- Polymer Property : Deflection Temperature at 0.46 MPa (66 psi) = 212 °F
Polymer Property : Deflection Temperature at 0.46 MPa (66 psi) = 212 °F Product List
Thermal PropertiesTips: 30 items are displayed at most. For the rest of the results, please contact customer service.
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 100 °C @Thickness 3.18 mm |
212 °F @Thickness 0.125 in |
Unannealed; ASTM D648 |
| PolyOne Nanoblend™ LST 5501 Polypropylene, Unspecified (PP, Unspecified) Nanoblend compounds, formerly known as Maxxam LST, are LIGHT, STIFF AND TOUGH. Using nanoclay technology, these compounds deliver a combination of high stiffness and impact resistance to meet demand.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 100 °C | 212 °F | ASTM D648 |
| Mytex Polymers AS33L(W)-06 Polypropylene, Rubber modified, Talc filled, Compounded Description: AS33L(W)-06 is a compounded, talc, rubber modified polypropylene for exterior automotive applications. Material has outstanding moldability and excellent balance of high stiffness and .. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 100 °C | 212 °F | ISO 75B |
| Polyplastic Armlen® PP MF 40-4M Polypropylene Copolymer, 40% Calcium Carbonate High impact resistance at low temperatureInformation provided by PolyPlastic Group. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 100 °C | 212 °F | ASTM D648 |
| SABIC PP 526P Polypropylene Homopolymer for Cast Film Product Description: PP 526P is specially developed for cast film applications for producing clear films and does not contain slip or antiblock additives.Films produced using PP 526P will exhibit:C.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 100 °C @Thickness 3.20 mm |
212 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| SABIC Innovative Plastics Cycoloy® CX3222ME PC+ABS Cycoloy* resin grade CX3222ME is an extrudable & thermoformable PC/ABS blend with non brominated and non chlorinated flame retardant systems. Key features of low gloss and good impact make it ideal .. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 100 °C @Thickness 3.20 mm |
212 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| SABIC Innovative Plastics Cycoloy® CX7240 PC+ABS Cycoloy* CX7240 resin is an injection moldable PC/ABS blend. It contains non-brominated and non-chlorinated flame retardant systems to meet UL-94 V0 at 0.75mm, V1 at 0.6mm, V2 at 0.2mm and 5VB at 1... |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 100 °C | 212 °F | ASTM D648 |
| Hyosung Topilene R601 PP R601 Injection Random CopolymerApplications:High transparent productISBM bottleCharacteristics:High transparencyStiffnessInformation provided by Hyosung Corporation |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 100 °C | 212 °F | ASTM D648 |
| Hyosung Topilene R701 PP R701 Injection Random CopolymerApplications:High transparent productISBM bottleCharacteristics:High transparencyStiffnessInformation provided by Hyosung Corporation |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 100 °C @Thickness 6.40 mm |
212 °F @Thickness 0.252 in |
Unannealed; ASTM D648 |
| LG Chemical KEYFLEX BT 1055D Ester Type TPE Description: Injection Molding, TPC-ET, General Purpose, Medium ModulusApplication: Antenna Cover, Injection Parts for Leisure & SportsCAS: 37282-12-5Information provided by LG Chemical |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 100 °C | 212 °F | ISO 75 |
| GEHR Plastics ABS Acrylonitrile Butadiene Styrene Acrylonitrile Butadiene Styrene copolymer has a good thermal and dimensional stability and scratch resistance. Advantagesgood mechanical strengthresists scratchinghigh surface strengthhigh impact st.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 100 °C | 212 °F | ASTM D648-97 |
| Ipiranga Petrochem PH 1310 Polypropylene The production of polypropylene (PP) employs Spheripol technology from Montell / Italy. This technology has been acclaimed all over the world and is known as clean technology, because it does not pr.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 100 °C | 212 °F | ISO 75-1, -2 |
| Lanxess Pocan® C 1202 000000 PET + PC PBT + PC, non-reinforced, injection molding, improved impact strength, low tendency to warp, UV-stabilizedInformation provided by LANXESS. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 100 °C @Thickness 3.20 mm |
212 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| SABIC Innovative Plastics LNP THERMOCOMP Lexan_SP7602 PC (Asia Pacific) |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 100 °C @Thickness 6.40 mm |
212 °F @Thickness 0.252 in |
ASTM D648 |
| Samsung Cheil Industries Starex® VE-0860SE ABS, Unreinforced FR Flame-retardant ABS material that can be used in the exterior of adaptors, chargers etc.Information provided by Samsung Cheil Industries. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 100 °C | 212 °F | Edgew 120*10*4 sp=100mm; ISO 75/Be |
