strength 18.0 - 53.0 kV/mm
457 - 1350 kV/in
Average value: 29.6 kV/mm Grade Count:6
Dissipation Factor 0.00100 - 0.00270
0.00100 - 0.00270
Average value: 0.00171 Grade Count:5
Comparative Tracking Index 175 - 325 V
175 - 325 V
Average value: 236 V Grade Count:7
Processing Properties Metric English Comments
Processing Temperature 232 - 282 °C
450 - 540 °F
Average value: 257 °C Grade Count:3
Melt Temperature 249 - 316 °C
480 - 600 °F
Average value: 288 °C Grade Count:9
Mold Temperature 65.6 - 120 °C
150 - 248 °F
Average value: 86.8 °C Grade Count:12
Drying Temperature 80.0 - 110 °C
176 - 230 °F
Average value: 95.1 °C Grade Count:7
Injection Pressure 68.9 - 103 MPa
10000 - 15000 psi
Average value: 86.2 MPa Grade Count:4