Styrolution Luran® 368 R Crystal Clear Transparent 77851 SAN

Category	Polymer , Thermoplastic , SAN Polymer , Styrene Acrylonitrile (SAN), Transparent
Manufacturer	Styrolution
Trade Name	Luran®
Port	Ningbo port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Styrolution Luran® 368 R Crystal Clear Transparent 77851 SAN.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Description: General-purpose grade with well-balanced properties, suitable for injection molding and extrusion. Especially for applications where highest transparency and low natural color is required.Information provided by STYROLUTION, which is a joint venture between BASF and INEOS

Physical Properties	Metric	English	Comments
Density	1.08 g/cc	0.0390 lb/in³	ISO 1183
Moisture Absorption at Equilibrium	0.20 %	0.20 %	23°C/50% RH; ISO 62
Linear Mold Shrinkage, Flow	0.0030 - 0.0070 cm/cm	0.0030 - 0.0070 in/in
Melt Flow	10.8 g/10 min @Load 10.0 kg, Temperature 220 °C	10.8 g/10 min @Load 22.0 lb, Temperature 428 °F	ISO 1133
	12.96 g/10 min @Load 21.6 kg, Temperature 200 °C	12.96 g/10 min @Load 47.6 lb, Temperature 392 °F	ISO 1133

Mechanical Properties	Metric	English	Comments
Hardness, Rockwell M	83	83	ISO 2039-2
Ball Indentation Hardness	165 MPa @Load 36.5 kg, Time 30.0 sec	23900 psi @Load 80.5 lb, Time 0.00833 hour	ISO 2039-1
Tensile Strength at Break	75.0 MPa	10900 psi	ISO 527-1/-2
Elongation at Break	3.0 %	3.0 %	ISO 527-1/-2
Tensile Modulus	3.70 GPa	537 ksi	ISO 527-1/-2
Flexural Strength	125 MPa	18100 psi	ISO 178
Izod Impact, Notched (ISO)	2.00 kJ/m²	0.952 ft-lb/in²	ISO 180/A
Charpy Impact Unnotched	1.80 J/cm² @Temperature 23.0 °C	8.57 ft-lb/in² @Temperature 73.4 °F	ISO 179/1eU
Charpy Impact, Notched	0.200 J/cm² @Temperature 23.0 °C	0.952 ft-lb/in² @Temperature 73.4 °F	ISO 179/1eA

Thermal Properties	Metric	English	Comments
CTE, linear, Parallel to Flow	70.0 µm/m-°C @Temperature 23.0 - 80.0 °C	38.9 µin/in-°F @Temperature 73.4 - 176 °F	ISO 11359-1/-2
Thermal Conductivity	0.170 W/m-K	1.18 BTU-in/hr-ft²-°F	DIN 52612-1
Maximum Service Temperature, Air	85.0 °C	185 °F
Deflection Temperature at 0.46 MPa (66 psi)	100 °C	212 °F	ISO 75-1/-2
Deflection Temperature at 1.8 MPa (264 psi)	88.0 °C	190 °F	ISO 75-1/-2
Vicat Softening Point	106 °C	223 °F	VST B50; ISO 306
Flammability, UL94	HB @Thickness 0.800 mm	HB @Thickness 0.0315 in	IEC 60695-11-10
	HB @Thickness 1.60 mm	HB @Thickness 0.0630 in	IEC 60695-11-10

Optical Properties	Metric	English	Comments
Transmission, Visible	90 %	90 %	transparent; thickness not quantified

Electrical Properties	Metric	English	Comments
Volume Resistivity	1.00e+14 ohm-cm	1.00e+14 ohm-cm	IEC 60093
Surface Resistance	>= 1.00e+15 ohm	>= 1.00e+15 ohm	IEC 60093
Dielectric Constant	2.7 @Frequency 1.00e+6 Hz	2.7 @Frequency 1.00e+6 Hz	IEC 60250
	3.0 @Frequency 100 Hz	3.0 @Frequency 100 Hz	IEC 60250
Dielectric Strength	34.0 kV/mm	864 kV/in	K20/P50; IEC 60243-1
Dissipation Factor	0.0040 @Frequency 100 Hz	0.0040 @Frequency 100 Hz	IEC 60250
	0.0070 @Frequency 1.00e+6 Hz	0.0070 @Frequency 1.00e+6 Hz	IEC 60250

Processing Properties	Metric	English	Comments
Melt Temperature	220 - 260 °C	428 - 500 °F	Injection Molding
Mold Temperature	40.0 - 80.0 °C	104 - 176 °F	Injection Molding
Drying Temperature	80.0 °C	176 °F	Pre-drying
Dry Time	2 - 4 hour	2 - 4 hour	Pre-drying

Descriptive Properties	Value	Comments
Color	Transparent 77851
Commercial Status	Europe
Primary Processing Technique	Injection Molding and Extrusion