DuPont Performance Polymers Zytel® 101 NC010 Nylon 66  (Unverified Data**)

Category Polymer , Thermoplastic , Nylon , Nylon 66
Manufacturer
Trade Name
Port Shanghai port,China
Trade Terms EXW, FOB, CFR, CIF
Payment Terms L/C, T/T, PayPal
Download PDF DuPont Performance Polymers Zytel® 101 NC010 Nylon 66  (Unverified Data**).pdf
Price EMAIL US    sales@lookpolymers.com
Material Notes:
Zytel® 101 NC010 is a general purpose polyamide 66 resin for injection molding and extrusion.Information provided by DuPont Performance Polymers
Physical Properties Metric English Comments
Specific Gravity 1.14 g/cc
1.14 g/cc
DAM; ASTM D792
Density 1.14 g/cc
0.0412 lb/in³
DAM; ISO 1183
Water Absorption 1.2 %
<br>@Temperature 23.0 °C
 1.2 %
<br>@Temperature 73.4 °F
 Immersion 24h; DAM; ASTM D570
2.6 %
<br>@Temperature 23.0 °C
 2.6 %
<br>@Temperature 73.4 °F
 Equilibrium 50%RH; DAM; ISO 62, Similar to
8.5 %
<br>@Temperature 23.0 °C
 8.5 %
<br>@Temperature 73.4 °F
 Saturation; DAM; ASTM D570
8.5 %
<br>@Temperature 23.0 °C
 8.5 %
<br>@Temperature 73.4 °F
 Saturation, immersed; DAM; ISO 62, Similar to
Linear Mold Shrinkage 0.015 cm/cm
<br>@Thickness 3.20 mm
 0.015 in/in
<br>@Thickness 0.126 in
 Flow; DAM
Linear Mold Shrinkage, Flow 0.014 cm/cm
<br>@Thickness 2.00 mm
 0.014 in/in
<br>@Thickness 0.0787 in
 DAM; ISO 294-4
Linear Mold Shrinkage, Transverse 0.014 cm/cm
<br>@Thickness 2.00 mm
 0.014 in/in
<br>@Thickness 0.0787 in
 DAM; ISO 294-4
Melt Index of Compound 24 g/10 min
<br>@Load 1.20 kg,<br> Temperature 275 °C
 24 g/10 min
<br>@Load 2.65 lb,<br> Temperature 527 °F
 DAM; cm3/10 min; ISO 1133
Mechanical Properties Metric English Comments
Hardness, Rockwell M 59
59
50%RH; ASTM D785
79
79
DAM; ASTM D785
Hardness, Rockwell R 108
108
50%RH; ASTM D785
121
121
DAM; ASTM D785
Tensile Strength 38.0 MPa
<br>@Temperature 121 °C
 5510 psi
<br>@Temperature 250 °F
 50%RH; ASTM D638
41.0 MPa
<br>@Temperature 77.0 °C
 5950 psi
<br>@Temperature 171 °F
 50%RH; ASTM D638
43.0 MPa
<br>@Temperature 121 °C
 6240 psi
<br>@Temperature 250 °F
 DAM; ASTM D638
62.0 MPa
<br>@Temperature 77.0 °C
 8990 psi
<br>@Temperature 171 °F
 DAM; ASTM D638
77.0 MPa
<br>@Temperature 23.0 °C
 11200 psi
<br>@Temperature 73.4 °F
 50%RH; ASTM D638
83.0 MPa
<br>@Temperature 23.0 °C
 12000 psi
<br>@Temperature 73.4 °F
 DAM; ASTM D638
110 MPa
<br>@Temperature -40.0 °C
 16000 psi
<br>@Temperature -40.0 °F
 50%RH; ASTM D638
114 MPa
<br>@Temperature -40.0 °C
