Kazanorgsintez PE2NT21-13 High Density Polyethylene Composite

Category	Polymer , Thermoplastic , Polyethylene (PE) , HDPE , High Density Polyethylene (HDPE), Injection Molded
Manufacturer	Kazanorgsintez
Trade Name
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Kazanorgsintez PE2NT21-13 High Density Polyethylene Composite.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Production Method: Copolymerization of eythylene at low pressure in presence of complex catalysts using gaseous-phase method. Application: Composition is intended for injection molding processing into goods for household and domestic use or for other field of application and characterized by advanced crack resistance.Information Provided by Kazanorgsintez

Physical Properties	Metric	English	Comments
Density	0.948 - 0.955 g/cc @Temperature 23.0 Â°C	0.0342 - 0.0345 lb/inÂ³ @Temperature 73.4 Â°F
	0.950 - 0.957 g/cc @Temperature 20.0 Â°C	0.0343 - 0.0346 lb/inÂ³ @Temperature 68.0 Â°F
Environmental Stress Crack Resistance	>= 30 hour	>= 30 hour
Melt Flow	4.0 - 7.0 g/10 min @Load 2.16 kg, Temperature 190 Â°C	4.0 - 7.0 g/10 min @Load 4.76 lb, Temperature 374 Â°F	Â±15%
	80 - 245 g/10 min @Load 21.6 kg, Temperature 190 Â°C	80 - 245 g/10 min @Load 47.6 lb, Temperature 374 Â°F

Mechanical Properties	Metric	English	Comments
Tensile Strength, Yield	>= 25.0 MPa	>= 3630 psi
Elongation at Break	>= 600 %	>= 600 %

Descriptive Properties	Value	Comments
Amount of impurities [pcs]	10