Techmer ES Electrafil® J-50/CF/10 Polycarbonate, 10% Carbon Fiber Reinforced
| Category | Polymer , Thermoplastic , Polycarbonate (PC) , Polycarbonate, Carbon Fiber Reinforced |
| Manufacturer | Techmer ES |
| Trade Name | Electrafil® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Techmer ES Electrafil® J-50/CF/10 Polycarbonate, 10% Carbon Fiber Reinforced.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Carbon Fiber Reinforced
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.24 g/cc | 0.0448 lb/in³ | ASTM D792 |
| Water Absorption | 0.15 % | 0.15 % | 24 hrs; ASTM D570 |
| Linear Mold Shrinkage | 0.0015 cm/cm @Thickness 3.17 mm |
0.0015 in/in @Thickness 0.125 in |
ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Ultimate | 103 MPa | 15000 psi | ASTM D638 |
| Elongation at Break | 3.0 % | 3.0 % | ASTM D638 |
| Modulus of Elasticity | 7.58 GPa | 1100 ksi | ASTM D638 |
| Flexural Yield Strength | 165 MPa | 24000 psi | ASTM D790 |
| Flexural Modulus | 7.58 GPa | 1100 ksi | ASTM D790 |
| Izod Impact, Notched | 0.587 J/cm @Thickness 3.17 mm |
1.10 ft-lb/in @Thickness 0.125 in |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 32.4 µm/m-°C @Temperature 20.0 °C |
18.0 µin/in-°F @Temperature 68.0 °F |
ASTM D696 |
| Deflection Temperature at 0.46 MPa (66 psi) | 146 °C | 295 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 142 °C | 288 °F | ASTM D648 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Electrical Resistivity | 1000 - 10000 ohm-cm | 1000 - 10000 ohm-cm | ASTM C611 |
| Surface Resistance | 1e+05 - 1.00e+6 ohm | 1e+05 - 1.00e+6 ohm | ASTM D4496 |
Users viewing this material also viewed the following:
- Multibase Multi-Pro® 4518 CU W 45% Mineral Filled Polypropylene
- PolyOne Edgetek® SF2-40CF/000 NATURAL Polyphenylene Sulfide (PPS)
- DSM Akulon® Ultraflow™ K-FHGM24 Nylon 6-30% Glass and Mineral Reinforced (European Grade) (Cond) (discontinue
- Lehmann & Voss LUVOCOM® 80/CF/12/TF/10/GY Polyacetal-copolymer, with carbon fiber and PTFE
- Multibase Dow Corning® MB50-004 Siloxane Additive
- LATI Latamid 6 H2 G/30-V2HF PA 6, 30% Glass Fiber Reinforced, Heat Stabilized, Flame Retardant
- Westlake EF403 Low Density Polyethylene
- Polyram RamTough PZ126 Polycarbonate, Low Viscosity
- DSM Akulon® K224-G6 (Cond.) 30% Glass Reinforced Nylon 6 (North America)
- Arlon 48B12R005 0.005" (0.127 mm) Cured Silicone Rubber with Fiberglass Substrate
Copyright © lookpolymers.com All Rights Reserved