 16500 psi
<br>@Temperature -40.0 °F
 DAM; ASTM D638
Tensile Strength, Yield 28.0 MPa
<br>@Temperature 121 °C
 4060 psi
<br>@Temperature 250 °F
 50%RH; ASTM D638
33.0 MPa
<br>@Temperature 121 °C
 4790 psi
<br>@Temperature 250 °F
 DAM; ASTM D638
40.0 MPa
<br>@Temperature 77.0 °C
 5800 psi
<br>@Temperature 171 °F
 50%RH; ASTM D638
45.0 MPa
<br>@Temperature 77.0 °C
 6530 psi
<br>@Temperature 171 °F
 DAM; ASTM D638
55.0 MPa
<br>@Temperature 23.0 °C
 7980 psi
<br>@Temperature 73.4 °F
 50%RH; ISO 527
58.0 MPa
<br>@Temperature 23.0 °C
 8410 psi
<br>@Temperature 73.4 °F
 50%RH; ASTM D638
82.0 MPa
<br>@Temperature 23.0 °C
 11900 psi
<br>@Temperature 73.4 °F
 DAM; ISO 527
83.0 MPa
<br>@Temperature 23.0 °C
 12000 psi
<br>@Temperature 73.4 °F
 DAM; ASTM D638
110 MPa
<br>@Temperature -40.0 °C
 16000 psi
<br>@Temperature -40.0 °F
 50%RH; ASTM D638
114 MPa
<br>@Temperature -40.0 °C
 16500 psi
<br>@Temperature -40.0 °F
 DAM; ASTM D638
Elongation at Break 15 %
<br>@Temperature -40.0 °C
 15 %
<br>@Temperature -40.0 °F
 DAM; ASTM D638
20 %
<br>@Temperature -40.0 °C
 20 %
<br>@Temperature -40.0 °F
 50%RH; ASTM D638
25 %
<br>@Temperature 23.0 °C
 25 %
<br>@Temperature 73.4 °F
 DAM; nominal; ISO 527
45 %
<br>@Temperature 23.0 °C
 45 %
<br>@Temperature 73.4 °F
 50mm/min; DAM; ISO 527
>= 50 %
<br>@Temperature 23.0 °C
 >= 50 %
<br>@Temperature 73.4 °F
 50%RH; nominal; ISO 527
60 %
<br>@Temperature 23.0 °C
 60 %
<br>@Temperature 73.4 °F
 DAM; ASTM D638
>= 300 %
<br>@Temperature 23.0 °C
 >= 300 %
<br>@Temperature 73.4 °F
 50%RH; ASTM D638
>= 300 %
<br>@Temperature 77.0 °C
 >= 300 %
<br>@Temperature 171 °F
 50%RH; ASTM D638
>= 300 %
<br>@Temperature 77.0 °C
 >= 300 %
<br>@Temperature 171 °F
 DAM; ASTM D638
>= 300 %
<br>@Temperature 121 °C
 >= 300 %
<br>@Temperature 250 °F
 50%RH; ASTM D638
>= 300 %
<br>@Temperature 121 °C
 >= 300 %
<br>@Temperature 250 °F
 DAM; ASTM D638
Elongation at Yield 4.0 %
<br>@Temperature -40.0 °C
 4.0 %
<br>@Temperature -40.0 °F
 DAM; ASTM D638
4.5 %
<br>@Temperature 23.0 °C
 4.5 %
<br>@Temperature 73.4 °F
 DAM; ISO 527
5.0 %
<br>@Temperature 23.0 °C
 5.0 %
<br>@Temperature 73.4 °F
 DAM; ASTM D638
25 %
<br>@Temperature 23.0 °C
 25 %
<br>@Temperature 73.4 °F
 50%RH; ASTM D638
25 %
<br>@Temperature 23.0 °C
 25 %
<br>@Temperature 73.4 °F
 50%RH; ISO 527
30 %
<br>@Temperature 77.0 °C
 30 %
<br>@Temperature 171 °F
 50%RH; ASTM D638
30 %
<br>@Temperature 77.0 °C
 30 %
