Material Notes:

General purpose ASA. Excellent weatherability, good flow/aesthetics and high impact. Rated F2 by UL.

Physical Properties	Metric	English	Comments
Specific Gravity	1.06 g/cc	1.06 g/cc	ASTM D792
Moisture Absorption at Equilibrium	0.55 %	0.55 %	ASTM D570
Linear Mold Shrinkage, Flow	0.0050 - 0.0070 cm/cm @Thickness 3.20 mm	0.0050 - 0.0070 in/in @Thickness 0.126 in	SABIC Method
Melt Flow	7.0 g/10 min @Load 10.0 kg, Temperature 220 °C	7.0 g/10 min @Load 22.0 lb, Temperature 428 °F	ASTM D1238
	13 g/10 min @Load 5.00 kg, Temperature 260 °C	13 g/10 min @Load 11.0 lb, Temperature 500 °F	ASTM D1238
	19.5 g/10 min @Load 3.80 kg, Temperature 280 °C	19.5 g/10 min @Load 8.38 lb, Temperature 536 °F	ASTM D1238

Mechanical Properties	Metric	English	Comments
Hardness, Rockwell R	86	86	ASTM D785
Tensile Strength at Break	29.0 MPa	4210 psi	50 mm/min; ISO 527
	34.0 MPa	4930 psi	Type I, 50 mm/min; ASTM D638
Tensile Strength, Yield	39.0 MPa	5660 psi	50 mm/min; ISO 527
	41.0 MPa	5950 psi	Type I, 50 mm/min; ASTM D638
Elongation at Break	40 %	40 %	Type I, 50 mm/min; ASTM D638
	44 %	44 %	50 mm/min; ISO 527
Elongation at Yield	3.1 %	3.1 %	50 mm/min; ISO 527
Tensile Modulus	1.79 GPa	260 ksi	50 mm/min; ASTM D638
	2.00 GPa	290 ksi	1 mm/min; ISO 527
Flexural Yield Strength	58.0 MPa	8410 psi	1.3 mm/min, 50 mm span; ASTM D790
Flexural Modulus	1.79 GPa	260 ksi	1.3 mm/min, 50 mm span; ASTM D790
	2.00 GPa	290 ksi	2 mm/min; ISO 178
Izod Impact, Notched	3.20 J/cm	5.99 ft-lb/in	ASTM D256
	0.580 J/cm @Temperature -30.0 °C	1.09 ft-lb/in @Temperature -22.0 °F	ASTM D256
Izod Impact, Notched (ISO)	19.0 kJ/m²	9.04 ft-lb/in²	80104; ISO 180/1A
	4.00 kJ/m² @Temperature -30.0 °C	1.90 ft-lb/in² @Temperature -22.0 °F	80104; ISO 180/1A
Charpy Impact, Notched	1.70 J/cm²	8.09 ft-lb/in²	Edgew 80104 sp=62mm; ISO 179/1eA
Dart Drop, Total Energy	20.0 J @Temperature -30.0 °C	14.8 ft-lb @Temperature -22.0 °F	ASTM D3763
	35.0 J @Temperature 23.0 °C	25.8 ft-lb @Temperature 73.4 °F	ASTM D3763

Thermal Properties	Metric	English	Comments
CTE, linear, Parallel to Flow	84.6 µm/m-°C @Temperature -30.0 - 0.000 °C	47.0 µin/in-°F @Temperature -22.0 - 32.0 °F	ASTM E 831
	86.4 µm/m-°C @Temperature -40.0 - 40.0 °C	48.0 µin/in-°F @Temperature -40.0 - 104 °F	ASTM E 831
	90.0 µm/m-°C @Temperature 0.000 - 100 °C	50.0 µin/in-°F @Temperature 32.0 - 212 °F	ASTM E 831
CTE, linear, Transverse to Flow	91.8 µm/m-°C @Temperature -40.0 - 40.0 °C	51.0 µin/in-°F @Temperature -40.0 - 104 °F	ASTM E 831
Deflection Temperature at 0.46 MPa (66 psi)	91.0 °C	196 °F	Flatw 80104 sp=64mm; ISO 75/Bf
	87.0 °C @Thickness 3.20 mm	189 °F @Thickness 0.126 in	unannealed; ASTM D648
	90.0 °C @Thickness 6.40 mm	194 °F @Thickness 0.252 in	unannealed; ASTM D648
Deflection Temperature at 1.8 MPa (264 psi)	80.0 °C	176 °F	Flatw 80104 sp=64mm; ISO 75/Af
	95.0 °C	203 °F	annealed; ASTM D648
	76.0 °C @Thickness 3.20 mm	169 °F @Thickness 0.126 in	unannealed; ASTM D648
	79.0 °C @Thickness 6.40 mm	174 °F @Thickness 0.252 in	unannealed; ASTM D648
Vicat Softening Point	90.0 °C	194 °F	Rate B/50; ISO 306
	99.0 °C	210 °F	Rate B/50; ASTM D1525
UL RTI, Electrical	50.0 °C	122 °F	UL 746B
UL RTI, Mechanical with Impact	50.0 °C	122 °F	UL 746B
UL RTI, Mechanical without Impact	50.0 °C	122 °F	UL 746B
Flammability, UL94	HB @Thickness 1.47 mm	HB @Thickness 0.0579 in	UL 94

Optical Properties	Metric	English	Comments
Gloss	95 %	95 %	untextured, 60 degrees; ASTM D523

Electrical Properties	Metric	English	Comments
Surface Resistance	>= 1.00e+15 ohm	>= 1.00e+15 ohm	ASTM D257
Dielectric Constant	3.21 @Frequency 1.00e+6 Hz	3.21 @Frequency 1.00e+6 Hz	ASTM D150
	5.2 @Frequency 50.0 - 60.0 Hz	5.2 @Frequency 50.0 - 60.0 Hz	ASTM D150
Dielectric Strength	15.9 kV/mm @Thickness 3.20 mm	404 kV/in @Thickness 0.126 in	in oil; ASTM D149
Dissipation Factor	0.026 @Frequency 1.00e+6 Hz	0.026 @Frequency 1.00e+6 Hz	ASTM D150
	0.15 @Frequency 50.0 - 60.0 Hz	0.15 @Frequency 50.0 - 60.0 Hz	ASTM D150
Comparative Tracking Index	>= 600 V	>= 600 V	UL 746A
Hot Wire Ignition, HWI	15 - 30 sec	15 - 30 sec	UL 746A
High Amp Arc Ignition, HAI	>= 120 arcs	>= 120 arcs	UL 746A

Descriptive Properties	Value	Comments
UV-light, water exposure/immersion	F2	UL 746C