Polymer Property : Tensile Modulus = 10.0 GPa Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Tensile Modulus	10.0 GPa	1450 ksi	STN EN ISO 527-2
Plastcom SLOVASTER® B GF 30 Polybutylene Terephthalate, 30% Glass Fiber FeaturesPBT for injection moulding, chemically reinforced with 30% glass fiber. Characterized by excellent properties also at low temperatures like tensile and flexural modulus, tensile strength, a..
Tensile Modulus	10.0 GPa	1450 ksi	ASTM D638
Premix Premi-Glas® 1201-20 Fiberglass Reinforced Thermoset SMC Premi-Glas® 1201-20 is a fiberglass reinforced thermoset sheet molding compound for sanitary ware applications such as shower bases and surrounds, bathtubs and vanity tops.Key features and benefits..
Tensile Modulus	10.0 GPa	1450 ksi	ASTM D638
Premix Premi-Glas® 2203-20 CR-SX Fiberglass Reinforced Thermoset SMC Premi-Glas® 2203-20 CR-SX is a fiberglass reinforced thermoset sheet molding compound for electrical and flame retardant applications.Key features and benefits are:Excellent stiffness to weight rat..
Tensile Modulus	10.0 GPa	1450 ksi	ASTM D638
Premix Premi-Glas® 3140-22 Fiberglass Reinforced Thermoset Thick Molding Compound Premi-Glas® 3140-22 is a fiberglass reinforced thermoset thick molding compound for electrical and flame retardant applications.Key features and benefits are:TMC compounding process preserves glass..
Tensile Modulus	10.0 GPa	1450 ksi	ASTM D638
Premix Premi-Glas® 3404 33% Glass Reinforced SMC Description: Premi-Glas® 3404 is a glass reinforced thermoset sheet molding compound designed for mass transit and high strength flame retardant applications where low smoke and flame are required...
Tensile Modulus	10.0 GPa	1450 ksi	1 mm/min; ISO 527
SABIC Innovative Plastics Lexan® 3414R PC (Europe-Africa-Middle East) LEXAN 3414R is a high viscosity, 40% glass reinforced, flame retardant grade, especially designed for applications requiring high rigidity together with high heat resistance.
Tensile Modulus	10.0 GPa	1450 ksi
LATI Latistat 66-06 G/30 PA66, 30% Glass Fiber Reinforced Dissipative product based on Polyamide 66 (PA66). Glass fibers. Availability: Africa & Middle East; Asia Pacific; Europe; Latin America; North AmericaInformation provided by Lati Industria Termoplas..
Tensile Modulus	10.0 GPa	1450 ksi	ISO 527-1/-2
Unitika B2040G33 PA66, 33% Glass Fiber Reinforced, Dry Information provided by Unitika Ltd.
Tensile Modulus	10.0 GPa	1450 ksi	ASTM-D790
Polyram Polytron P40B11 Homopolymer Polypropylene, Chemically Coupled 40% LGF A chemically coupled 40% LGF reinforced black PP, heat stabilized for injection molding applications.Information provided by Polyram Ram On Ind.
Tensile Modulus	10.0 GPa	1450 ksi	ISO 527
Polyram Polytron P40N11 Polypropylene, 40% Long Glass Fibers A chemically coupled 40% long glass fiber reinforced natural polypropylene, heat stabilized, for injection molding applications.Information provided by Polyram.
Tensile Modulus	10.0 GPa	1450 ksi	ASTM-D790
Polyram RamOfin PPH300G9 Polypropylene, 45% Glass Fiber 45% glass fiber reinforced polypropylene for injection molding applicationsInformation provided by Polyram Ram On Ind.
Tensile Modulus	10.0 GPa	1450 ksi	conditioned; ISO 527-1/-2
EMS-Grivory Grivory® 1SBVX-30H LDS black PA1010-GF30 Product Description: Grilamid 1SBVX-30H LDS black is a 30% glass fiber reinforced Polyamide 1010 injection molding grade. This grade is specifically optimized for the laser Direct Structuring techno..
