- Polymer Property : Deflection Temperature at 0.46 MPa (66 psi) = 100 °C
Polymer Property : Deflection Temperature at 0.46 MPa (66 psi) = 100 °C Product List
Thermal PropertiesTips: 30 items are displayed at most.
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 100 °C | 212 °F | ISO 75B |
|
Polyplastic Armlen® PP MF 40-3M Polypropylene Copolymer, 40% Calcium Carbonate
Injection moldingInformation provided by PolyPlastic Group.
|
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 100 °C | 212 °F | ASTM D648 |
|
SABIC PP 502P Polypropylene Homopolymer for Raffia Applications
Product Description: PP 502P is intended for producing low denier stretched tapes with the following features:Consistent processabilityGood processability at high line speedsLow water carry overGoo..
|
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 100 °C | 212 °F | ASTM D648 |
|
SABIC PP 506P Polypropylene Homopolymer for Raffia Applications
Product Description: PP 506P is intended for producing low denier stretched tapes with the following features:Consistent processabilityGood processability at high line speeds and low deniersLow tap..
|
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 100 °C | 212 °F | ASTM D648 |
|
SABIC PP 526P Polypropylene Homopolymer for Cast Film
Product Description: PP 526P is specially developed for cast film applications for producing clear films and does not contain slip or antiblock additives.Films produced using PP 526P will exhibit:C..
|
|||
| Deflection Temperature at 0.46 MPa (66 psi) |
100
°C @Thickness 3.20 mm |
212
°F @Thickness 0.126 in |
unannealed; ASTM D 648 |
|
SABIC Innovative Plastics Cycoloy® C3650 PC+ABS (Europe-Africa-Middle East)
Flame retardant PC/ABS blend using non-brominated and non-chlorinated flame retardant systems, offering high impact and excellent extrusion and thermoforming characteristics. Halogen free according ..
|
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 100 °C | 212 °F | For EP-F101 |
|
EVALCA EVAL® LC-L101A Ethylene Vinyl Alcohol Copolymer Resin
(discontinued **)
27 mol % Ethylene.Data provided by EVALCA. Applications: Blown film, melt phase forming. Highest gas barrier EVOH available. EVOH is used in packaging applications because of its outstanding gas ..
|
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 100 °C | 212 °F | ASTM D648 |
|
Hyosung Topilene R801H PP
R801H Injection Random CopolymerApplications:High transparent productLarge articlesCharacteristics:High transparencyStiffnessInformation provided by Hyosung Corporation
|
|||
| Deflection Temperature at 0.46 MPa (66 psi) |
100
°C @Thickness 6.40 mm |
212
°F @Thickness 0.252 in |
ASTM D648 |
|
Kingfa JH960 6300 Non-halogenated Flame Retardant PC/ABS Alloy
Features:Halogen free flame retardant, V-0/1.5mm5VB/1.6mm, 5VA/3.2mmExcellent balance propertiesHigh heat resistanceGood chemical resistanceGood hydrolysis resistanceSuit for paint and electo-platin..
|
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 100 °C | 212 °F | ASTM D648 |
|
LG Chemical LUMAX HF-5006F High Flow PBT, Weather Resistant, Flame Retardant
LUMAX resins are a family of thermoplastic blends of polybutyleneterephthalate(PBT) and styrenic resins that combine the most desirable properties of both resins and fillers. They offer high heat r..
|
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 100 °C | 212 °F | Unannealed; ASTM D648 |
|
Global PP-2311-SC Polypropylene Block Copolymer
Description-opacity, medium to high stiffness, high impact strength at low temperatureApplications-electronic appliances, wall panelsInformation provided by Global Polymers Corporation.
|
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 100 °C | 212 °F | |
|
LATI Latene® EP 7-V2 PP Copolymer, Flame Retardant
Polypropylene copolymer (PPc) based compound. UL94 V-2 classified, with brominated flame retardants, PBB/PBDE free. Availability: Africa & Middle East; Asia Pacific; Europe; Latin America; North Ame..
|
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 100 °C | 212 °F | |
|
LATI Latiohm 36/07 PD01 G/20 ABS, 20% Glass Fiber Reinforced
Semiconductive/dissipative product based on Acrylonitrile-Butadiene-Styrene copolymer (ABS). Glass fibers. Availability: Africa & Middle East; Asia Pacific; Europe; Latin America; North AmericaInfor..
|
|||
| Deflection Temperature at 0.46 MPa (66 psi) |
100
°C @Thickness 3.20 mm |
212
°F @Thickness 0.126 in |
unannealed; ASTM D648 |
|
SABIC Innovative Plastics NORYL S100G10 PPE+PS (Asia Pacific) |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 100 °C | 212 °F | ASTM D648 |
|
SCG Chemicals EL-Proâ„¢ P851JO Polypropylene Injection Molding
Key Characteristics:Good processabilityHigh gloss and brightnessOdorlessSafe for food contactRecommended Applications:Clear food containerClear large size containerThin wall productsInformation prov..
|
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 100 °C | 212 °F | ISO 75-2 |
|
Borealis Daplen™ EE137AI Polypropylene Compound 10% Mineral Filled
Daplen EE137AI is a 10% mineral filled grade intended for injection molding. EE137AI has been developed especially for the car industry, to be used in interior parts where high scratch resistance i..
