Songhan Plastic Technology Co.,Ltd.
 POLYMER SEARCH

SABIC Innovative Plastics Valox® 420SE0U PBT

Category Polymer , Thermoplastic , Polyester, TP , Polybutylene Terephthalate (PBT)
Manufacturer SABIC Innovative Plastics (GE Plastics)
Trade Name Valox®
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF SABIC Innovative Plastics Valox® 420SE0U PBT.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
PBT, 30% Glass Reinforced, Flame Retardant UL94 V-0/5VA rated, UV-Stabilized
Physical Properties Metric English Comments
Specific Gravity 1.63 g/cc
1.63 g/cc
ASTM D792
Density 1.63 g/cc
0.0589 lb/in³
ISO 1183
Water Absorption 0.060 %

@Time 86400 sec
 0.060 %

@Time 24.0 hour
 ASTM D570
Moisture Absorption 0.0700 %
0.0700 %
23°C / 50% RH; ISO 62
Water Absorption at Saturation 0.090 %
0.090 %
ISO 62
Linear Mold Shrinkage, Flow 0.0010 - 0.0050 cm/cm
0.0010 - 0.0050 in/in
on Tensile Bar; SABIC Method
0.0030 - 0.0050 cm/cm

@Thickness 1.50 - 3.20 mm
 0.0030 - 0.0050 in/in

@Thickness 0.0591 - 0.126 in
 SABIC Method
0.0050 - 0.0070 cm/cm

@Thickness 3.20 mm
 0.0050 - 0.0070 in/in

@Thickness 0.126 in
 SABIC Method
0.0050 - 0.0080 cm/cm

@Thickness 3.20 - 4.60 mm
 0.0050 - 0.0080 in/in

@Thickness 0.126 - 0.181 in
 SABIC Method
Linear Mold Shrinkage, Transverse 0.0040 - 0.0080 cm/cm
0.0040 - 0.0080 in/in
on Tensile Bar; SABIC Method
0.0040 - 0.0060 cm/cm

@Thickness 1.50 - 3.20 mm
 0.0040 - 0.0060 in/in

@Thickness 0.0591 - 0.126 in
 SABIC Method
0.0060 - 0.0090 cm/cm

@Thickness 3.20 - 4.60 mm
 0.0060 - 0.0090 in/in

@Thickness 0.126 - 0.181 in
 SABIC Method
0.0050 - 0.010 cm/cm

@Thickness 3.20 mm
 0.0050 - 0.010 in/in

@Thickness 0.126 in
 SABIC Method
Melt Flow 42 g/10 min

@Load 5.00 kg,
Temperature 250 °C
 42 g/10 min

@Load 11.0 lb,
Temperature 482 °F
 ASTM D1238
Melt Index of Compound 29 g/10 min

@Load 5.00 kg,
Temperature 250 °C
 29 g/10 min

@Load 11.0 lb,
Temperature 482 °F
 MVR [cm^3/10 min]; ISO 1133
Mechanical Properties Metric English Comments
Hardness, Rockwell R 119
119
ASTM D785
119
119
ISO 2039-2
Hardness, H358/30 118 MPa
17100 psi
ISO 2039-1
Tensile Strength at Break 120 MPa
17400 psi
Type I, 5 mm/min; ASTM D638
120 MPa
17400 psi
5 mm/min; ISO 527
Tensile Strength, Yield 120 MPa
17400 psi
Type I, 5 mm/min; ASTM D638
120 MPa
17400 psi
5 mm/min; ISO 527
Elongation at Break 1.9 %
1.9 %
5 mm/min; ISO 527
2.0 %
2.0 %
Type I, 5 mm/min; ASTM D638
Elongation at Yield 1.9 %
1.9 %
5 mm/min; ISO 527
2.0 %
2.0 %
Type I, 5 mm/min; ASTM D638
Tensile Modulus 10.0 GPa
1450 ksi
1 mm/min; ISO 527
12.0 GPa
1740 ksi
5 mm/min; ASTM D638
Flexural Strength 180 MPa
26100 psi
ISO 178
186 MPa
27000 psi
1.3 mm/min, 50 mm span; ASTM D790
Flexural Modulus 9.50 GPa
1380 ksi
2 mm/min; ISO 178
9.80 GPa
1420 ksi
1.3 mm/min, 50 mm span; ASTM D790
Izod Impact, Notched 0.600 J/cm
1.12 ft-lb/in
ASTM D256
0.570 J/cm

