- Polymer Property : Deflection Temperature at 1.8 MPa (264 psi) = 181 °F
Polymer Property : Deflection Temperature at 1.8 MPa (264 psi) = 181 °F Product List
Thermal PropertiesTips: 30 items are displayed at most. For the rest of the results, please contact customer service.
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 82.8 °C @Thickness 6.35 mm |
181 °F @Thickness 0.250 in |
Unannealed; ASTM D648 |
| PolyOne LubriOne™ 5209 FPL 20 Natural Acetal (POM) Copolymer LubriOne™ Lubricated and Wear-Resistant Compounds have been specifically formulated to be self-lubricating materials, offering low coefficient of friction and improved wear resistance properties. L.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 82.8 °C @Thickness 6.35 mm |
181 °F @Thickness 0.250 in |
Unannealed; ASTM D648 |
| PolyOne LubriOne™ AT-000/20T Black Acetal (POM) Copolymer LubriOne™ Lubricated and Wear-Resistant Compounds have been specifically formulated to be self-lubricating materials, offering low coefficient of friction and improved wear resistance properties. L.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 83.0 °C | 181 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| SABIC Innovative Plastics Cycoloy® C7410 PC+ABS (Asia Pacific) Cycoloy* C7410 resin is a talc-filled PC+ABS, nonhalogenated FR for thinwall molding applications. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 83.0 °C @Thickness 3.20 mm |
181 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| SABIC Innovative Plastics Cycoloy® CM6140 PC+ABS (Asia Pacific) Cycoloy resin grade CM6140 is a flame retardant, filled PC/ABS blend. It is of non-brominated & non-chlorinated FR system to meet UL94 V0 at 0.8mm. Key features include thin wall FR, higher stiffnes.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 83.0 °C @Thickness 6.35 mm |
181 °F @Thickness 0.250 in |
Unannealed; ASTM D648 |
| PolyOne Edgetek® XT EX3600-0002 UV Black Polycarbonate + PBT (PC+PBT) EDGETEK™ XT High Performance Polymers are polycarbonate and polyester alloys that combine strength, durability and chemical resistance. The Edgetek XT product family includes a complete line of gen.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 83.0 °C @Thickness 3.20 mm |
181 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| SABIC Innovative Plastics LNP LUBRICOMP CZL36 PS LNP LUBRICOMP* CZL36 is a compound based on Polystyrene resin containing 30% Milled Glass and 15% PTFE. Added features of this material include: Internally Lubricated. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 83.0 °C | 181 °F | ASTM D648 |
| Resirene Resirene® 4220 High Impact Polystyrene Features:High FlowEasy ProcessingFDA Rating: 21 CFR 177.1640FlexibilityExternal LubricatedApplications:InjectionTV CabinetsTyping Machine CasesPrintersToysInformation provided by US distributor Cals.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 82.8 °C | 181 °F | Unannealed; ASTM D648 |
| M. Holland Company GS410WC Polystyrene
(discontinued **) Features: High Clarity, High FlowUses: Household Goods, LabwareApprovals: FDA 21 CFR 177.1640 Processing Method: Injection MoldingInformation provided by M. Holland. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 83.0 °C | 181 °F | |
| Polimeri Europa SINKRAL PD H330/S ABS, Heat Stabilized
(discontinued **) Symbol according to ISO 1043-1: ABS Grade designation according to ISO 2580-ABS 1,MG,095-15-16-25 Injection moulding grade with high flow and gloss, specially developed to meet the requirements of.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 83.0 °C | 181 °F | |
| Arkema Group Oroglas® HFI-7 Acrylic
(discontinued **) OROGLAS HFI-7 is a medium impact grade that in addition to the improvement in impact resistance provides superior flow which contribute to reduce the cycle time and improve demolding.Key features :.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 83.0 °C @Thickness 6.40 mm |
181 °F @Thickness 0.252 in |
Unannealed; ASTM D648 |
| LG Chemical ALPHALAC SG970 HIPS Description: Injection Molding, General Purpose, Good Processability, High glossApplication: Air Conditioner Panel, Washer CoverCAS No. 9003-55-8Information provided by LG Chemical |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 83.0 °C @Thickness 6.40 mm |
181 °F @Thickness 0.252 in |
Unannealed; ASTM D648 |
| LG Chemical ALPHALAC SG970NSU HIPS Description: Injection Molding, General Purpose, Good Processability, High gloss, antistatic and UV stabilizedApplication: Air Conditioner Panel, Washer CoverCAS No. 9003-55-8Information provided by.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 83.0 °C | 181 °F | annealed; ASTM D648 |
