Overview of materials for Polyphenylene Ether, Mineral Filled

Category Polymer , Thermoplastic , Polyphenylene Ether/PPO , Polyphenylene Ether, Mineral Filled
Manufacturer
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Overview of materials for Polyphenylene Ether, Mineral Filled.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
This property data is a summary of similar materials in the MatWeb database for the category "Polyphenylene Ether, Mineral Filled". Each property range of values reported is minimum and maximum values of appropriate MatWeb entries. The comments report the average value, and number of data points used to calculate the average. The values are not necessarily typical of any specific grade, especially less common values and those that can be most affected by additives or processing methods.
Physical Properties Metric English Comments
Density 1.23 - 1.62 g/cc
0.0444 - 0.0585 lb/in³
Average value: 1.34 g/cc Grade Count:5
Linear Mold Shrinkage 0.00100 - 0.00700 cm/cm
0.00100 - 0.00700 in/in
Average value: 0.00505 cm/cm Grade Count:5
Mechanical Properties Metric English Comments
Tensile Strength, Ultimate 65.0 - 74.1 MPa
9430 - 10800 psi
Average value: 71.0 MPa Grade Count:3
20.0 - 55.0 MPa

@Temperature 60.0 - 120 °C
2900 - 7980 psi

@Temperature 140 - 248 °F
Average value: 38.3 MPa Grade Count:1
Elongation at Break 2.00 - 2.50 %

@Temperature 60.0 - 120 °C
2.00 - 2.50 %

@Temperature 140 - 248 °F
Average value: 2.23 % Grade Count:1
Elongation at Yield 1.50 - 1.50 %

@Temperature 120 - 120 °C
1.50 - 1.50 %

@Temperature 248 - 248 °F
Average value: 1.50 % Grade Count:1
Modulus of Elasticity 3.20 - 4.30 GPa

@Temperature 60.0 - 120 °C
464 - 624 ksi

@Temperature 140 - 248 °F
Average value: 3.70 GPa Grade Count:1
Flexural Modulus 3.38 - 11.7 GPa
490 - 1700 ksi
Average value: 5.50 GPa Grade Count:4
Izod Impact, Notched 0.160 - 2.14 J/cm
0.300 - 4.00 ft-lb/in
Average value: 1.57 J/cm Grade Count:4
Thermal Properties Metric English Comments
Deflection Temperature at 1.8 MPa (264 psi) 107 - 135 °C
225 - 275 °F
Average value: 114 °C Grade Count:5