- Wellman Wellamid® T-731E-BK 10% Reinforced Abrasion Resistant Nylon 6
Wellman Wellamid® T-731E-BK 10% Reinforced Abrasion Resistant Nylon 6
| Category | Polymer , Thermoplastic , Nylon , Nylon 6 |
| Manufacturer | Wellman Engineering Resins |
| Trade Name | Wellamid® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Wellman Wellamid® T-731E-BK 10% Reinforced Abrasion Resistant Nylon 6.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Description: Abrasion Resistant Nylon 6Information provided by Wellman.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.18 g/cc | 0.0426 lb/in³ | ISO 1183-87 |
| Filler Content | 10 % | 10 % | |
| Linear Mold Shrinkage, Flow | 0.0155 - 0.0175 cm/cm | 0.0155 - 0.0175 in/in | ISO DIS 294-4 |
| Linear Mold Shrinkage, Transverse | 0.014 - 0.016 cm/cm | 0.014 - 0.016 in/in | ISO DIS 294-4 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 65.0 MPa | 9430 psi | ISO 527-93 |
| Elongation at Break | 30 % | 30 % | ISO 527-93 |
| Flexural Strength | 90.0 MPa | 13100 psi | ISO 178-93 |
| Flexural Modulus | 2.60 GPa | 377 ksi | ISO 178-93 |
| Izod Impact, Notched (ISO) | 7.50 kJ/m² | 3.57 ft-lb/in² | ISO 180-93 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 220 °C | 428 °F | ISO 3146 |
| Deflection Temperature at 1.8 MPa (264 psi) | 55.0 °C | 131 °F | ISO 75-93 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Rear Barrel Temperature | 277 - 293 °C | 530 - 560 °F | |
| Middle Barrel Temperature | 271 - 288 °C | 520 - 550 °F | |
| Front Barrel Temperature | 266 - 282 °C | 510 - 540 °F | |
| Nozzle Temperature | 254 - 293 °C | 490 - 560 °F | |
| Melt Temperature | 271 - 293 °C | 520 - 560 °F | |
| Mold Temperature | 71.1 - 93.3 °C | 160 - 200 °F | |
| Drying Temperature | 79.4 °C | 175 °F | Opened bags and gaylord boxes |
| Dry Time | 2 - 4 hour | 2 - 4 hour | Opened bags and gaylord boxes |
| Moisture Content | 0.050 - 0.20 % | 0.050 - 0.20 % | During molding to prevent hydrolytic degradation |
| <= 0.20 % | <= 0.20 % | In shipping bags, ready to mold | |
| Injection Pressure | 34.5 - 138 MPa | 5000 - 20000 psi | |
| Back Pressure | 0.345 MPa | 50.0 psi | |
| Screw Speed | 30 - 120 rpm | 30 - 120 rpm |
Users viewing this material also viewed the following:
- DuPont Performance Polymers Sorona® 3015GV NC010 Polytrimethylene Terephthalate (PTT) (Unverified Data**)
- Lehmann & Voss LUVOCOM® 1-7004 Polyamide 66, with glass fiber and carbon fiber, heat stabilized
- Mitsubishi Xantar® SF 22 Polycarbonate
- Kuraray HYBRAR® Low Rebound Compound # 1
- LyondellBasell Petrothene® LP5100 High Density Polyethylene
- SABIC Innovative Plastics Valox® IQNH4550 PBT (Asia Pacific)
- Samsung Cheil Industries Infino® NH-1027HF PC/ABS, Unreinforced FR
- ChevronTexaco Rando® HD 68 Ashless
- Toyobo E2080A Thermoplastic Polyurethane Elastomer, Extrusion Grade
- Carpenter Gall-Tough® Stainless, Annealed and Cold Drawn Bar, 10% Cold Work
Copyright © lookpolymers.com All Rights Reserved