| KKPC Kuhmo HF 430U Weather-resistant Flame Retarded HIPS Key features: Excellent weather-resistance, non-deca heat-resistance. Common Uses: TV and VCR housing, parts needing non-deca type.HIPS is a functional resin made by copolymerization of styrene mono.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 83.0 °C | 181 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| SABIC Innovative Plastics LNP LUBRICOMP KL003E POM (Europe-Africa-Middle East) LNP* LUBRICOMP* KL003E is a compound based on Acetal Copolymer resin containing PTFE. Added features include: Internally Lubricated, Easy Molding. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 83.0 °C @Thickness 3.20 mm |
181 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| SABIC Innovative Plastics Xenoy® CL101 PBT+PC (Asia Pacific) Xenoy CL101 is an unfilled, impact modified PC/PBT blend with excellent solvent resistance and low-temperature ductility. It has a proven track record in off-line painted exterior automotive applica.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 83.0 °C | 181 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| SABIC Innovative Plastics LNP THERMOCOMP C7410 PC+ABS (Asia Pacific) LNP* Thermocomp* C7410 compound is a talc-filled PC+ABS, nonhalogenated FR for thinwall molding applications. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 83.0 °C | 181 °F | ISO 75 |
| Teijin Multilon TN-7100F Filler Reinforced Type, Halogen-Free Flame Resistant PC/ABS Polymer Alloy Halogen-free flame retardant PC/ABS polymer alloy, and is also antimony-free. High stiffness and flowability realize the thin wall of large-scale business machine chassis.Information provided by Tei.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 83.0 °C @Thickness 6.40 mm |
181 °F @Thickness 0.252 in |
ASTM D648 |
| Samsung Cheil Industries Starex® EA-0640 ABS, Unreinforced Permanent static prevention ABS material such as LCD carrierInformation provided by Samsung Cheil Industries. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 83.0 °C @Thickness 6.40 mm |
181 °F @Thickness 0.252 in |
ASTM D648 |
| Samsung Cheil Industries Starex® SF-0505HWR MABS, Unreinforced Scratch Resistant Information provided by Samsung Cheil Industries. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 83.0 °C | 181 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| SABIC Innovative Plastics LNP Thermocomp WB006 PBT (Europe-Africa-Middle East) LNP* THERMOCOMP* WB006 is a compound based on Polybutylene Terephalate resin containing Glass Bead.This data was supplied by SABIC-IP for the Europe-Africa-Middle East region. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 83.0 °C | 181 °F | ASTM D648 |
| Supreme Petrochem SH 2114 High Impact Polystyrene Characteristics Very high impact strength Easy processing High heat Processing Extrusion MoldingApplications Toys, shoe heels, cosmetic boxes, pill vials Luggage cases Blending with clear polys.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 83.0 °C | 181 °F | ASTM D648 |
| Eastman Tenite 285E3720005 Butyrate Clear, Trsp Tenite cellulosic plastics are noted for their excellent balance of properties - toughness, hardness, strength, surface gloss, clarity, and a warm feel. The mechanical properties of Tenite cellulosi.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 83.0 °C | 181 °F | annealed; ISO 75 |
| Chi Mei Kibiton® PB-5910 SBC High transparency, medium stiffness, toughness |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 82.8 °C | 181 °F | 0.125 in bar Annealed 4 hours at 80°C; ASTM D648 |
| Diamond Polymers ABS VP-12 Description: Flame Retardant with UVInformation provided by Diamond Polymers, Inc. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 82.8 °C | 181 °F | 0.125 in bar Unannealed/Conditioned 48 hours at 23°C; ASTM D648 |
| Diamond Polymers ASA S510 Description: ASA Weatherable Polymer, Injection Molding Grade, Medium ImpactInformation provided by Diamond Polymers, Inc. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 82.8 °C | 181 °F | |
| Aclo Accutech Polypropylene Homopolymer HP0339M40CL Mica Reinforced Coupled |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 83.0 °C | 181 °F | ASTM D648 |
| Ashley Polymers Ashlene® 520 Nylon 66 A general purpose basic Nylon 66 resin, slightly lubricated.Data provided by the manufacturer |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 83.0 °C | 181 °F | ASTM D648 |
| Beijing Chemical Industry KAIFA® GL3100 ABS Flame-Retardant Grade Good flammabilityInformation provided by Beijing Chemical Industry Research Institute (Group) |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 83.0 °C | 181 °F | ASTM D648 |
| Albis Plastics Cellulose Acetate Butyrate B9004 (Odor Mask Added), 5% Plasticizer
(discontinued **) Amorphous Cellulose Acetate Butyrate (CAB)Characteristics: Dimensional Stability, Weatherability and Low Temp Impact StrengthApplications: Pens, Ski Goggles, Auto Trim, Skylights, Tool Handles and T.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 82.8 °C | 181 °F | Unannealed (0.250"); ASTM D648 |
| LTL Color Compounds ColorFast® GPA300 ABS Super-tough ABS with our highest impact strength, injection moldingAll information provided by LTL Color Compounders, Inc. |
|||