Unitika UNILATE® 1 NC PET

Category Polymer , Thermoplastic , Polyester, TP , Polyethylene Terephthalate (PET)
Manufacturer Unitika
Trade Name UNILATE® 1
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Unitika UNILATE® 1 NC PET.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Flame resisting gradeUNILATE® products are plate materials prepared by using a polyethylene terephthalate (PET resin) as the main component, blending it with glass staple fiber, inorganic filler, and others, and extruding the composite resins into plates, and laminating and heat-pressing the plates. UNILATE plates and boards are superior in heat resistance, withstand voltage, strength, and processability to the plates and boards of thermoplastic resins such as nylon, polyacetal, and others. The UNILATE plates and boards are greatly improved in water-absorbing property, electrical properties, and processability, compared to other thermosetting resin laminated sheets used in electric insulation applications.Information provided by Unitika Ltd.
Physical Properties Metric English Comments
Density 1.74 g/cc
0.0629 lb/in³
ASTM D792
Water Absorption 0.22 %
0.22 %
ASTM D570
Mechanical Properties Metric English Comments
Hardness, Rockwell R 80
80
ASTM D785
Tensile Strength at Break 56.0 MPa
8120 psi
Horizontal; ASTM D570
95.0 MPa
13800 psi
Vertical; ASTM D570
Elongation at Break 1.4 %
1.4 %
Horizontal; ASTM D570
2.0 %
2.0 %
Vertical; ASTM D570
Flexural Strength 95.0 MPa
13800 psi
Horizontal; ASTM D790
190 MPa
27600 psi
Vertical; ASTM D790
Flexural Modulus 6.00 GPa
870 ksi
Horizontal; ASTM D790
9.00 GPa
1310 ksi
Vertical; ASTM D790
Compressive Strength 130 MPa
18900 psi
ASTM D695
Shear Strength 49.0 MPa
7110 psi
ASTM D732
Izod Impact, Unnotched 0.540 J/cm
1.01 ft-lb/in
ASTM D256
Thermal Properties Metric English Comments
CTE, linear 50.0 µm/m-°C

@Temperature 25.0 - 100 °C
27.8 µin/in-°F

@Temperature 77.0 - 212 °F
Vertical; ASTM D696
80.0 µm/m-°C

@Temperature 25.0 - 100 °C
44.4 µin/in-°F

@Temperature 77.0 - 212 °F
Horizontal; ASTM D696
Thermal Conductivity 0.310 W/m-K
2.15 BTU-in/hr-ft²-°F
ASTM C177
Deflection Temperature at 0.46 MPa (66 psi) 235 °C
455 °F
ASTM D648
Flammability, UL94 V-0

@Thickness 0.600 mm
V-0

@Thickness 0.0236 in
Electrical Properties Metric English Comments
Volume Resistivity 1.00e+13 ohm-cm
1.00e+13 ohm-cm
ASTM D257
Surface Resistance 1.00e+15 ohm
1.00e+15 ohm
ASTM D257
Insulation Resistance 3.80e+14 ohm
3.80e+14 ohm
ASTM D257
Dielectric Constant 3.6

@Frequency 1.00e+6 Hz
3.6

@Frequency 1.00e+6 Hz
ASTM D150
Dielectric Strength 34.0 kV/mm
864 kV/in
Under ambient atmosphere; ASTM D149
34.0 kV/mm
864 kV/in
After water absorption; ASTM D149
Dissipation Factor 0.019

@Frequency 1.00e+6 Hz
0.019

@Frequency 1.00e+6 Hz
ASTM D150
Arc Resistance 80 sec
80 sec
Comparative Tracking Index 200 V
200 V
IEC 112
Descriptive Properties Value Comments
Appearance Opaque
Ignition Temperature 460°C
Copyright © lookpolymers.com All Rights Reserved