Polymer Property : Flexural Strength = 65.0 MPa Product List

Mechanical Properties

Tips: 30 items are displayed at most.

Mechanical Properties	Metric	English	Comments
Flexural Strength	65.0 MPa	9430 psi	2 mm/min; ASTM D 790
Polimeri Europa Sinkral® C 442 ABS Resin Sinkral C 442 is a heat resistant injection molding grade offering good flow and impact resistance together with excellent thermal stability during processing. Designation: Thermoplastic ISO 2580-AB..
Flexural Strength	<= 65.0 MPa	<= 9430 psi	ISO 178
Polykemi AB POLYfill PP HIP15025 HC Polypropylene Information provided by Polykemi AB
Flexural Strength	65.0 MPa	9430 psi	ISO 178
Radici Radilon® CS38 Copolyamide 6 semiaromatic Film extrusion gradeInformation provided by Radici group.
Flexural Strength	65.0 MPa	9430 psi	ISO 178
SABIC Innovative Plastics LNP COLORCOMP AX03654 ABS LNP COLORCOMP* AX03654 is a compound based on Acrylonitrile Butadiene Styrene resin containing Flame Retardant, Unfilled Custom Color. Added features of this material include: Flame Retardant.
Flexural Strength	65.0 MPa	9430 psi	ISO 178
Solvay Specialty Polymers Amodel® AT-5001 Polyphthalamide (PPA) Resin, Dry as Molded  (discontinued **) AMODEL AT-5001 polyphthalamide resin is a neat ductile material that offers superior retention of properties after humid thermal aging, high impact at low temperature, and better mechanical properti..
Flexural Strength	65.0 MPa	9430 psi	ASTM D790
Kostat 7440 Conductive ABS Compound KOSTAT 7440 is a conductive thermoplastic compound based on Acrylonitrile Butadiene Styrene and a special carbon black. KOSTAT 7440 is not dependant on atmospheric conditions and is used for ESD in..
Flexural Strength	65.0 MPa	9430 psi
Lehmann & Voss LUVOCOMÂ® 1200-7899 ABS, with steel fiber Applications: Office communication.Electrically conductive, suitable for continuous discharging of statically generated electricity.Isotropic shrinkage characteristics.Information provided by Lehman..
Flexural Strength	65.0 MPa	9430 psi
Lehmann & Voss LUVOCOMÂ® 80-8003 Polyacetal-copolymer, with carbon fiber Applications: Automotive industry, textile- and office machinery, apparatus- and precision engineering.Strong, stiff parts.Electrically conductive, suitable for continuous discharging of statically ..
Flexural Strength	65.0 MPa	9430 psi
Lehmann & Voss LUVOCOMÂ® AC-80/TF/22/BK Polyacetal-copolymer, with PTFE Applications: Automotive industry, textile- and office machinery, apparatus- and precision engineering.Improved friction and wear behaviour. Emergency running property.Emergency running property, gl..
Flexural Strength	65.0 MPa	9430 psi	ISO 178
SABIC Innovative Plastics LNP LUBRICOMP DZL24 PC LNP LUBRICOMP* DZL24 is a compound based on Polycarbonate resin containing 20% Milled Glass, 10% PTFE. Added features of this material include: Internally Lubricated.
Flexural Strength	65.0 MPa	9430 psi	ISO 178
SABIC Innovative Plastics LNP LUBRILOY K2000 Acetal (Asia Pacific) LNP LUBRILOY* K2000 is a compound based on Acetal resin containing Proprietary Lubricant. Added features of this material include: Internally Lubricated.
Flexural Strength	65.0 MPa	9430 psi	ISO 178
SABIC Innovative Plastics LNP LUBRILOY R2000 PA 66 (Asia Pacific) LNP* Lubriloy* R2000 is a compound based on Nylon 66 resin containing Proprietary Lubricant. Added features of this material include: Internally Lubricated.
Flexural Strength	65.0 MPa	9430 psi	ISO 178
SABIC Innovative Plastics LNP THERMOCOMP MX06402H PP LNP* THERMOCOMP* MX06402H is a compound based on Polypropylene resin containing 20% Glass Fiber. Added features of this material include: Heat Stabilized, Low Extractable.
Flexural Strength	65.0 MPa	9430 psi	ASTM Test
Styrolution TerluranÂ® GP-35 ABS Terluran GP-35 is a very high flow grade of ABS for injection molding with good resistance to impact and heat deflection.Information provided by STYROLUTION, which is a joint venture between BASF an..