| SABIC Innovative Plastics Noryl HIN120P PPE+HIPS (Europe-Africa-Middle East) Noryl HIN120P is designed for selected one layer water-based paint systems. Noryl HIN120P has a Vicat B/120 of 120 °C and is targetedThis data was supplied by SABIC-IP for the Europe-Africa-Middl.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 100 °C | 212 °F | ASTM D648 |
| A. Schulman POLYFORT™ FXP 2600-3120 CaC02 Filled Homopolymer Polypropylene DescriptionPolyfort® FXP 2600-3120 is a 20% GAC02 filled homopolymer polypropylene compound.Information provided by A. Schulman. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 100 °C | 212 °F | ASTM D648 |
| A. Schulman PP 3486-01 Polypropylene Homopolymer Polypropylene DescriptionPolypropylene PP 3486-01 is a special homopolymer polypropylene designed with long term heat aging formula for appliance application.ApplicationThis product is for injection molded applic.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 100 °C | 212 °F | ASTM D648 |
| A. Schulman POLYFORT™ FXP 2600-3120 CaC02 Filled Homopolymer Polypropylene DescriptionPolyfort® FXP 2600-3120 is a 20% GAC02 filled homopolymer polypropylene compound.Information provided by A. Schulman. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 100 °C | 212 °F | ASTM D648 |
| Formosa Plastics Formolene® 4100P Injection Molding Polypropylene Homopolymer with ESCR AdditivesApplications: Closures, small appliances, housewares and toys.Formolene 4100P is a low viscosity, highly isotactic polypropylene homopolymer designed for various injec.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 100 °C | 212 °F | ASTM D648 |
| Formosa Plastics Formolene® 6507N Impact Copolymer Polypropylene Impact Copolymer for Injection Molding Formolene® 6507N is a medium impact copolymer of polypropylene characterized by its easy mold flow, physical property balance and excellent dimensional stabil.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 100 °C | 212 °F | ASTM D648 |
| A. Schulman PP 3353-01 Polypropylene Medium Impact Polypropylene DescriptionPolypropylene PP 3353-01 is a high flow medium impact polypropylene which is suitable for molding thin parts with long mold flow distances. It permits reduction of cycle times, temperatu.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 100 °C | 212 °F | ASTM D648 |
| A. Schulman PP 829-01 Polypropylene Homopolymer Polypropylene DescriptionPolypropylene PP 829-01 is a homopolymer polypropylene approved to Ford specification ESB-M4D63A. Primarily used for interior automotive components, this material is also well suited for.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 100 °C | 212 °F | ASTM D648 |
| A. Schulman PP 829-01 Polypropylene Homopolymer Polypropylene DescriptionPolypropylene PP 829-01 is a homopolymer polypropylene approved to Ford specification ESB-M4D63A. Primarily used for interior automotive components, this material is also well suited for.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 100 °C | 212 °F | 120°C per hour; ISO 75-2 |
| Total PPC 13442 Polypropylene, Heterophasic Copolymer ATOFINA Propylene 13442 is a nucleated antistatic heterophasic copolymer. PPC 13442 is characterized by very high fluidity with good mechanical properties. It has been formulated for excellent ant.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 100 °C | 212 °F | ASTM D648 |
| A. Schulman POLYFORT™ PP 2173HU Toyota High Impact Copolymer Polypropylene DescriptionPolyfort® PP 2173HU Toyota is a high flow, UV stabilized, high impact copolymer polypropylene.Information provided by A. Schulman. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 100 °C | 212 °F | ISO 75-1/-2 |
| EMS-Grivory Grivory® L 20 W 20 PA12 Product Description: Grilamid L 20 W 20 is a semi-flexible plasticized medium viscosity polyamide 12 (PA12) extrusion grade. Grilamid L 20 W 20 is heat stabilized. The main features of Grilamid L 20.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 100 °C | 212 °F | |
| BASF Procom® X10S 773 Polypropylene Car bumpers and spoilers where good paintability is required.Data was collected by ISO methods and provided by BASF. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 100 °C | 212 °F | ASTM D648 |
| A. Schulman POLYFORT™ PP 2268UX Heat Resistant Polypropylene DescriptionPolyfort® PP 2268UX is a UV stabilized, extra high flow unique high modulus, heat resistant polypropylene.Information provided by A. Schulman. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 100 °C | 212 °F | |
| Aardvark Polymers Aardalloy® 3326 POM Alloy Rotational Molding Resin Aardalloy 3326 is an acetal alloy formulated for enhanced impact resistance and elongation.Aardalloy 3326 maintains the high degree of chemical resistance and low fuel permeation rates of unfilled a.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 100 °C | 212 °F | ISO 75 |
| Polyram RamSter PF801 PBT, High Impact Modified High impact modified PBT for injection molding applications.Information provided by Polyram. |
|||