Styron MAGNUMâ„¢ 3325 MT Acrylonitrile Butadiene Styrene (ABS) Resin

Category Polymer , Thermoplastic , ABS Polymer
Manufacturer Styron
Trade Name Magnum™
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Styron MAGNUMâ„¢ 3325 MT Acrylonitrile Butadiene Styrene (ABS) Resin.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Overview: MAGNUMâ„¢ 3325 MT is a resin with excellent processing characteristics and matt surface finish. The mass (continuous process) ABS technology of Styron ensures an ABS resin that combines excellent processability with a stable light base color that is ideal for self-color.Applications: Matt/unpainted interior automotive trimDoor linersDashboard componentsPillar coversConsolesGlove boxesInformation provided by Styron
Physical Properties Metric English Comments
Density 1.04 g/cc
0.0376 lb/in³
ASTM D792
1.05 g/cc
0.0379 lb/in³
ISO 1183/B
Apparent Bulk Density 0.600 g/cc
0.0217 lb/in³
ISO 60
Linear Mold Shrinkage, Flow 0.0040 - 0.0070 cm/cm
0.0040 - 0.0070 in/in
ASTM D955; ISO 294-4
Melt Flow 2.5 g/10 min

@Load 3.80 kg,
Temperature 230 °C
 2.5 g/10 min

@Load 8.38 lb,
Temperature 446 °F
 ASTM D1238
10 g/10 min

@Load 10.0 kg,
Temperature 220 °C
 10 g/10 min

@Load 22.0 lb,
Temperature 428 °F
 ISO 1133
Mechanical Properties Metric English Comments
Tensile Strength at Break 25.0 MPa

@Thickness 3.20 mm
 3630 psi

@Thickness 0.126 in
 Injection Molded; ASTM D638
Tensile Strength, Yield 42.3 MPa
6140 psi
Type I, 51 mm/min; ASTM D638
Elongation at Break 25 %
25 %
Type I, 51 mm/min; ASTM D638
Elongation at Yield 3.3 %

@Thickness 3.20 mm
 3.3 %

@Thickness 0.126 in
 Injection Molded; ISO 527-2/50
Tensile Modulus 2.07 GPa
300 ksi
Type I, 51 mm/min; ASTM D638
2.20 GPa

@Thickness 3.20 mm
 319 ksi

@Thickness 0.126 in
 Injection Molded; ISO 527-2
Flexural Strength 64.5 MPa
9350 psi
Type I, 5.1 mm/min; ASTM D790
65.0 MPa

@Thickness 3.20 mm
 9430 psi

@Thickness 0.126 in
 3-points, 2 mm/min, Injection Molded; ISO 178
Flexural Modulus 2.21 GPa
321 ksi
Type I, 5.1 mm/min; ASTM D790
2.10 GPa

@Thickness 3.20 mm
 305 ksi

@Thickness 0.126 in
 3-points, 2 mm/min, Injection Molded; ISO 178
Izod Impact, Notched 3.10 J/cm

@Thickness 3.20 mm,
Temperature 23.0 °C
 5.81 ft-lb/in

@Thickness 0.126 in,
Temperature 73.4 °F
 0.25 mm Notch Depth; ASTM D256
Izod Impact, Notched (ISO) 10.0 kJ/m²

@Temperature -30.0 °C
 4.76 ft-lb/in²

@Temperature -22.0 °F
 ISO 180/1A
17.0 kJ/m²

@Temperature 23.0 °C
 8.09 ft-lb/in²

@Temperature 73.4 °F
 ISO 180/1A
Charpy Impact, Notched 0.800 J/cm²

@Temperature -30.0 °C
 3.81 ft-lb/in²

@Temperature -22.0 °F
 Compression Molded; ISO 179/2
1.10 J/cm²

@Temperature -30.0 °C
 5.23 ft-lb/in²

@Temperature -22.0 °F
 Injection Molded; ISO 179/1eA
1.20 J/cm²

@Temperature 23.0 °C
 5.71 ft-lb/in²

@Temperature 73.4 °F
 Compression Molded; ISO 179/2
1.70 J/cm²

@Temperature 23.0 °C
 8.09 ft-lb/in²

@Temperature 73.4 °F
 Injection Molded; ISO 179/1eA
Dart Drop, Total Energy 31.1 J

@Thickness 3.20 mm,
Temperature 23.0 °C
 22.9 ft-lb

@Thickness 0.126 in,
Temperature 73.4 °F
 3.39 m/sec, Peak Energy; ASTM D3763
31.7 J

@Thickness 3.20 mm,
Temperature -29.0 °C
 23.4 ft-lb

@Thickness 0.126 in,
Temperature -20.2 °F
 3.39 m/sec, Peak Energy; ASTM D3763
34.3 J

@Thickness 3.20 mm,
Temperature -29.0 °C
 25.3 ft-lb

@Thickness 0.126 in,
Temperature -20.2 °F
 3.39 m/sec, Total Energy; ASTM D3763
45.4 J

@Thickness 3.20 mm,
Temperature 23.0 °C
 33.5 ft-lb

@Thickness 0.126 in,
Temperature 73.4 °F
 3.39 m/sec, Total Energy; ASTM D3763
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 94.0 µm/m-°C
52.2 µin/in-°F
ASTM D696
Deflection Temperature at 0.46 MPa (66 psi) 96.1 °C

@Thickness 3.20 mm
 205 °F

@Thickness 0.126 in
 Unannealed; ASTM D648
Deflection Temperature at 1.8 MPa (264 psi) 101 °C
214 °F
Annealed; ISO 75-2/A
82.8 °C

@Thickness 3.20 mm
 181 °F

@Thickness 0.126 in
 Unannealed; ASTM D648
Vicat Softening Point 102 °C
216 °F
ISO 306/B50
108 °C
226 °F
ASTM D1525
Flammability, UL94 HB

@Thickness 1.50 mm
 HB

@Thickness 0.0591 in
HB

@Thickness 3.00 mm
 HB

@Thickness 0.118 in
Flame Spread 60.0 mm/min
2.36 in/min
ISO 3795
Descriptive Properties Value Comments
Carbon Emission 20000 µg/g
VDA 277