Tensile Modulus	10.0 GPa	1450 ksi	ISO 527-1/-2
DSM Stanyl® TW200F6 (DAM) Nylon 46 30% Glass Reinforced, Heat Stabilized (North America) Information provided by DSM Engineering Plastics.
Tensile Modulus	10.0 GPa	1450 ksi	ISO 527-1/-2
DSM Stanyl® TW241F10 Nylon 46-50% Glass Reinforced (European Grade) (Cond) Stanyl is a high performance polyamide providing good performance and value across a broad range of automotive and electronic applications. Stanyl offers:Highest mechanical properties at high temper..
Tensile Modulus	10.0 GPa @Temperature 200 °C	1450 ksi @Temperature 392 °F	ISO 527-1/-2
DSM Stanyl® TW272B6 (PA46+PTFE)-CF30 30% Carbon Reinforced, Heat Stabilized, Wear and Friction Modified
Tensile Modulus	10.0 GPa	1450 ksi	DAM; ISO 527-1/-2
DuPont Performance Polymers Minlon® 10B40HS1 BK061 Nylon 66 (Unverified Data**) 40% Mineral Reinforced Heat Stabilized Polyamide 66 Minlon 10B40HS1 BK061 is a 40% mineral reinforced heat stabilized black polyamide 66 resin for injection molding.Information provided by DuPont Pe..
Tensile Modulus	10.0 GPa	1450 ksi	DAM; ISO 527-1/-2
DuPont Performance Polymers Zytel® HTN FR52G30NH BK337 Polyphthalamide (PPA) (Unverified Data**) 30% Glass Reinforced Flame Retardant Non-Halogenated PPA High Performance Polyamide Zytel HTNFR52G30NH BK337 is a 30% glass reinforced flame retardant lubricated high performance polyamide resin. It..
Tensile Modulus	10.0 GPa	1450 ksi	1 mm/min; ISO 527
Eurostar Staramide BG7H PA6, 35% Glass Fiber Filled, Heat Stabilized, Injection Molded Staramide BG7H is a Heat Stabilized, 35% Glass Fiber Reinforced, Polyamide 6, Injection Molding ResinInformation provided by Eurostar.
Tensile Modulus	10.0 GPa	1450 ksi	1 mm/min; ISO 527
Eurostar Starglas CF006 Styrenic, 30% Glass Filled, Injection Molding Starglas CF006 is a 30% Glass Fiber Reinforced Styrenic Injection Molding ResinInformation provided by Eurostar.
Tensile Modulus	10.0 GPa	1450 ksi	dry; ISO 527
Azoty Tarnow™ Tarnamid® T-27 GF30 FRV0 Polyamide 6 - Flame Retarded, Reinforced Flame retarded grades, flammability class V0, reinforced with 30% glass fibers, without addition of any halogen compounds, red phosphorus and asbestos, doesn't release any toxic gases during burning..
Tensile Modulus	10.0 GPa	1450 ksi	1[mm/min]; ISO 527-1/2
Akro-Plastic Akromid® A3 GF 30 (2397) PA 6.6 Dry, 30% Glass Filled AKROMID® A (Polyamide 6.6) is an engineering compound, characterized by high mechanical strength, stiffness and thermal resistance. Furthermore, this polyamide offers high toughness at low temperat..
Tensile Modulus	10.0 GPa	1450 ksi	ISO 527-2
Ascend Performance Materials Vydyne® R530H NAT Nylon 66, 30% Glass Reinforced, DAM Vydyne® R530H NAT is general-purpose, heat-stabilized, hydrolysis-resistant, 30% glass-fiber reinforced PA66 resin. Available in natural, it is specifically designed to maximize the retention of ph..
Tensile Modulus	10.0 GPa	1450 ksi	ISO 527-1/-2
DuPont Performance Polymers Crastin® SK615SF NC010 Polybutylene Terephthalate (PBT) (Unverified Data**)&l 30% Glass Reinforced Low Viscosity Polybutylene Terephthalate Developed for Super Fast Production Crastin SK615SF is a 30% glass fiber reinforced low viscosity polybutylene terephthalate for injecti..