- Polyram PlusTek PA4801G6 Nylon 6.6, 30% Glass Fiber Reinforced, PTFE lubricated
Polyram PlusTek PA4801G6 Nylon 6.6, 30% Glass Fiber Reinforced, PTFE lubricated
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, 30% Glass Fiber Filled |
| Manufacturer | Polyram |
| Trade Name | PlusTek |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Polyram PlusTek PA4801G6 Nylon 6.6, 30% Glass Fiber Reinforced, PTFE lubricated.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
30% glass fiber reinforced, PTFE lubricated polyamide 6.6 for injection molding applicationsInformation provided by Polyram Ram On Ind.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.47 g/cc | 0.0531 lb/in³ | DIN 53479 |
| Water Absorption | 0.80 % | 0.80 % | DIN 53495 |
| Linear Mold Shrinkage | 0.0030 - 0.0040 cm/cm | 0.0030 - 0.0040 in/in |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 175 MPa | 25400 psi | ASTM-D638 |
| Elongation at Break | 3.0 % | 3.0 % | ASTM-D638 |
| Tensile Modulus | 8.30 GPa | 1200 ksi | ASTM-D790 |
| Flexural Strength | 250 MPa | 36300 psi | ASTM D790 |
| Flexural Modulus | 6.80 GPa | 986 ksi | ASTM-D790 |
| Izod Impact, Notched | 1.70 J/cm @Temperature 23.0 °C |
3.18 ft-lb/in @Temperature 73.4 °F |
ASTM-D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 256 °C | 493 °F | |
| Deflection Temperature at 0.46 MPa (66 psi) | 243 °C | 469 °F | DIN 53461 |
| Deflection Temperature at 1.8 MPa (264 psi) | 227 °C | 441 °F | DIN 53461 |
| Flammability, UL94 | HB @Thickness 3.00 mm |
HB @Thickness 0.118 in |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+14 ohm-cm | 1.00e+14 ohm-cm | DIN 53482 |
Users viewing this material also viewed the following:
- RheTech Products UVP254-01 Polypropylene Copolymer, UV Stabilized, Black
- LG Chemical Ethylene
- Indium Corp. Indalloy 116 Tin-Lead Solder Alloy
- A. Schulman FORMION™ FI 301 Ionomer
- Polyram PlusTek PB150 Nylon 6, Injection Molding
- DSM Arnite® AV2 390 XT PET GF50
- ChevronTexaco Superla® 5 White Oil
- Bond Laminates TEPEX® dynalite 408-C200(2)-FG290(2)/45% Carbon – Filament Glass – TPU Consolidated Composite Laminate
- BASF Paliogen® Maroon L 3980 Color Additive
- A. Schulman POLYFLAM™ FPP 1006S Talc Filled Homopolymer Polypropylene
Copyright © lookpolymers.com All Rights Reserved