<br>@Temperature 171 °F
 DAM; ASTM D638
40 %
<br>@Temperature 121 °C
 40 %
<br>@Temperature 250 °F
 50%RH; ASTM D638
45 %
<br>@Temperature 121 °C
 45 %
<br>@Temperature 250 °F
 DAM; ASTM D638
Tensile Modulus 1.40 GPa
<br>@Temperature 23.0 °C
 203 ksi
<br>@Temperature 73.4 °F
 50%RH; ISO 527
3.10 GPa
<br>@Temperature 23.0 °C
 450 ksi
<br>@Temperature 73.4 °F
 DAM; ISO 527
Flexural Modulus 0.414 GPa
<br>@Temperature 121 °C
 60.0 ksi
<br>@Temperature 250 °F
 50%RH; ASTM D790
0.538 GPa
<br>@Temperature 121 °C
 78.0 ksi
<br>@Temperature 250 °F
 DAM; ASTM D790
0.565 GPa
<br>@Temperature 77.0 °C
 81.9 ksi
<br>@Temperature 171 °F
 50%RH; ASTM D790
0.689 GPa
<br>@Temperature 77.0 °C
 99.9 ksi
<br>@Temperature 171 °F
 DAM; ASTM D790
1.20 GPa
<br>@Temperature 23.0 °C
 174 ksi
<br>@Temperature 73.4 °F
 50%RH; ISO 178
1.21 GPa
<br>@Temperature 23.0 °C
 175 ksi
<br>@Temperature 73.4 °F
 50%RH; ASTM D790
2.80 GPa
<br>@Temperature 23.0 °C
 406 ksi
<br>@Temperature 73.4 °F
 DAM; ISO 178
2.83 GPa
<br>@Temperature 23.0 °C
 410 ksi
<br>@Temperature 73.4 °F
 DAM; ASTM D790
3.241 GPa
<br>@Temperature -40.0 °C
 470.1 ksi
<br>@Temperature -40.0 °F
 DAM; ASTM D790
3.447 GPa
<br>@Temperature -40.0 °C
 499.9 ksi
<br>@Temperature -40.0 °F
 50%RH; ASTM D790
Shear Strength 66.2 MPa
<br>@Temperature 23.0 °C
 9600 psi
<br>@Temperature 73.4 °F
 DAM; ASTM D732
Izod Impact, Notched 0.270 J/cm
<br>@Temperature -40.0 °C
 0.506 ft-lb/in
<br>@Temperature -40.0 °F
 50%RH; ASTM D256
0.320 J/cm
<br>@Temperature -40.0 °C
 0.599 ft-lb/in
<br>@Temperature -40.0 °F
 DAM; ASTM D256
0.530 J/cm
<br>@Temperature 23.0 °C
 0.993 ft-lb/in
<br>@Temperature 73.4 °F
 DAM; ASTM D256
1.12 J/cm
<br>@Temperature 23.0 °C
 2.10 ft-lb/in
<br>@Temperature 73.4 °F
 50%RH; ASTM D256
Izod Impact, Notched (ISO) 5.50 kJ/m²
<br>@Temperature -40.0 °C
 2.62 ft-lb/in²
<br>@Temperature -40.0 °F
 DAM; ISO 180/1A
5.50 kJ/m²
<br>@Temperature -30.0 °C
 2.62 ft-lb/in²
<br>@Temperature -22.0 °F
 DAM; ISO 180/1A
5.50 kJ/m²
<br>@Temperature 23.0 °C
 2.62 ft-lb/in²
<br>@Temperature 73.4 °F
 DAM; ISO 180/1A
12.0 kJ/m²
<br>@Temperature 23.0 °C
 5.71 ft-lb/in²
<br>@Temperature 73.4 °F
 50%RH; ISO 180/1A
Izod Impact, Unnotched (ISO) 300 kJ/m²
<br>@Temperature -30.0 °C
 143 ft-lb/in²
<br>@Temperature -22.0 °F
 DAM; ISO 180/1U
NB
<br>@Temperature 23.0 °C
 NB
<br>@Temperature 73.4 °F
 DAM; ISO 180/1U
NB
<br>@Temperature 23.0 °C
 NB
<br>@Temperature 73.4 °F
 50%RH; ISO 180/1U