@Temperature -30.0 °C
 1.07 ft-lb/in

@Temperature -22.0 °F
 ASTM D256
Izod Impact, Unnotched 6.20 J/cm
11.6 ft-lb/in
ASTM D4812
Izod Impact, Notched (ISO) 7.00 kJ/m²
3.33 ft-lb/in²
80*10*4; ISO 180/1A
6.00 kJ/m²

@Temperature -30.0 °C
 2.86 ft-lb/in²

@Temperature -22.0 °F
 80*10*4; ISO 180/1A
Izod Impact, Unnotched (ISO) 45.0 kJ/m²
21.4 ft-lb/in²
80*10*4; ISO 180/1U
45.0 kJ/m²

@Temperature -30.0 °C
 21.4 ft-lb/in²

@Temperature -22.0 °F
 80*10*4; ISO 180/1U
Charpy Impact Unnotched 5.00 J/cm²
23.8 ft-lb/in²
Edgew 80*10*4 sp=62mm; ISO 179/1eU
5.00 J/cm²

@Temperature -30.0 °C
 23.8 ft-lb/in²

@Temperature -22.0 °F
 Edgew 80*10*4 sp=62mm; ISO 179/1eU
Charpy Impact, Notched 0.700 J/cm²
3.33 ft-lb/in²
Edgew 80*10*4 sp=62mm; ISO 179/1eA
0.600 J/cm²

@Temperature -30.0 °C
 2.86 ft-lb/in²

@Temperature -22.0 °F
 Edgew 80*10*4 sp=62mm; ISO 179/1eA
Dart Drop, Total Energy 5.00 J

@Temperature 23.0 °C
 3.69 ft-lb

@Temperature 73.4 °F
 ASTM D3763
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 25.0 µm/m-°C

@Temperature -40.0 - 40.0 °C
 13.9 µin/in-°F

@Temperature -40.0 - 104 °F
 ISO 11359-2
25.0 µm/m-°C

@Temperature -40.0 - 40.0 °C
 13.9 µin/in-°F

@Temperature -40.0 - 104 °F
 ASTM E 831
25.2 µm/m-°C

@Temperature 60.0 - 138 °C
 14.0 µin/in-°F

@Temperature 140 - 280 °F
 ASTM E 831
CTE, linear, Transverse to Flow 89.0 µm/m-°C

@Temperature -40.0 - 40.0 °C
 49.4 µin/in-°F

@Temperature -40.0 - 104 °F
 ASTM E 831
89.0 µm/m-°C

@Temperature -40.0 - 40.0 °C
 49.4 µin/in-°F

@Temperature -40.0 - 104 °F
 ISO 11359-2
Thermal Conductivity 0.250 W/m-K
1.74 BTU-in/hr-ft²-°F
ISO 8302
Deflection Temperature at 0.46 MPa (66 psi) 220 °C
428 °F
Flatw 80*10*4 sp=64mm; ISO 75/Bf
212 °C

@Thickness 3.20 mm
 414 °F

@Thickness 0.126 in
 unannealed; ASTM D648
215 °C

@Thickness 6.40 mm
 419 °F

@Thickness 0.252 in
 unannealed; ASTM D648
Electrical Properties Metric English Comments
Volume Resistivity >= 1.00e+15 ohm-cm
>= 1.00e+15 ohm-cm
ASTM D257
Dielectric Constant 3.7

@Frequency 1.00e+6 Hz
 3.7

@Frequency 1.00e+6 Hz
 ASTM D150
3.8

@Frequency 100 Hz
 3.8

@Frequency 100 Hz
 ASTM D150
Dielectric Strength 19.0 kV/mm

@Thickness 3.20 mm
 483 kV/in

@Thickness 0.126 in
 in air; ASTM D149
24.0 kV/mm

@Thickness 1.60 mm
 610 kV/in

@Thickness 0.0630 in
 in oil; ASTM D149
Dissipation Factor 0.0020

@Frequency 100 Hz
 0.0020

@Frequency 100 Hz
 ASTM D150
0.020

@Frequency 1.00e+6 Hz
 0.020

@Frequency 1.00e+6 Hz
 ASTM D150
Arc Resistance 60 - 120 sec
60 - 120 sec
Tungsten; ASTM D495
Comparative Tracking Index 175 - 250 V
175 - 250 V
UL 746A
Hot Wire Ignition, HWI 30 - 60 sec
30 - 60 sec
UL 746A
High Amp Arc Ignition, HAI >= 120 arcs
>= 120 arcs
UL 746A
High Voltage Arc-Tracking Rate, HVTR >= 150 mm/min
>= 5.91 in/min
UL 746A
Users viewing this material also viewed the following: