SABIC Innovative Plastics Noryl HS2000 PPE (Asia Pacific)
| Category | Polymer , Thermoplastic , Polyphenylene Ether/PPO |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | Noryl |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics Noryl HS2000 PPE (Asia Pacific).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
This data was supplied by SABIC-IP for the Asia Pacific region.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.24 g/cc | 1.24 g/cc | ASTM D 792 |
| Water Absorption | 0.12 % @Time 86400 sec |
0.12 % @Time 24.0 hour |
ASTM D 570 |
| Linear Mold Shrinkage, Flow | 0.0050 - 0.0070 cm/cm @Thickness 3.20 mm |
0.0050 - 0.0070 in/in @Thickness 0.126 in |
SABIC Method |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 121 | 121 | ASTM D 785 |
| Tensile Strength, Yield | 63.0 MPa | 9140 psi | SABIC - Japan Method |
| Elongation at Break | 60 % | 60 % | SABIC - Japan Method |
| Flexural Strength | 100 MPa | 14500 psi | ASTM D 790 |
| Flexural Modulus | 3.50 GPa | 508 ksi | ASTM D 790 |
| Izod Impact, Notched | 1.07 J/cm @Temperature 23.0 °C |
2.00 ft-lb/in @Temperature 73.4 °F |
ASTM D 256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 55.0 µm/m-°C @Temperature -30.0 - 30.0 °C |
30.6 µin/in-°F @Temperature -22.0 - 86.0 °F |
TMA |
| Deflection Temperature at 0.46 MPa (66 psi) | 115 °C @Thickness 3.20 mm |
239 °F @Thickness 0.126 in |
unannealed; ASTM D 648 |
| Flammability, UL94 | V-0 @Thickness 1.57 mm |
V-0 @Thickness 0.0618 in |
UL 94 |
| 5VA @Thickness 2.00 mm |
5VA @Thickness 0.0787 in |
UL 94 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Surface Resistance | 1.00e+14 ohm | 1.00e+14 ohm | ASTM D 257 |
| Dielectric Constant | 2.8 @Frequency 50.0 - 60.0 Hz |
2.8 @Frequency 50.0 - 60.0 Hz |
ASTM D 150 |
| Arc Resistance | 60 - 120 sec | 60 - 120 sec | Tungsten, PLC code 6; ASTM D 495 |
Users viewing this material also viewed the following:
- Michelman® Licomer® W 11 Anionic / Nonionic polyethylene emulsion
- Iran Petrochemical (PCC) Arak I3 HDPE
- A. Schulman POLYBATCH™ Navajo 10294U/4 Concentrate Based In LLDPE
- Formosa Plastics Formolon® 622F PVC
- TSE Industries Millathane® 5004 Millable Polyurethane Elastomer with 20 PHR N330 (HAF) Black
- Corning Large Cover Gorilla® Glass Touch Screen Glass
- BASF Ultramid® TG3S BK 5966 15% Glass Filled PA6 (Conditioned)
- Arkema Group Lacovyl® GB 1150 PVC, Pipe Grade
- Haynes Hastelloy® C-4 alloy, welded plate 12.7 mm (1/2 in.) thick, GTAW
- LATI Latimass 53-04 D009 PP Homopolymer, Impact Modified
Copyright © lookpolymers.com All Rights Reserved