Flexural Strength	65.0 MPa	9430 psi	ISO 178
Styrolution TerblendÂ® N NM-21 XP ABS+PA (Dry) Information provided by STYROLUTION, which is a joint venture between BASF and INEOS
Flexural Strength	65.0 MPa	9430 psi	at rupture; ASTM D790
Sumitomo Bakelite North America SI 9550 Silicone Compound SI 9550 is a short fiberglass reinforced silicone molding compound, which offers moderate strength properties, and dimensional stability and excellent long-term thermal stability at elevated tempera..
Flexural Strength	65.0 MPa	9430 psi	ASTM D 790
SABIC Innovative Plastics Noryl EBN9003 PPE+HIPS (Asia Pacific) This data was supplied by SABIC-IP for the Asia Pacific region.
Flexural Strength	65.0 MPa	9430 psi	ASTM D790
Plenco 6990 Phenolic, Briquette, Compression Molded PLENCO 06990 is a glass and mineral filled novolac phenolic molding compound. UL recognized under component file E40654.Information supplied by Plenco.
Flexural Strength	65.0 MPa	9430 psi	ISO 178
Polyram RamLloy PJ702 ASA & ABS Alloy A general purpose injection molding ASA & ABS alloy. It has good mechanical properties similar to ABS with much better weather resistance.Information provided by Polyram.
Flexural Strength	65.0 MPa	9430 psi	ISO 178
Polyram RamShine PV101 Acrylonitrile Butadiene Styrene General purpose ABS for injection molding applications.Information provided by Polyram.
Flexural Strength	65.0 MPa	9430 psi	ASTM D790
Eastman Provista MP002 Copolymer Provista Copolymer MP002 is a resin specifically developed for extrusion into profiles for medical applications where aesthetics such as high clarity and gloss, coupled with design flexibility and e..
Flexural Strength	65.0 MPa	9430 psi	dry; ISO 178
DSM Akulon® Fuel Lock FL-LP PA6 Low fuel permeation PA6 suitable for use in injection molding/welding of small engine fuel tanks, UV stabilized
Flexural Strength	65.0 MPa	9430 psi	ISO 178
Denka MALECCA K-700 ABS A heat-resistant ABS resin based on "DENKA IP" – a Styrene-N-Phenylmaleimide copolymer. It has been designed as an easy-to-use resin by improving conventional heat-resistant ABS resins which had de..
Flexural Strength	65.0 MPa	9430 psi	2mm/min; ASTM D790
Denka TH-23 Transparent Resin Polymer (MBS resin) Polymethacrylate Butadiene Styrene "TX Polymer" (methyl methacrylate styrene), MS resins as an alternative to acrylic resins, with low density, low moisture absorption, and good moldability, "TH Polymer/TP Polymer," MBS resins with a..
Flexural Strength	65.0 MPa	9430 psi	JIS-K-6740
Denka VINYKON R3105 PVC, R grade for hard extrusion A PVC resin compound offering excellent physical properties and workability. A broad product lineup is available, including hard and soft grades, as well as those for extrusion and injection molding..
Flexural Strength	65.0 MPa	9430 psi	2 mm/min; ISO 178
Chi Mei Polylac® PA-756H ABS - High Flow Super high flow
Flexural Strength	65.0 MPa	9430 psi	ISO 178
Azoty Tarnow™ TARNOFORM 300 M POM Tribological modified grade with addition of molybdenum disulphide, which causes decreased coefficient of friction and wear, especially for applications requiring high load at low sliding speed.Info..
Flexural Strength	65.0 MPa	9430 psi	ISO Data
BASF Ultramid® 8231G HS BK-102 14% Glass Filled PA6 (Conditioned) Ultramid 8231G HS BK-102 is a black pigmented heat stabilized, 14% glass fiber reinforced PA6 injection molding compound.The glass fiber reinforcement enhances performance such as strength, stiffnes..
Flexural Strength	65.0 MPa	9430 psi	ASTM D790
Beijing Chemical Industry KAIFA® GL2200 ABS Good Flow Grade High impact, Easy processingInformation provided by Beijing Chemical Industry Research Institute (Group)
Flexural Strength	65.0 - 85.0 MPa	9430 - 12300 psi	At Rupture; ISO 178
Vyncolit 3520 CG Novolac Phenolic Graphite filled phenolic molding compound with excellent dimensional stability. Self-lubricating and has a low coefficient of friction. Not suitable for electrical applications.USES: Gas meter par..