|
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 100 °C | 212 °F | DIN 53461 |
|
Polyram PlusTek PA602 Nylon 6.6, Heat Stabilized
Heat stabilized polyamide 6.6 for injection molding applicationsInformation provided by Polyram Ram On Ind.
|
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 100 °C | 212 °F | ASTM D648 |
|
A. Schulman PP 3466-01 Polypropylene Homopolymer Polypropylene
DescriptionPolypropylene PP 3466-01 is a homopolymer polypropylene with the addition of antistatic. This product enhances processing with fast cycle times in injection molding.ApplicationPP 3466-01..
|
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 100 °C | 212 °F | 120°C per hour; ISO 75-2 |
|
Total PPH 4060 Polypropylene, Homopolymer
ATOFINA Polypropylene PPH 4060 is homopolymer.ApplicationATOFINA Polypropylene PPH 4060 is specially suitable for tape extrusion for woven applications and for extrusion thermoforming. PPH 4060 is..
|
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 100 °C | 212 °F | 120°C per hour; ISO 75-2 |
|
Total PPH 5060 Polypropylene, Homopolymer
ATOFINA Polypropylene PPH 5060 is homopolymer.ApplicationATOFINA Polypropylene PPH 5060 is specially suitable for tape extrusion for woven applications and for extrusion thermoforming. PPH 5060 is..
|
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 100 °C | 212 °F | ASTM D648 |
|
A. Schulman POLYFORT™ PP 2268UX Heat Resistant Polypropylene
DescriptionPolyfort® PP 2268UX is a UV stabilized, extra high flow unique high modulus, heat resistant polypropylene.Information provided by A. Schulman.
|
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 100 °C | 212 °F | ISO 75-1/-2 |
|
Covestro Bayblend® FR 3010 Polycarbonate + ABS, Flame Retardant Grade
Injection molding gradeincreased heat resistanceVicat/B 120 temperature = 110 °CUL-listing 94 V-0 (1.5 mm) antimony-, chlorine- and bromine-free flame retardantglow wire test (GWFI): 960 °C (..
|
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 100 °C | 212 °F | ISO 75-1,-2 |
|
Covestro Bayblend® FR3040 PC/ABS Blend
Main characteristics:• High toughness even at low temperatures• High dimensional accuracy and stability• Good paintability• Good flowabilityGrade characteristics:• Flame-retardant• Injec..
|
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 100 °C | 212 °F | ISO 75-1/-2 |
|
DSM Arnitel® PB582-H 58 Shore D, Blow Molding Grade, Heat Stabilized Copolyester Elastomer (North America)
Product description: Arnitel® combines the advantages of engineering thermoplastics, being easy to process with excellent mechanical properties, at the same time with the flexibility of rubbers.Arn..
|
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 100 °C | 212 °F | ISO 75-2/B |
|
ExxonMobil Exxtral™ CMU 101 Performance Polyolefin
Product Description: A specialty thermoplastic polyolefin resin designed for automotive interior trim in which good surface finish, high scratch resistance and good UV resistance are required.Availa..
|
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 100 °C | 212 °F | Unannealed; ASTM D648 |
|
Dow C702-20NA Polypropylene Impact Copolymer Resin
OverviewHigh impact performanceContains a nucleating additiveContains an antistatic additiveComplies with: U.S. FDA FCN 843, Canadian HPFB No ObjectionDOW C702-20NA Polypropylene Resin is intended f..
|
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 100 °C | 212 °F | ISO 75-1/-2 |
|
EMS-Grivory Grivory® L 25 W 20 PA12
Product Description: Grilamid L 25 W 20 is a semi-flexible plasticized high viscosity extrusion grade of Polyamide 12 (PA12). Grilamid L 25 W 20 is UV and heat stabilized. The main features of Grila..
|
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 100 °C | 212 °F | ISO 75-1/-2 |
|
DuPont Performance Polymers Crastin® ST820 BK503 Polybutylene Terephthalate (PBT)
(Unverified Data**)
Unreinforced Polybutylene Terephthalate with Excellent Impact Resistance Crastin ST820 BK503 is an unreinforced Super Tough black polybutylene terephthalate resin for injection molding.Information p..
|
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 100 °C | 212 °F | ISO 75-1/-2 |
|
DSM Arnitel® PB581-H Polyether Ester Elastomer (European Grade)
(discontinued **)
Product description: Arnitel® combines the advantages of engineering thermoplastics, being easy to process with excellent mechanical properties, at the same time with the flexibility of rubbers.Arn..
|
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 100 °C | 212 °F | ISO 75-2/B |
|
ExxonMobil PP7064L1 Polypropylene Impact Copolymer
Product Description: A nucleated impact copolymer resin with medium flow, high stiffness and antistatic properties. It is suitable for molding applications like consumer products, closures, contain..
|
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 100 °C | 212 °F | ASTM D648 |
|
SCG Chemicals EL-Pro™ P441JU Polypropylene Injection Molding
Key Characteristics:Excellent impact strengthContains UV stabilizer and anti-static agentSuitable for small to medium partsRecommended Applications:High impact and durable automotive and electrical ..
|
|||